In situ laser raman spectroscopy during sequential oxidizing and reducing conditions for a vanadium-phosphorous-oxide catalyst

Authors


Abstract

A VPO catalyst prepared in an organic medium has been studied by in situ laser Raman spectroscopy for n-butane oxidation to maleic anhydride. Data could be obtained at low laser power and brief collection times. Raman characterization during continuous flow (steady-state) studies revealed that (VO)2P2O7 was present. Sequential oxidizing (10% O2 in N2) and reducing (2% n-butane in N2) conditions were explored at 350°C and 400°C. These cycling (unsteady-state) operations revealed that formation of V(5+) phases was enhanced during oxidizing conditions. The intensity of Raman bands due to (VO)2P2O7 increased during reducing conditions.

Abstract

Un catalyseur VPO préparé dans un milieu organique a été étudie par spectroscopie Raman au laser in situ pour l'oxydation du n-butane en anhydride maléique. Des données ont pu ětre obtenues à une faible puissance du laser et à des temps d'acquisition brefs. La caractérisation Raman durant les études d'écoulement continu (régime permanent) révèlent la présence de (VO)2P2O7. Des conditions séquentielles d'oxydation (10%O2 dans N2) et de réduction (2%n-butane dans N2) ont été explorées à 350°C et 400°C. Ces opérations de recyclage (régime permanent) montrent que la formation des phases V(5+) est augmentée dans les conditions d'oxydation. L'intensité des bandes Raman dues à (VO)2P2O7 augmente dans les conditions de réduction.

Ancillary