Keywords:

  • hot corrosion;
  • nanostructured ceramic;
  • thermal barrier coating;
  • yttria stabilized zirconia

Thermal barrier coatings of nanostructured and microstructured yttria stabilized zirconia (YSZ) were deposited on GH4049 substrate by air plasma spray, respectively. Hot corrosion behaviors of both coatings were evaluated in comparative aspects. Results revealed that the nanostructured YSZ displayed higher resistance to the hot corrosion attack by Na2SO4 and V2O5. It was also shown, through X-ray diffraction quantitative phase analysis, that the nanostructured YSZ had good resistance to the tetragonal-monoclinic phase transformation during the hot corrosion process.