Surface tensions and contact angles due to lignin sulphonates in the system: Liquid sulphur, aqueous zinc sulphate and zinc sulphide

Authors


Abstract

Surface tension and contact angle measurements were made in the liquid sulphur-aqueous zinc sulphate-zinc sulphide system at superatmospheric pressures, and showed that, in the absence of surfactants, the liquid sulphur-aqueous solution interfacial tension was 54.0 ± 1.0 mN/m, falling to 27.0-30.0 mN/m when 0.3 g/L or more of lignin sulphonate was added to the solution. At the same time, the contact angle between liquid sulphur and the same solution increased from 80 ± 5° to 148 ± 5°. As a result, the work of adhesion between liquid sulphur and zinc sulphide falls from 63.7 mJ/m2 to about 5.3 mJ/m2. The results indicate that adsorption of lignin sulphonate occurs on both the mineral-aqueous and the sulphur-aqueous interfaces.

Abstract

On a effectué des mesures de tension de surface et d'angle de contact dans un système soufre liquid-sulfate de zinc aqueux-sulfure de zinc, à des pressures super-atmosphériques et on montre qu'en l'absence de surfactants, la tension interfaciale du soufre liquide avec la solution aqueuse est de 54,0 ± 1,0 mN/m, tombant à 27, 0-30,0 mN/m lorsqu'on ajoute 0,3 g/L de sulfonate de lignine à la solution. En même temps, l'angle de contact entre le soufre liquide et la même solution augmente de 80 ± 5° à 148 ± 5°. Par conséquent, le travail d'adhésion entre le soufre liquide et le sulfure de zinc tombe de 63,7 mJ/m2 à environ 5,3 mJ/m2. Les résultats indiquent que l'adsorption du sulfonate de lignine survient dans les deux interfaces minéral-aqueux et soufre-aqueux.

Ancillary