Kinetic studies of the dissolution of brass

Authors


  • Based on a paper presented to the C. I. C. 49th Canadian Chemical Conference, Saskatoon, Sask., June 5-8, 1966.

Abstract

The rates of dissolution of 85/15 brass, 70/30 brass, and 60/40 brass in oxygenated dilute hydrochloric acid solution have been measured in the temperature range 25°C to 57°C. In each case the dissolution was found to occur in several distinct stages, described by different rate laws and having different energies of activation. The activation energies indicate that the process is not completely mass transfer controlled. Significant dezincification occurred only in the case of the 60/40 brass. The data indicate that the dezincification occurred through a total corrosion step followed by redeposition of copper. A modification of a mechanism proposed by Habashi(6) is shown to correlate the observed data for monophase brasses.

Abstract

On a mesuré les vitesses de dissolution des laitons 85/15, 70/30, et 60/40 dans une solution oxygénée et diluée d'acide chlorhydrique, pour une échelle de températures comprises entre 25°C et 57°C. On a trouvé que, dans chaque cas, la dissolution se faisait en plusieurs étapes distinctes, sujettes à diverses lois de vitesse et possédant des énergies d'activation différentes. Les énergies d'activation ont indiqué que le procédé n'est pas complètement un transfert de masse contro'lé. Une déperdition appréciable de zinc ne s'est produite que dans le cas delaiton 60/40 et, d'après les résultats obtenus, elle s'est faite par voit de corrosion totale suivie de la formation d'un dépo't de cuivre. On a indiqué qu'une modification du mécanisme proposé par Habashi permet de mettre en corrélation les résultats obtenus dans le cas des laitons uniphasés.

Ancillary