Rheological comparison of four blow molding resins

Authors


Abstract

For molten polymers, each theological property provides a different basis for comparison and characterization. This point is illustrated by reference to the results of an extensive testing program involving a series of four commercial blow molding resins, each produced by a different Canadian manufacturer. Three high density polyethylenes were studied at 170°C, while a polypropylene was studied at 190°C. Properties measured included viscosity, first normal stress difference, dynamic viscosity, storage modulus, extrudate swell as a function of time and shear rate, and stress growth functions for both shear and uniaxial elongation.

Abstract

Dans le cas des polymères fondus, chaque propriété rhéologique fournit une base différentc de comparison et de caractérisation. On a illustré cet énoncé en se référant aun résultats d'un programme d'essais impliquant quatre résines commerciales de moulage par soufflage, chacuue de celles-ci ayant été produite par un fabricant canadien différent. On a étudié trois polyéthylènes à forte densité à 170°C et un polypropylène a 190°C. Les propriétés mesurées incluaient la viscosité, la différence des contraintes normales binaires, la viscosité dynamique, le module de stockage, le gonflement de l'extrudat en fonction du temps et de la vitesse de cisaillement ainsi que les functions d'accroissement des contraintes pour les élongations uniaxiales et en cisaillement.

Ancillary