Keywords:

  • CdZnTe;
  • passivation;
  • XPS;
  • surface leakage current

Abstract

The chemical etching and the passivation processes of CdZnTe wafers were studied. The treatment effects were tested through an X-Ray Photoelectron Spectroscopy (XPS) analysis and I–V measurement. The chemical etching in 2%Br–MeOH solution may effectively remove the damaged layer and improve the ohmic contact between CdZnTe wafer and Au electrodes making rich the surface with Te. After different etching times, the CdZnTe wafers were passivated with NH4F/H2O2.CdZnTe wafer passivated immediately after etching showed the best passivation efficiency because the enriched Te on the surface was fully oxidized to TeO2, which results in the thickest oxide layer, and the most stoichiometric surface. Also the surface leakage current was reduced in comparison with the sample passivated 24 h after etching. (© 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim)