Exploring the possible interlinked structures in single-wall carbon nanotubes under pressure by Raman spectroscopy


  • Shuangchen Lu,

  • Mingguang Yao,

  • Quanjun Li,

  • Hang lv,

  • Dedi Liu,

  • Bo Liu,

  • Ran Liu,

  • Linhai Jiang,

  • Zhen Yao,

  • Zhaodong Liu,

  • Bo Zou,

  • Tian Cui,

  • Bingbing Liu

    Corresponding author
    • State Key Laboratory of Superhard Materials, Jilin University, Changchun, China
    Search for more papers by this author

Correspondence to: Bingbing Liu, State Key Laboratory of Superhard Materials, Jilin University, Changchun 130012, China



High-pressure Raman measurements on single-wall carbon nanotubes (SWNTs) have been carried out in a diamond anvil cell by using two wavelength lasers: 830 and 514.5 nm. Irrespective of using a pressure transmitting medium (PTM) or not, we found that nanotubes undergo similar transformations under pressure. The pressure-induced changes in Raman signals at around 2 and 5 GPa are attributed to the nanotube cross-section transitions from circle to ellipse and then to a flattened shape, respectively. Especially with pressure increasing up to 15–17 GPa, we observed that the third transition takes place in both the Raman wavenumber and the linewidth of G-band. We propose explanations that the interlinked configuration with sp3 bonds forms in the bundles of SWNTs under pressure, which was the cause for the occurrence of those Raman anomalies, similar to the structural-phase transition of graphite above 14 GPa. Our TEM observations and Raman measurements on the decompressed samples support this transition picture. Copyright © 2012 John Wiley & Sons, Ltd.