Keywords:

  • melting temperatures;
  • copolymer;
  • branching;
  • molecular weight

Abstract

A generalized equation was derived to calculate the melting temperatures of homopolymers and copolymers. The Gibbs-Thomson equation for homopolymers and a modified application to copolymers were derived using the proposed equation. The melting temperature Tm0 in the Flory equation corresponds to the melting temperature TmC,∞ of copolymer crystals with stems of infinite length. Also, TmC,n*, the melting temperature for copolymer crystals with stems containing the maximum possible number of structural units, n*, should be used instead of Tm0 as the basis of supercooling in crystallization. The proposed equation shows good agreement with experimental data for α-alkene-ethylene homogeneous copolymers.

Une équation généralisée a été proposée pour calculer les températures de fusion d' homopolymères et copolymères. L'équation de Gibbs-Thomson pour les homopolymères et une équation modifiée pour les copolymères ont été obtenues à partir de l'équation proposée. La température de fusion Tm0 dans l'équation de Flory correspond à la température de fusion TmC,∞ des cristaux de copolymères ayant une taille infinie. De plus, TmC,n*, la température de fusion pour des cristaux de copolymères contenant le nombre maximum possible d'unités structurales, n*, devrait être utilisée à la place de TmO comme la base de sous-refroidissement pour la cristallisation. L'équation proposée est en bon accord avec les données expérimentales pour les copolymères homogènes d'α-alcène-éthylène.