Kinetics of Silica Dissolution from Rice Husk Char

Authors


Abstract

The effect of leaching time and temperature on the ash content of rice husk char and the resultant surface area development was investigated. Experiments on dissolution of rice husk char ash with 0.5 mol NaOH solution were conducted at 40°C, 60°C, 80°C and 95°C for different times up to 7200 s. The surface areas of the leached chars after drying were determined using Micromeritics 2200 surface area analyzer. The leaching data was analyzed using different models applicable for fluid-solid non-catalytic reactions. It was found that the data could be satisfactorily represented by diffusion-controlled mechanism as well as modified shrinking core models. The activation energies were in the range of 41.75 to 51.25 kJ/mole. The surface areas of the leached chars were found to depend linearly on the percentage of ash content in the chars.

Abstract

On a étudié l'effet du temps de lessivage et de la température sur la teneur en cendres de cosses de riz carbonisées et le développement de surface qui en résulte. Des expériences ont été menées sur la dissolution des cendres de cosses de riz avec une solution de NaOH de 0,5 mole à 40 ºC, 60 ºC, 80 ºC et 95 ºC pour différents temps allant jusqu'à 7200 sec. Les aires de surfaces des cendres après le séchage ont été déterminées à l'aide d'un analyseur de surface 2200 de Micromeritics. Les données de lessivage ont été analysées à l'aide de différents modèles applicables à des réactions fluide-solide non catalytiques. On a trouvé que les données pouvaient être représentées de manière satisfaisante par le mécanisme contrôlé par la diffusion et par les modèles de noyau rétrécissant modifiés. Les énergies d'activation sont comprises entre 41,75 et 51,25 kJ/mole. On a trouvé que les aires de surfaces des cendres lessivées dépendaient linéairement du pourcentage de teneur en cendres dans les produits carbonisés.

Ancillary