Behavior of macromolecules in dilute solutions: II—On the axial dispersion coefficient



Using pulse-input technique, axial dispersion coefficients were determined for polystyrene in tetrahydrofuran, in toluene and in a toluene/methanol mixture flowing in a long capillary tube under conditions such that the Reynolds number was less than 500. Low polydispersity polystyrene materials with nominal molecular weights ranging from 900 to 1.8 × 106 were used. For the system studied and for fixed Reynolds numbers, the coefficient, on log-log scales, was found to be a linear function of the product of the intrinsic viscosity and the molecular weight. An empirical equation relating this coefficient to the Reynolds number and to [η]M was obtained. This equation predicted results which agreed well with experimentally determined values.


En utilisant une méthode à base d'impulsions, on a détermine les coefficients de dispersion axiale dans le cas du polystyrène dans le tétrahydrofurane, dans le toluène et dans un mélange de toluène et d'alcool méthylique; le produit coulait dans un long tube capillaire dans des conditions telles que le nombre de Reynolds était inférieur à 500. On a employé des types de polystyrène à faible dispersion, dont les poids moléculaires nominaux variaient entre 900 et 1.8 × 106. On a trouvé, dans le cas du système étudié et pour des nombres de Reynolds fixes, que le coefficient, sous forme logarithmique, était une fonction linéaire du produit de la viscosité intrinsèque multipliée par le poids moléculaire. On a obtenu une équation empirique qui reliait ledit coefficient an nombre de Reynolds ct à [η]M; elle a prévu des résultats qui concordaient bien avec les valeurs déterminées expérimentalement.