A study of the deposition of silt onto the surface of type 304 stainless steel

Authors


Abstract

The deposition rate of Lake Ontario silt onto type 304 stainless steel at a fluid velocity of 1.05 m/s is given by:

N = 2.1 × 10−5 exp (-E/RT) Cb p.

where E = 25.3 kJ/mol. Both the magnitude and the temperature dependence of the deposition rate is consistent with deposition that is surface rather than transport limited. The release rates were small compared to the deposition rates and independent of the surface temperature. Only particles less than 5 μm were found in the deposits at 1.05 m/s, even though particles up to 25 μm were in the flowing silt suspension. The maximum particle size in the deposit decreased with increasing deposition velocity.

Abstract

La vitesse de déposition de limon du Lac Ontario sur de l'acier inoxydable de type 304 à une vitesse de fluide de 1,05 m/s est exprimée par:

N = 2.1 × 10−5 exp (-E/RT) Cb p.

ou E = 25,3 kJ/mol. L'importance et la dependence en la température de la vitesse de déposition sont toutes deux cohérentes avec la déposition de type limité en surface plutôt que de type transport. Les vitesses de libération sont très faibles comparativement aux vitesses de déposition et sont indépendantes de la température de surface. Seules les particules inférieures à 5 μm ont été trouvées dans les dépôts à 1,05 m/s, bien que des particules allant jusqu'à 25 μm se trouvaient dans la suspension de limon en écoulement. La taille maximale des particules dans le dépôt diminue avec l'augmentation de la vitesse du dépôt.