Member, The American Ceramic Society.
Effects of Postdensification Annealing upon Microstructures and Microwave Dielectric Characteristics in Ba((Co0.6−x/2Zn0.4−x/2Mgx)1/3Nb2/3)O3 Ceramics
Article first published online: 2 AUG 2013
© 2013 The American Ceramic Society
Journal of the American Ceramic Society
Volume 96, Issue 11, pages 3417–3424, November 2013
How to Cite
Ma, P. P., Yi, L., Liu, X. Q., Li, L., Chen, X. M. (2013), Effects of Postdensification Annealing upon Microstructures and Microwave Dielectric Characteristics in Ba((Co0.6−x/2Zn0.4−x/2Mgx)1/3Nb2/3)O3 Ceramics. Journal of the American Ceramic Society, 96: 3417–3424. doi: 10.1111/jace.12486
- Issue published online: 11 NOV 2013
- Article first published online: 2 AUG 2013
- Manuscript Accepted: 1 JUN 2013
- Manuscript Received: 7 APR 2013
- National Science Foundation of China. Grant Number: 11274270
- Chinese National Basic Research Program. Grant Number: 2009CB623302
Effects of postdensification annealing upon microstructures and microwave dielectric characteristics in Ba((Co0.6−x/2Zn0.4−x/2Mgx)1/3Nb2/3)O3 (x = 0, 0.1, 0.2, and 0.3) complex perovskite ceramics have been investigated. Long-time annealing at temperatures below the order–disorder transition temperature enhances the cation ordering degree and promotes the ordering domain growth. The most significant improvement of Qf value is obtained together with the suppressed temperature coefficient of resonant frequency in the samples annealed at 1400°C for 12 h, while the dielectric constant decreases slightly. The Qf value of ceramics annealed at 1400°C mainly attributes to the enhanced cation ordering degree, because their low-energy domain boundaries are not detrimental to the Qf value. As the annealing temperature increases close to the transition temperature, coarse ordering domains with high-energy boundaries are formed, and then the Qf value steadily decreases because of the inferior domain structure, even the cation ordering degree increases. The microwave dielectric characteristics of Ba((Co0.6−x/2Zn0.4−x/2Mgx)1/3Nb2/3)O3 ceramics are affected by the common function of ordering degree and domain structure. The best combination of microwave dielectric characteristics is obtained in the composition of x = 0.3 after annealing at 1400°C for 12 h: εr = 33.2, Qf = 117 200 GHz, and τf = 8.6 ppm/°C.