Pseudo block copolymers with tunable micro- or macrophase-separated structures are created by introducing multiple hydrogen-bonding groups at the polymer ends (see Figure). The resulting materials are stabilized up to 80 °C above the glass-transition temperature (Tg) of the higher-Tg component.