A new unsteady-state method for measuring the high temperature effective thermal conductivity of porous spheres is described. The method is based on moving a spherical body from an enclosure at a low temperature into one at a higher temperature and measuring the surface temperature with a recording radiation pyrometer. The thermal conductivity is evaluated using the known relations between the dimensionless surface temperature and time. The apparatus requirements are discussed in detail.

The thermal conductivities of calcined dolomite/silicon metal mixtures, of the type used in the production of magnesium, were measured at 750 to 1150°C with compaction pressures of 67 to 185 MPa both before and after reaction.

On décrit une nouvelle méthode de mesure en régime transitoire de la conductivité thermique effective de sphères poreuses à haute température. On déplace un corps sphérique depuis une enceinte à basse température vers une autre à plus haute température, et on enregistre la température de surface à l'aide d'un pyromètre optique équipé d'un enregistreur. La conductivité thermique est évaluée grǎce aux relations déjà établies entre la température de surface adimensionnelle et le temps. L'appareillage est décrit de manière détaillée.

Les conductivités thermiques de mélanges de métaux, de dolomite et de silicium calcinés, du měme type que le mélange utilisé dans la production du magnésium, ont été mesurées à des températures comprises entre 750 et 1150° C avec des pressions de compaction de 67 à 185 MPa, avant et après la réaction.