Preparation and characterisation of copper-substituted SBA-16 type mesoporous materials by modified pH-adjusting method

Authors


Abstract

Copper-containing SBA-16 type mesoporous material was synthesised by modified pH-adjusting method at different pH values (pH 3, 5, and 7). In this method after formation of materials' basic structure the pH of mixture was adjusted with aqueous ammonia solution, stirred and filtered directly avoiding second hydrothermal treatment. The characterisation results revealed that copper was successfully incorporated into silica framework. The pH value was found to be a very important parameter in deciding the final structure, pH 5 was the most suitable pH value for preparation of ordered Cu-SBA-16, increase in pH to 7 resulted in formation of structure with less order. The material was applied for adsorption desulfurisation of dibenzothiophene (DBT) to check its performance.

Abstract

Un matériau mésoporeux de type SBA-16 contenant du cuivre a été synthétisé par une méthode modifiée d'ajustement de pH pour différentes valeurs de pH (pH 3, 5 et 7). Dans cette méthode, après formation de la structure de base du matériau, le pH du mélange a été ajusté avec une solution d'ammoniaque aqueuse, mélangée et filtrée directement afin d'éviter un second traitement hydrothermique. Les résultats de caractérisation ont révélé que du cuivre avaient été incorporé avec succès dans le cadre de silice. On a conclu que la valeur de pH était un paramètre très important pour décider de la structure finale. Ph = 5 a été considéré comme la valeur la mieux appropriée pour la préparation, une augmentation du pH jusqu'à 7 résultant à la formation d'une structure d'ordre moindre. Le matériau a été utilisé pour la désulfuration par adsorption du dibenzothiophène (DBT) pour vérifier son efficacité.

Ancillary