Corrosion of stainless steel grades in H2O/KOH 50% at 120 °C: AISI304 austenitic and 2205 duplex
Article first published online: 2 MAR 2012
Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
Materials and Corrosion
Volume 64, Issue 11, pages 988–995, November 2013
How to Cite
Bozzini, B., Bogani, F., Giovannelli, G., Natali, S., Scarselli, G. and Boniardi, M. (2013), Corrosion of stainless steel grades in H2O/KOH 50% at 120 °C: AISI304 austenitic and 2205 duplex. Materials and Corrosion, 64: 988–995. doi: 10.1002/maco.201106469
- Issue published online: 8 NOV 2013
- Article first published online: 2 MAR 2012
- Manuscript Accepted: 2 JAN 2012
- Manuscript Received: 6 DEC 2011
Options for accessing this content:
- If you have access to this content through a society membership, please first log in to your society website.
- If you would like institutional access to this content, please recommend the title to your librarian.
- Login via other institutional login options http://onlinelibrary.wiley.com/login-options.
- You can purchase online access to this Article for a 24-hour period (price varies by title)
- If you already have a Wiley Online Library or Wiley InterScience user account: login above and proceed to purchase the article.
- New Users: Please register, then proceed to purchase the article.
Type your institution's name in the box below. If your institution is a Wiley customer, it will appear in the list of suggested institutions and you will be able to log in to access content. Some users may also log in directly via OpenAthens.
Please note that there are currently a number of duplicate entries in the list of institutions. We are actively working on fixing this issue and apologize for any inconvenience caused.
Registered Users please login:
- Access your saved publications, articles and searches
- Manage your email alerts, orders and subscriptions
- Change your contact information, including your password
Please register to:
- Save publications, articles and searches
- Get email alerts
- Get all the benefits mentioned below!