Penetrative Internal Oxidation from Alloy 690 Surfaces and Stress Corrosion Crack Walls during Exposure to PWR Primary Water

  1. Jeremy T. Busby,
  2. Gabriel Ilevbare and
  3. Peter L. Andresen
  1. Matthew J. Olszta,
  2. Daniel K. Schreiber,
  3. Larry E. Thomas and
  4. Stephen M. Bruemmer

Published Online: 26 JUN 2012

DOI: 10.1002/9781118456835.ch31

15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors

15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors

How to Cite

Olszta, M. J., Schreiber, D. K., Thomas, L. E. and Bruemmer, S. M. (2012) Penetrative Internal Oxidation from Alloy 690 Surfaces and Stress Corrosion Crack Walls during Exposure to PWR Primary Water, in 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (eds J. T. Busby, G. Ilevbare and P. L. Andresen), John Wiley & Sons, Inc., Hoboken, New Jersey, Canada. doi: 10.1002/9781118456835.ch31

Author Information

  1. Pacific Northwest National Laboratory Richland, WA 99352 USA

Publication History

  1. Published Online: 26 JUN 2012
  2. Published Print: 2 APR 2012

ISBN Information

Print ISBN: 9781118132418

Online ISBN: 9781118456835

SEARCH

Keywords:

  • alloy 690;
  • penetrative oxidation;
  • SCC

Summary

This chapter contains sections titled:

  • Introduction

  • Experimental

  • Results

  • Discussion

  • Conclusion

  • Acknowledgements