The effect of low temperature oxidation on the viscosity of Athabasca bitumen was investigated over the temperature range 320 to 370K, and to extents of oxidation as high as 41.7 × 10−3 kg-O2/kg-bitumen. Even at this relatively low extent of oxidation, the viscosity was observed to be more than two orders of magnitude higher than that of unoxidized bitumen. It was found that the Andrade viscosity model could adequately characterize the temperature dependence of the viscosity at all extents of oxidation. However, the pre-exponential constant in the model was observed to be a strong function of extent of oxidation.

On a étudié l'effet de l'oxydation à basse température sur la viscosité du bitume de l'Athabasca sur une gamme de température variant de 320 à 370K et à des degrés d'oxydation atteignant 41.7 × 10−3 kg/O2/kg de bitume. On a observé que, měme à ce degré relativement faible d'oxydation, la viscosité est de plus de deux ordres de grandeur plus élevée que celle du bitume non oxydé. On a constaté que le modèle de viscosité d'Andrade pouvait caractériser adéquatement la variation de la viscosité avec la température pour tous les degrés d'oxydation. On a toutefois noté que la constante pré-exponentielle du modèle était fortement fonction du degré d'oxydation.