Polymer-Clay Nanocomposites Based on Blends of Polyamide-6 and Polyethylene

Authors


Abstract

The preparation of polyamide-6/clay, high-density polyethylene/clay, and high-density polyethylene/ polyamide-6/clay nanocomposites is considered. X-ray diffraction (XRD), differential scanning calorimetry (DSC), and Fourier Transform Infrared (FTIR) measurements show that the clay enhances the crystallization of the γ-form of polyamide-6. The clay also acts as a nucleation agent and causes a reduction of spherulitte size. Scanning electron microscopy (SEM) analysis of fracture surfaces shows that the clay reduces the PA-6 particle size in the HDPE/PA-6/clay nanocomposites and changes the morphology. Mechanical properties and the effect of maleated polyethylene are also reported.

Abstract

On considère la préparation de nanocomposites de polyamide-6/argile, de polyéthylène/argile de haute densité et de polyéthylène/polyamide-6/argile de haute densité. Des mesures de diffraction aux rayons X (XRD), de calorimétrie à balayage différentielle (DSC) et de spectroscopie infrarouge à transformée de Fourier (FTIR) montrent que l'argile améliore la cristallisation de la forme γ du polyamide-6. L'argile agit également comme agent de nucléation et entraîne une réduction de taille des sphérolites. L'analyse par microscopie électronique à balayage (SEM) des surfaces de fractures montre que l'argile réduit la taille des particules de PA-6 dans les nanocomposites HDPE/PA-6/argile et modifie leur morphologie. Les propriétés mécaniques et l'effet du polyéthylène maléaté sont également décrits.

Get access to the full text of this article

Ancillary