Correction: Graphene-Confined Sn Nanosheets with Enhanced Lithium Storage Capability

Authors

  • Bin Luo,

  • Bin Wang,

  • Xianglong Li,

  • Yuying Jia,

  • Minghui Liang,

  • Linjie Zhi

Errata

This article corrects:

  1. Graphene-Confined Sn Nanosheets with Enhanced Lithium Storage Capability Volume 24, Issue 26, 3538–3543, Article first published online: 8 June 2012

The cycle performance (Figure 4a and Figure S6) and thermal gravimetric analysis data for the control sample (G-Sn) in the above-mentioned article are incorrect. We provide the corrected Figure 4 below.

original image

Also, the sentences “The first discharge and charge steps (Figure S6) deliver a specific discharge capacity of 1380 mAh g−1 for G/Sn/G, 1013 mAh g−1 for G-Sn@C, and 1572 mAh g−1 for G-Sn electrodes, with initial Coulombic efficiencies of 66.5%, 65.6%, and 64.8%, respectively.” on page 3541 should be “The first discharge and charge steps (Figure S6) deliver a specific discharge capacity of 1380 mAh g−1 for G/Sn/G, 1013 mAh g−1 for G-Sn@C, and 1637 mAh g−1 for G-Sn electrodes, with initial Coulombic efficiencies of 66.5%, 65.6%, and 61%, respectively.”

The corresponding first discharge and charge curves (Figure S6) and the thermal gravimetric analysis data (Figure S2) for the control sample (G-Sn) are shown in the Supporting Information for this correction which is available from the Wiley Online Library or from the author.

The arguments and conclusions of the original article are not affected. The authors apologize for any inconvenience caused.