Free-radical copolymerization and kinetic treatment of methyl methacrylate with N-P-tolylmaleimide



The free-radical copolymerization of methyl methacrylate (MMA) with N-P-tolylmalemide (NPTMI) at 77°C in cyclohexanone solution initiated by AIBN was studied. The copolymer composition was calculated from the nitrogen content estimated by the Mico–Kijedldahl's method and by elemental analysis. The reactivity ratios have been calculated by Fineman and Ross method. The monomer reactivity ratios were rNPTMI = 1.24, rMMA = 2.1. The glass transition temperature (Tg) of the copolymers were determined by torsion braid analysis (TBA). The thermal stability was determined by thermogravimetric analysis (TGA). T50, temperature at which the weight loss reaches 50%, was abstained. The results showed that the Mn and Mw increased, whereas the NPTMI feed content increased. The Tg and T50 increased dramatically. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 91: 867–870, 2004