Keywords:

  • Sol–gel chemistry;
  • X-ray diffraction;
  • BaTiO3

Abstract

Highly crystalline BaTiO3 particles were prepared by sol–gel process. Ultrasound and microwave techniques were used to facilitate the synthesis of BaTiO3. BaTiO3 samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), particle size analyser, and high temperature differential scanning calorimetry/thermogravimetric analysis (DSC/TGA). The results indicate that both barium and titanium sources and preparation techniques affected BaTiO3 purity and crystallite size. The smallest particle and crystallite sizes were obtained by using BaCl2 and (C4H9O)4Ti and the crystallite size of BaTiO3 was 8 ± 1 nm via MW technique.

Les particules hautement cristallines de BaTiO3 ont été préparées par procédé sol-gel. Des techniques d'échographie et à micro-ondes ont été utilisées pour faciliter la synthèse de BaTiO3. Les échantillons de BaTiO3 ont été caractérisés par diffraction des rayons X (XRD), microscopie électronique à balayage (MEB), analyseur de taille de particules et analyse calorimétrique à compensation de puissance haute température/analyse thermogravimétrique (DSC/TGA). Les résultats indiquent que les sources de baryum et de titane et les techniques de préparation ont influé sur la pureté de BaTiO3 et la grosseur des cristallites. La grosseur des plus petites particules et cristallites a été obtenue en utilisant BaCl2 et (C4H9O)4Ti et la grosseur des cristallites de BaTiO3 était de 8 ± 1 nm en faisant appel à la technique de masse moléculaire relative (Mr.)