Electrochemical study of nanostructured electrode for low-temperature solid oxide fuel cell (LTSOFC)



Zn-based nanostructured Ba0.05Cu0.25Fe0.10Zn0.60O (BCFZ) oxide electrode material was synthesized by solid-state reaction for low-temperature solid oxide fuel cell. The cell was fabricated by sandwiching NK-CDC electrolyte between BCFZ electrodes by dry press technique, and its performance was assessed. The maximum power density of 741.87 mW-cm−2 was achieved at 550°C. The crystal structure and morphology were characterized by X-ray diffractometer (XRD) and SEM. The particle size was calculated to be 25 nm applying Scherer's formula from XRD data. Electronic conductivities were measured with the four-probe DC method under hydrogen and air atmosphere. AC Electrochemical Impedance Spectroscopy of the BCFZ oxide electrode was also measured in hydrogen atmosphere at 450°C. Copyright © 2013 John Wiley & Sons, Ltd.