Kinetic parameters for decomposition of calcium carbonate

Authors


Abstract

The intrinsic reaction rate constant for calcium carbonate decomposition was determined based on a structural model (grain model). Experiments were conducted with thin slab type pellets (thickness 0.044 - 0.086 cm) in the temperature range of 670-740°C under isothermal conditions for determining the rate constant. The effective diffusivity, effective thermal conductivity, and heat and mass transfer coefficients were determined from experimental data obtained from cylindrical pellets (L/D ≈ 1) at 840 and 875°C, taking into consideration the temperature variations in the solid. The results obtained are in good agreement with the values reported in literature.

Abstract

On a déterminé la constante de vitesse de réaction intrinsèque pour la décomposition du carbonate de calcium à partir ďun modèle structural (modèle de grain). Des expériences ont été réalisées avec des pastilles minces de type de plaques (épaisseur de 0,044 à 0,086 cm) pour des températures comprises entre 670 et 740 °C dans des conditions isothermes afin de déterminer la constante de vitesse. La diffusivité efficace, la conductivité thermique efficace et les coefficients de transfert de matière et de chaleur ont été déterminés à partir de données expérimentales obtenues avec des pastilles cylindriques (L/D ≈ 1) à 840 et 875°C, en prenant en considération les variations de températures dans le solide. Les résultats obtenus montrent un bon accord avec les valeurs publiées dans la littérature scientifique.

Ancillary