Formation of fine magnetite particles by oxidation of aqueous suspensions of ferrous hydroxide

Authors


Abstract

Fine magnetite particles were prepared by oxidation of aqueous ferrous hydroxide suspensions in a bubble column equipped with an internal concentric draft tube. The oxidation reaction rate could be expressed apparently as zero-order with respect to the concentration of total ferrous species and first-order with respect to the concentration of dissolved oxygen. The final particle size generally decreased with increasing reaction rate. The geometric Standard deviation of size-distribution ranged from 1.20 to 1.35 under the present experimental conditions, and increased with an increase in reaction rate.

Abstract

Des particules de magnetite fines ont été préparées par oxydation de suspensions d'hydroxide ferreux aqueux dans une colonne à bulles munie d'un tube d'aspiration concentrique interne. La vitesse de réaction d'oxydation pourrait être apparemment exprimée comme étant d'ordre zéro par rapport à la concentration des espèces ferreuses totales et du premier ordre par rapport à la concentration d'oxygène dissous. La taille finale des particules diminue généralement avec l'augmentation de la vitesse de réaction. L'écart—type géométrique de la distribution de tailles varie entre 1,20 et 1,35 dans les conditions expérimentales présentes et augmente avec la vitesse de réaction.

Ancillary