Keywords:

  • adamantane;
  • cationic polymerization;
  • cyclopolymer;
  • cyclopolymerization;
  • divinyl ether;
  • glass transition temperature;
  • norbornane;
  • norbornene;
  • vinyl ether

ABSTRACT

Cationic cyclopolymerizations of 2,2-bis(vinyloxymethyl)bicyclo[2.2.1]heptane (1), 5,5-bis(vinyloxymethyl)-2-bicyclo[2.2.1]heptene (2), and 2,2-bis(vinyloxymethyl)tricyclo[3.3.1.1]3, 7decane (3), divinyl ethers with a norbornane, norbornene, or adamantane unit, respectively, were investigated with the HCl/ZnCl2 initiating system in toluene and methylene chloride at −30 °C. All the reactions proceeded quantitatively to give gel-free, soluble polymers in organic solvents. The number-average molecular weight (Mn) of the polymers increased in direct proportion to monomer conversion and further increased on addition of a fresh monomer feed to the almost completely polymerized reaction mixture. The contents of the unreacted vinyl groups in the produced soluble polymers were less than ∼10 mol %, and therefore, the degree of cyclization of the polymers was determined to be over ∼90%. These facts show that cyclopolymerization of 1, 2, and 3 exclusively occurred and the poly(vinyl ether)s with the cyclized repeating units and polycyclic pendants were obtained with their molecular weights being regulated. BF3OEt2 initiator also caused cyclopolymerization of 1, 2, and 3 to give the corresponding high-molecular-weight cyclopolymers quantitatively. Glass transition temperatures (Tg's) of poly(1) and poly(2) were 165–180 °C, and Tg's of poly(3) were 211–231 °C; these values are very high as vinyl ether polymers. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 2445–2454