SEARCH

SEARCH BY CITATION

Keywords:

  • molten salt oxidation;
  • halogenated plastics;
  • metal partitioning;
  • particle size distribution

Abstract

Halogenated plastics such as PVC pipe, PTFE tube, and latex gloves were test-burned in a bench-scale molten salt oxidation reactor. Hydrogen halides (HCl and HF) and free halogens (Cl2 and F2) first released by the thermal decomposition of halogenated plastics (PVC and PTFE) were nearly completely collected in the hot sodium carbonate salt bath. Compared to halogen collection, sulfur collection was not complete and SO2 emission for rubber gloves decreased with stoichiometric air ratio. The entrainment of spiked metals and their fraction in the sub-micron particle size range increased with the chlorine content as well as the operating temperature.

Des plastiques halogénés comme les conduites en PVC et les tubes en PTFE, ainsi que des gants de latex, ont été brûlés dans un réacteur d'oxydation à sels fondus à l'échelle de laboratoire. Les halogénures d'hydrogène (HCl et HF) et les halogènes libres (Cl2 et F2) d'abord libérés par la décomposition thermique des plastiques halogénés (PVC et PTFE) ont été presque entièrement recueillis dans le bain de sel de carbonate de sodium chaud. Contrairement à la collecte des halogènes, la collecte du soufre n'est pas complète et l'émission de SO2 pour les gants de caoutchouc diminue avec le taux d'air stoechiométrique. L'entraînement de pointes de métal et la quantité de pointes de taille sub-micronique augmentent avec la teneur en chlore tout comme avec la température de fonctionnement.