In situ measurement using FBGs of process-induced strains during curing of thick glass/epoxy laminate plate: experimental results and numerical modelling
Article first published online: 17 SEP 2012
Copyright © 2012 John Wiley & Sons, Ltd.
Volume 16, Issue 8, pages 1241–1257, November 2013
How to Cite
Nielsen, M. W., Schmidt, J. W., Hattel, J. H., Andersen, T. L. and Markussen, C. M. (2013), In situ measurement using FBGs of process-induced strains during curing of thick glass/epoxy laminate plate: experimental results and numerical modelling. Wind Energ., 16: 1241–1257. doi: 10.1002/we.1550
- Issue published online: 14 NOV 2013
- Article first published online: 17 SEP 2012
- Manuscript Accepted: 28 JUL 2012
- Manuscript Revised: 24 JUL 2012
- Manuscript Received: 24 APR 2012
- shape distortions;
- numerical analysis;
- process monitoring;
For large composite structures, such as wind turbine blades, thick laminates are required to withstand large in-service loads. During the manufacture of thick laminates, one of the challenges met is avoiding process-induced shape distortions and residual stresses. In this paper, embedded fibre Bragg grating sensors are used to monitor process-induced strains during vacuum infusion of a thick glass/epoxy laminate. The measured strains are compared with predictions from a cure hardening instantaneous linear elastic (CHILE) thermomechanical numerical model where different mechanical boundary conditions are employed. The accuracy of the CHILE model in predicting process-induced internal strains, in what is essentially a viscoelastic boundary value problem, is investigated. A parametric study is furthermore performed to reveal the effect of increasing the laminate thickness. The numerical model predicts the experimental transverse strains well when a tied boundary condition at the tool/part interface is used and the tool thermal expansion is taken into account. However, the CHILE approach is shown to overestimate residual strains after demoulding because of the shortcomings of the model in considering viscoelastic effects. The process-induced strain magnitude furthermore increases when the laminate thickness was increased, owing mainly to a decrease in through-thickness internal transverse stresses. Copyright © 2012 John Wiley & Sons, Ltd.