Increase in the thermal stability during the methanation of CO2 over a Rh catalyst prepared from an amorphous alloy

Authors


Abstract

The hydrogenation of CO2 was investigated over a Rh catalyst prepared from an amorphous Rh20Zr80 alloy. After the reaction, the catalyst was regenerated by oxidation in air and reduction in H2. It was observed that the reaction activity increased with the repetition of regeneration. We also prepared the Rh/ZrO2 catalyst by the conventional impregnation method. The difference in the turnover frequency between the alloy-precursor catalyst and the conventionally prepared catalyst was small. For the alloy-precursor catalyst, however, the conversion and CH4 selectivity were stable at 723 K, whereas the conversion and CH4 selectivity decreased with time-on-stream even at 673 K for the catalyst prepared by the conventional impregnation method.

Abstract

On a étudié l'hydrogénation du CO2 sur un catalyseur Rh préparé à partir d'un alliage amorphe Rh20Zr80. Après la réaction, le catalyseur a été régénéré par oxydation dans l'air et réduction du H2. On a observé que l'activité de la réaction augmentait avec la répétition de la régénération. Le catalyseur Rh/ZrO2 a également été préparé par la méthode d'imprégnation classique. La différence dans la fréquence de renouvellement entre le catalyseur alliage-précurseur et le catalyseur préparé selon la méthode conventionnelle était faible. Cependant, pour le catalyseur alliage-précurseur, la conversion et la sélectivité du CH4 étaient stables à 723 K, tandis que la conversion et la sélectivité du CH4 diminuaient avec le temps d'utilisation même à 673 K pour le catalyseur préparé par la méthode d'imprégnation classique.

Ancillary