Lead-free (Na0.52K0.48−x)(Nb1−xySby)O3-xLiTaO3 (NKNS–LT) piezoelectric ceramics have been fabricated by ordinary sintering. A special attention was paid to the composition design through which the dielectric and piezoelectric properties of the (Li, Ta, Sb) modified NKN systems were significantly promoted. A property spectrum was generated with a particular discussion on the relationship between the Sb content, the LT content, the polymorphic phase transition, and the electrical properties and their temperature stability. Excellent and tunable electrical properties of d33=242–400 pC/N, kp=36%–54%, inline image, and Tc=230°–430°C demonstrate a tremendous potential of the compositions studied for device applications.


I. Introduction

  1. Top of page
  2. Abstract
  3. I. Introduction
  4. II. Experimental Procedures
  5. III. Results and Discussion
  6. IV. Conclusions
  7. References

The research and development of lead-free piezoelectric ceramics have been a hot topic since Saito et al.1 made good progress in the electrical properties in 2004. A flood of relevant publications have come forth in the last few years.2–4 A typical composition, (Na0.5K0.5)NbO3 (NKN), near a morphotropic phase boundary (MPB) has absorbed much attention owing to its good electrical properties, together with a relatively high Curie temperature.5 Pure NKN compositions demonstrate a polymorphic phase transition (PPT) at ∼200°C, except for a ferroelectric–paraelectric phase transition at ∼420°C.5 Although it is well known in pure NKN materials for last 50 years, the PPT was reported in modified NKN-based lead-free materials in 20066 where it was shifted below room temperature by the addition of Li, Ta, and/or Sb, such that a two-phase coexistence zone between orthorhombic and tetragonal phases was formed.7 This zone can be more appropriately called as the polymorphic phase boundary (PPB), not just a classical MPB, because this boundary is strongly dependent on temperature. However, similar to an MPB, two kinds of ferroelectric phases may coexist near a PPB. Therefore, the (Li, Ta, Sb) modified NKN compositions exhibit not only significantly improved sinterability but also enhanced electrical properties. However, the best properties reported so far for this system are still not as good as expected, in addition to both processing difficulties and temperature stability issues.2,8 Particularly, the piezoelectric constant d33 (∼300 pC/N)1 and the electromechanical coupling factor kp (∼45%) values have wandered at this level for quite a long time. Obviously, it is indispensable to further promote these properties in order to compete with lead-based piezoelectric materials. It has been realized that the relative content of Li, Ta, and Sb made a difference in changing the electrical properties of NKN-based systems,1 although the existence of a PPB was believed to be the main reason for the enhanced electrical properties of this system.8 It was pointed out that more covalent elements, for example, Sb, owing to higher electronegativities, could contribute more to the dielectric and piezoelectric properties.1

In this work, a special attention was paid to the composition design by prescribing a fixed amount of Sb in NKN compositions and then mixing with a changing amount of LiTaO3 (LT). The phase transformation and various electrical properties as a function of the Sb and LT content were investigated. A property spectrum concerning this material system was reported, among which the compositions with significantly improved piezoelectric properties and/or tunable properties were demonstrated.

II. Experimental Procedures

  1. Top of page
  2. Abstract
  3. I. Introduction
  4. II. Experimental Procedures
  5. III. Results and Discussion
  6. IV. Conclusions
  7. References

Ceramics with compositions of (Na0.52K0.48−x)(Nb1−xySby)O3-xLiTaO3 (NKNS–LTx/y) (0<x<0.07, 0<y<0.16) were manufactured by a solid-state reaction method. Based on that Na volatilizes more drastically than K at high temperature, a bit more Na was used in the initial compositions. Na2CO3 (99.8%), K2CO3 (99.0%), Li2CO3 (99.9%), Nb2O5 (99.5%), Ta2O5 (99.9%), and Sb2O3 (99.9%) were used as raw materials. After mixing and drying, the powder mixtures were calcined twice at 850°C for 5 h, followed by a ball milling for 24 h. The dried powders were then compacted into disk samples with desired aspect ratios and then sintered in air at 1060°–1120°C for 3 h.

Silver paste was fired on major surfaces at 550°C for 30 min as the electrodes for dielectric and piezoelectric measurements. The samples were poled at 110°C in stirred silicone oil by applying a dc field of 2 kV/mm for 15 min. The crystal structure was examined by an X-ray diffractometer (D/Mzx-rB, Rigaku, Tokyo, Japan) using a CuKα radiation. Dielectric properties were measured as a function of temperature by a LCR meter (Agilent E4980A, Santa Clara, CA). The piezoelectric strain constant d33 was measured by a Belincourt-meter (YE2730A, SINOCERA, Yangzhou, China). The planar electromechanical coupling factor kp were determined by a resonance–antiresonance method with an impedance analyzer (PV70A, Band ERA Co. Ltd., Beijing, China).

III. Results and Discussion

  1. Top of page
  2. Abstract
  3. I. Introduction
  4. II. Experimental Procedures
  5. III. Results and Discussion
  6. IV. Conclusions
  7. References

Figure 1 shows the X-ray diffraction patterns of NKNS compositions. For y<0.09, only phases with a perovskite structure are detected. A secondary phase K2Sb2O7 (ICDD: 44-0927) starts to appear at x=0.1, meaning that the solubility limit of Sb in the NKN lattice has been reached, owing to different structures of (Na,K)SbO3 (pseudoilmenite structure) and (Na,K)NbO3 (perovskite structure). A small amount of Sb can diffuse into the NKN lattice but seems to reduce its orthorhombicity within the studied composition range at room temperature, probably due to the coexistence of orthorhombic and tetragonal phases in a PPT system.

image

Figure 1.  X-ray diffraction patterns of (Na0.52K0.48)(Nb1−ySby)O3 ceramics with different y values as indicated. The symbol of stars stands for the secondary phases.

Download figure to PowerPoint

The effect of the Sb substitution on the phase structures of NKN ceramics can be also clarified by measuring the curves of the dielectric constant versus temperature, as summarized in Fig. 2. Similar to pure NKN ceramics,3,9 the Sb substituted NKN ceramics exhibit two phase transition points above room temperature: the orthorhombic–tetragonal (To−t) polymorphic phase transition and the tetragonal–cubic ferroelectric phase transition (Tc). It can be seen that Tc rapidly drops with increasing y and To−t decreases with y as well but at a relatively low speed (average 20° and 15°C/mol% Sb for Tc and To−t, respectively), such that the tetragonal zone has become narrow at the temperature scale. When y=0.1, the material becomes weakly orthorhombic at room temperature. On the one hand, it can be expected that further addition of Sb will not evidently influence these two transition points (Fig. 2), probably owing to the solubility limit of Sb in the NKN lattice. On the other hand, although the diffraction peaks (202) and (020) for NKNS ceramics with y≥0.07 seem to merge into a single peak (Fig. 1), their phase structures should belong to the coexistence of orthorhombic and tetragonal phases at room temperature (Fig. 2).

image

Figure 2.  Phase transformation of (Na0.52K0.48)(Nb1−ySby)O3 ceramics with changing the content of Sb.

Download figure to PowerPoint

Figure 3 shows the effect of the LT and Sb content on the phase transition behavior of NKNS–LT ceramics. For all compositions with varying content of Sb, there exists a phase transformation zone with a certain width between orthorhombic and tetragonal phases. The shadow in Fig. 3 corresponds to the PPB zone where there may coexist two kinds of ferroelectric phases with different symmetries.7 It can be seen that the phase structure of pure NKN ceramics (y=0) gradually transforms from an orthorhombic symmetry to a tetragonal symmetry as the LT content becomes more. With increasing the Sb content, the PPB zone slightly tilts down, meaning that less amount of LT is needed to induce a phase transformation. It can be realized that the formation of the PPB is actually through shifting a polymorphic phase transition To−t of NKNS compositions below room temperature. A small amount of LT with an ilmenite structure can diffuse into the perovskite NKN lattice to form solid solutions but tends to induce a change in the crystal symmetry of the matrix compositions.10

image

Figure 3.  Polymorphic phase transition of NKNS–LTx/y ceramics with changing the content of Sb (y) and LiTaO3 (x), together with d33 values for compositions within the polymorphic phase boundary (PPB) zone.

Download figure to PowerPoint

Various electrical properties as a function of the Sb content for poled PPB NKNS–LT ceramics are shown in Fig. 4. It can be seen that the dielectric, piezoelectric, and electromechanical properties almost linearly increase with increasing the Sb content in the compositions. It is noticeable that the d33 values increase averagely by 21 pC/N/mol% Sb. The partial substitution of Sb for Nb induces a more pronounced piezoelectric activity, which can be partially attributed to the enhancement of the dielectric properties or the increase in the polarity due to higher electronegativity of Sb than Nb.11 However, the Curie temperatures quickly decline with increasing the content of Sb. The average rate was estimated to be 20°C/mol% Sb. The results indicate that the tunability of the piezoelectric properties for NKNS–LT ceramics can be realized through a special composition design. The d33 values in the range of 242–400 pC/N can be achieved. By comparison, kp exhibits a different change, being saturated at ∼7% Sb, and then reaching a plateau. The different behaviors of d33 and kp account for two effects existed in the compositions: the enhancement of the dielectric properties owing to the addition of Sb, and the formation of the PPB. The change in kp can be believed to have less correlation with the dielectric properties. Therefore, kp will not obviously benefit from the addition of more Sb. However, both the enhancement of dielectric constants and the formation of the PPB can significantly promote the piezoelectric activity. Moreover, it can be seen from Fig. 3 that d33 exhibits a curved surface distribution and is relatively high at the tetragonal side for the PPB compositions, although it always reaches the optimum values near the PPB owing to the phase coexistence.7

image

Figure 4.  Antimony concentration dependence of various electrical properties for poled polymorphic phase boundary (PPB) NKNS–LTx/y ceramics. Note that for each PPB composition, the content of Sb (y) is different but fixed aforehand.

Download figure to PowerPoint

The thermal de-poling behavior of poled PPB NKNS–LT ceramics is shown in Fig. 5. The d33 values were measured at room temperature after annealing the samples at varying chosen annealing temperatures (Ta) for 20 min. Samples are open circuited during annealing but short circuited before d33 is remeasured. It can be found that the d33 values for three compositions show a slight variation when Ta is <Tc and vanish rapidly as Ta gets close to Tc. The first stage can be ascribed to the existence of the PPB, which may induce the temperature instability of piezoelectric properties.8,12 However, it is not serious for these three compositions probably because they lie close to the tetragonal side. This explains why the best values of d33 do not appear in the middle of the PPB but close to the tetragonal phase side (see Fig. 3). The poled compositions within the PPB will undergo a polymorphic phase transition during annealing, such that part of polarization vectors may vanish. This can be considered as one reason for the temperature instability of the (Li, Ta, Sb) modified NKN compositions. However, the post-poled compositions at the tetragonal side will not undergo a tetragonal–orthorhombic polymorphic phase transition during cooling to room temperature or reheating above room temperature. Furthermore, the second stage is just typical of a ferroelectric material whose piezoelectric properties should disappear above the Curie temperature where it becomes a paraelectric state. Therefore, the thermal depoling behavior reveals a relationship between the phase structure of compositions and the reliability of electrical properties.

image

Figure 5.  Piezoelectric constants d33 as a function of temperature for poled polymorphic phase boundary (PPB) NKNS–LTx/y ceramics with x and y indicated.

Download figure to PowerPoint

IV. Conclusions

  1. Top of page
  2. Abstract
  3. I. Introduction
  4. II. Experimental Procedures
  5. III. Results and Discussion
  6. IV. Conclusions
  7. References

Lead-free NKNS–LT piezoelectric ceramics were successfully manufactured with a special attention to the composition design. Excellent and tunable dielectric, piezoelectric, and electromechanical properties of d33=242–400 pC/N, kp=36%–54%, inline image, and Tc=230°–430°C were achieved. The property spectrum was provided with a detailed discussion on the effect of the Sb content and the PPB on the piezoelectric properties and the temperature stability. The results demonstrate a tremendous advantage of this material system for device applications.

References

  1. Top of page
  2. Abstract
  3. I. Introduction
  4. II. Experimental Procedures
  5. III. Results and Discussion
  6. IV. Conclusions
  7. References
  • 1
    Y. Saito, H. Takao, T. Tani, T. Nonoyama, K. Takatori, T. Homma, T. Nagaya, and M. Nakamura, “Lead-Free Piezoceramics,” Nature, 432, 847 (2004).
  • 2
    E. Hollenstein, M. Davis, D. Damjanovic, and N. Setter, “Piezoelectric Properties of Li- and Ta-Modified (K0.5Na0.5)NbO3 Ceramics,” Appl. Phys. Lett., 87, 182905 (2005).
  • 3
    R. Z. Zuo, X. S. Fang, and C. Ye, “Phase Structures and Electrical Properties of New Lead-Free (Na0.5K0.5)NbO3–(Bi0.5Na0.5)TiO3 Ceramics,” Appl. Phys. Lett., 90, 092904 (2007).
  • 4
    T. Lee, K. W. Kwok, and H. L. W. Chan, “Preparation and Piezoelectric Properties of CeO2-Added (Na0.475K0.475Li0.05)(Nb0.92Ta0.05Sb0.03)O3 Lead-Free Ceramics,” J. Phys. D: Appl. Phys., 41, 155402 (2008).
  • 5
    R. Z. Zuo, J. Rodel, R. Z. Chen, and L. T. Li, “Sintering and Electrical Properties of Lead-Free Na0.5K0.5NbO3 Piezoelectric Ceramics,” J. Am. Ceram. Soc., 89, 20105 (2006).
  • 6
    S. J. Zhang, R. Xia, and T. R. Shrout, “Piezoelectric Properties in Perovskite 0.948(K0.5Na0.5)NbO3–0.052LiSbO3 Lead Free Ceramics,” J. Appl. Phys., 100, 104108 (2006).
  • 7
    L. Wu, J. L. Zhang, S. F. Shao, P. Zheng, and C. L. Wang, “Phase Coexistence and High Piezoelectric Properties in (K0.40Na0.60)0.96Li0.04Nb0.80Ta0.20O3 Ceramics,” J. Phys. D: Appl. Phys., 41, 035402 (2008).
  • 8
    S. J. Zhang, R. Xia, and T. R. Shrout, “Modified (K0.5Na0.5)NbO3 Based Lead Free Piezoelectrics with Broad Temperature Usage Range,” Appl. Phys. Lett., 91, 132913 (2007).
  • 9
    D. M. Lin, K. W. Kwok, H. Y. Tian, and H. L. W. Chan, “Phase Transitions and Electrical Properties of (Na1−xKx)(Nb1−ySby)O3 Lead-Free Piezoelectric Ceramics with a MnO2 Sintering Aid,” J. Am. Ceram. Soc., 90 [5] 145862 (2007).
  • 10
    Y. P. Guo, K. I. Kakimoto, and H. Ohsato, “(Na0.5K0.5)NbO3–LiTaO3 Lead-Free Piezoelectric Ceramics,” Mater. Lett., 59, 2414 (2005).
  • 11
    Y. F. Chang, Z. P. Yang, L. R. Xiong, Z. H. Liu, and Z. L. Wang, “Phase Structure, Microstructure, and Electrical Properties of Sb-Modified (K,Na,Li)(Nb,Ta)O3 Piezoelectric Ceramics,” J. Am. Ceram. Soc., 91, 22116 (2008).
  • 12
    E. K. Akdogan, K. Kerman, M. Abazari, and A. Safari, “Origin of High Piezoelectric Activity in Ferroelectric (K0.44Na0.52Li0.04)(Nb0.84Ta0.1Sb0.06)O3 Ceramics,” Appl. Phys. Lett., 92, 112908 (2008).