  • nickel electrode;
  • oxygen evolution;
  • reaction electrodeposition;
  • electrocatalysis

Abstract

Nickel electrodes were prepared by electrodeposition in electrolytes of various anionic compositions. The deposition conditions and bath types were evaluated with special emphasis on the electrocatalytic properties for the oxygen evolution reaction (OER). Electrochemical characterizations in a 5 mol/L KOH solution at 25°C showed that the electrode deposited from the chloride bath, having a low Tafel slope of 50 mV/dec and an overpotential of 396 mV at 100 mA/cm2, is the most catalytically active among electrodes prepared in electrolytes of various anionic compositions. The electrode activity for the OER is related to the real surface areas, which depend on the anion compositions in the deposition bath and the deposition conditions.

Des électrodes de nickel ont été préparérs par électrodéposition dans des solutions de différentes composition anionique. Les conditions de déposition ainsi que les types de bains ont été évalus à ľaide de leurs caractéristiques électrocatalytiques pour la reaction de dégagement ďoxygène. II a été montré lors des caractérisations électrochimiques effectuées dans une solution 5 mol/L KOH à 25°C, que ľélectrode déposée en utilisant un bain chloruré et ayant une pente de Tafel de 50 mV/décade ainsi q'une surtension de 396 mV à 100 mA/cm2, présente la meilleure activité catalytique. Ľactivité catalytique des électrodes de Ni pour le dégagement ďoxygène dépend de la présence de fissures à la surface de celles-ci et dont la quantité varie en fonction des conditions de déposition et du bain utilisé.