Turgor pressure in plant cells is involved in many important processes. Stable and normal turgor pressure is required for healthy growth of a plant, and changes in turgor pressure are indicative of changes taking place within the plant tissue. The ability to quantify the turgor pressure of plant cells in vivo would provide opportunities to understand better the process of pressure regulation within plants, especially when plant stress is considered, and to understand the role of turgor pressure in cellular signaling. Current experimental methods do not separate the influence of the turgor pressure from the effects associated with deformation of the cell wall when estimates of turgor pressure are made. In this paper, nanoindentation measurements are combined with finite element simulations to determine the turgor pressure of cells in vivo while explicitly separating the cell-wall properties from the turgor pressure effects. Quasi-static cyclic tests with variable depth form the basis of the measurements, while relaxation tests at low depth are used to determine the viscoelastic material properties of the cell wall. Turgor pressure is quantified using measurements on Arabidopsis thaliana under three pressure states (control, turgid and plasmolyzed) and at various stages of plant development. These measurements are performed on cells in vivo without causing damage to the cells, such that pressure changes may be studied for a variety of conditions to provide new insights into the biological response to plant stress conditions.
If you can't find a tool you're looking for, please click the link at the top of the page to "Go to old article view". Alternatively, view our Knowledge Base articles for additional help. Your feedback is important to us, so please let us know if you have comments or ideas for improvement.
Plant cell walls are complex and dynamic structures composed mainly of a network of extended polysaccharides, providing structural support and protection to the cell (Somerville et al., 2004). This structure acts as an effective pressure vessel for the plant, preventing over-expansion due to water uptake by osmosis (Gorshkova et al., 2010). The thickness, rigidity and viscoelastic behavior of the cell wall determine the size, shape, morphology and growth behavior of a plant. These parameters also determine the behavior of the cell wall with respect to the hydrostatic pressure of the cell, commonly known as turgor pressure (Nobel, 2005). The typical turgor pressure in plants is in the range of 0.3–1.0 MPa, a value that translates to between 10 and 100 MPa of tensile stress in the walls (Wei and Lintilhac, 2007). It has been recognized that cell enlargement occurs due to wall relaxation, a viscoelastic process that causes yielding of the matrix and allows the microfibrils to rearrange or move apart, leading to growth of the plant. Turgor pressure provides the driving force for the wall deformation that occurs as a result of such relaxation (Cosgrove, 2005). A recent study by Heisler et al. (2010) showed that morphogenesis during plant development is determined by intercellular signaling molecules as well as by the mechanical properties of individual cell walls. This process involves complex interactions between cell components such as the cell wall and cortical microtubules (Allard et al., 2010a,b; Zhang et al., 2011). The microtubules are greatly influenced by the strain on the cell wall caused by the stress differential across the wall (Hamant et al., 2011). The origin of this stress on the cell wall is the turgor pressure inside the cell. Therefore, turgor pressure, in association with altered mechanical properties of the cell wall, may be involved in cell-to-cell signaling and growth responses, as well as coordination between growth direction and growth magnitude (Ache et al., 2010; Heisler et al., 2010; Hamant et al., 2011; Shi et al., 2011). To understand these cellular properties, it is important for scientists to be able to quantify the turgor pressure of cells, as well as the corresponding wall stress values, especially with respect to any in vivo changes that may occur due to biological or environmental effects.
Mean turgor pressure may be determined from measurements on entire leaves using tools such as thermocouple psychrometers and pressure chambers (Mokter and Nonami, 2010) or from ultrasonic spectroscopy measurements (Sancho-Knapik et al., 2010). These methods quantify the water status of a given tissue but cannot be used to study single cells. Measurement of pressure in single cells was first performed using a pressure probe (Green and Stanton, 1967), in which a pipette is used to puncture the cell wall while the pressure in the pipette is monitored. This technique, which measures pressure in a direct manner, is now the conventional method for measuring turgor pressure in single cells. However, the pressure probe has its own limitations. First, it is a destructive test that requires the cell wall to be punctured, so it is difficult to quantify biological or environmental effects that influence turgor pressure in a particular cell. Second, it is difficult to apply this procedure to very small cells because the volume of sap entering the pipette must be much smaller than the total cell volume to allow the cell to reach equilibrium after insertion of the probe (Green and Stanton, 1967). Otherwise, measurement errors will be too large. Later methods were developed to quantify the turgor pressure of a single cell non-destructively by applying a compression load to the cell and monitoring the contact area with a microscope (Lintilhac et al., 2000; Wang et al., 2006). Lintilhac et al. (2000) used a glass ball to apply a load to the surface of onion cells. The projected area of the contact patch was captured by video microscopy. From the load and projected area, the pressure was estimated assuming a balance between the load and pressure (i.e. it was assumed that the cell wall does not support the load). Wang et al. (2006) compared the value obtained for turgor pressure in a single tomato cell using a pressure probe and a compression load applied using micro-manipulation. Although such procedures are in principle applicable at any scale, their use on small cells such as those of Arabi;?>dopsis is not practical because the contact patch is too small to measure via optical microscopy. In this study, a method is developed that uses nanoindentation to quantify turgor pressure in vivo in Arabidopsis leaf epidermis cells. The technique is similar to that described by Lintilhac et al. (2000) because it involves a tip in contact with the cell wall. A recent study by Routier-Kierzkowska et al. (2012) also involved use of a tip to deform the cell walls of onion cells. They used finite element simulations to interpret their results and to examine the behavior of cells as they recover from plasmolysis. Here, the tip is small enough that measurements on Arabidopsis cells are not difficult. In addition, the loads are small enough that the influence of the cell wall must be included in the analysis because the wall's resistance to shear and bending loads is important.
Nanoindentation has proven itself to be a powerful technique for measurement of mechanical properties in diverse biomaterials ranging from mineralized tissues to soft tissues (Ebenstein and Pruitt, 2004; Hoffler et al., 2005; Ebenstein et al., 2008). This technique has a high spatial resolution due to the small tip diameter. Quasi-static and dynamic tests may be performed on samples so that elastic and viscoelastic properties may be determined (Fischer-Cripps, 2002). From the load displacement data, mechanical properties such as hardness and elastic modulus may be determined (Johnson, 1985). Such measurements may also be obtained as a function of time, such that the viscoelastic behavior of a sample may be quantified. A commonly used method to characterize viscoelastic properties is the relaxation test, in which the indenter is kept at a constant indentation depth and the changing load is recorded over time (Yuya et al., 2010). Another method, the dynamic nanoindentation technique, uses a small sinusoidal force that is superimposed with the applied quasi-static force to the indenter (Zhang et al., 2008). The dynamic nanoindentation method was recently used to quantify the viscoelastic properties of plant cell walls in vivo (Hayot et al., 2012).
In this paper, nanoindentation measurements are combined with finite element simulations to determine the turgor pressure of Arabidopsis cells in vivo. Quasi-static cyclic tests with variable depth form the basis for the measurements, and relaxation tests are used to determine the viscoelastic material properties of the cell wall. We hypothesize that low-depth measurements will be most sensitive to the cell-wall properties, while large-depth measurements will be most sensitive to the turgor pressure. This hypothesis is based on similar behavior associated with thin films deposited on substrates. As shown by others (Tsui and Pharr, 1999; Saha and Nix, 2002; Tricoteaux et al., 2010), low-depth indentations on thin films may be used to extract properties of the films. However, when the indentation depth is beyond a certain depth, the measurements are influenced greatly by the substrate properties. In our study, the response of the pressurized cell is analogous to the thin film problem, in which the cell wall plays the role of the film and the pressure boundary condition is analogous to the substrate: once the depth is large enough, the turgor pressure will influence the measurements. Therefore, a cyclic depth-dependent measurement will include the response of all important components.
In this study, initial nanoindentation experiments were performed in quasi-static mode using a spherical tip with 2.5 μm radius (so that the tip geometry is known). Feedback control testing, in displacement-controlled mode, provided precise control of the tip location with respect to the sample. The tip was first engaged with the sample to a prescribed initial load (here 2 μN). A displacement control function (displacement–time curve) was then defined for the tip motion during the experiment. The actual tip displacement and applied force were then recorded during testing. Such measurements generate a load–displacement curve from which sample properties may be determined. If such measurements are performed on homogeneous samples (which are large relative to the contact area; the sample is effectively a half space), the load–displacement curve may be used to extract the sample modulus using the slope of the unloading portion of the curve and contact area, assuming a linear elastic response (Oliver and Pharr, 2004). The sample here is much more complicated, as effects from the cell-wall properties as well as the turgor pressure must be included in the analysis as described above. These concepts led to the experiment design: a displacement profile is used with small unloading segments at various depths from which the slope at a given depth may be determined. Because cell-wall properties and turgor pressure influence all measurements to some degree, a computational model was necessary to separate these effects.
The measurement protocols were developed by performing several such depth-dependent tests. Figure 1(a) shows the displacement–time curve used, which includes a complete loading/unloading profile with several small unloading segments. The tests were performed at a constant depth rate of 200 nm/sec, with 150 nm loading and 50 nm unloading in each increment. Figure 1(b) shows the force–displacement response from an Arabidopsis cell resulting from the defined input cycle. From the force–displacement data at each depth, the slope (dF/dh) was calculated from the unloading section using a linear fit as shown in Figure 1(c).
In order to identify the influence of pressure change on the measurements, a cyclic nanoindentation experiment was performed on Arabidopsis cell walls under three environmental conditions; turgid (sample in water), plasmolyzed (sample in salt solution) and control (sample in air). More than 40 measurements were performed for each environmental condition. The slope–displacement curves of two such measurements for each case are shown in Figure 1(d). The data show that there is a clear difference in slope with cell environment: lowest for plasmolyzed, intermediate for control, and highest for turgid samples. Because these samples differ primarily in their turgor pressure, it is expected that the slope is related to the pressure. These initial results showed the sensitivity of the measurement with respect to the changing cell environment, and provide insight into the computational model required to extract turgor pressure.
There is another important feature in the measurements shown in Figure 1(d) that is unlike the response observed in half-space samples for which the slope increases with depth (Frommer and Overney, 2000). For plant cells, the slope increases until a certain depth (shown as a transition point in Figure 1d), and then tends toward an asymptotic value. This transition point varies slightly with measurement position, but is influenced greatly by the cell environment: more turgid samples have deeper transition points while the plasmolyzed sample does not show a clear transition point (see Supporting information, Figure S5).
To understand the measurements and to extract quantitative information from the data, computational simulations were created to model the indentation experiments (see Supporting information and Figure S1 for details). An example of a simulated indentation is shown in Figure 2. Subsequently, the method was applied to samples at various developmental stages to test the ability of the method to extract biological changes associated with development from the measurements.
Quantification of cell turgor pressure
Quantification of single-cell turgor pressure required a computational model for interpretation of the depth-dependent nanoindentation measurements. In addition to the unknown turgor pressure, several other parameters were needed (see Figure S1). These unknowns include the viscoelastic material properties (E1/E0 and τ1), the thickness of the cell wall, and the instantaneous elastic modulus E0. First, low-depth relaxation tests were used to determine the viscoelastic material parameters for entry into the computational model. Simulations of the depth-dependent cyclic tests were then used to relate the transition points (Figure 1d) of the experimental depth-dependent slopes to the cell-wall thickness (another model input). Finally, the computational model was used iteratively to determine the instantaneous elastic modulus and turgor pressure. Each of these steps is described in detail below.
The relaxation tests (see Supporting information) were performed at 500 nm depth. Each sample was indented using a displacement-controlled ramp function with 100 nm sec−1 loading, 500 nm peak displacement with a holding period of 40 sec, and then 100 nm sec−1 unloading. Multiple indents (seven or eight) were performed on the sample, and the force was recorded as a function of time for each measurement. A normalized force versus time plot for one such experiment is shown in Figure 3 (performed on a 22-day-old sample). The parameters E1/E0 and τ1 were calculated from the experimental data by fitting the hold section of the normalized load versus time plot for all the relaxation experiments performed (see Supporting information). The solid line in Figure 3 is the curve fit for the data shown.
The initial experimental results shown in Figure 1(d) indicate a distinct transition point in the slope versus depth curve. To understand the role of wall thickness on the transition point, numerous simulations were performed. Some of these results are shown in Figure 4, covering a range of thickness from 0.6–1.5 μm, a range of instantaneous modulus from 75–150 MPa, and a range of turgor pressure from 0.1–0.4 MPa. These results show that the transition depth is highly correlated with thickness. From our simulations, we conclude that the cell-wall thickness is approximately 1.8 times the transition depth. The cell-wall thickness was calculated for each experimental slope versus depth curve using the prescribed method by fitting a third-order polynomial to the experimental slope versus depth curve. The transition point was selected at the position at which the change in slope with an increase in depth was less than 2% (implying that the asymptotic value at large depth had been achieved). The thickness was then calculated from this transition value.
Turgor pressure and instantaneous elastic modulus
The two parameters that remain to be determined are the instantaneous elastic modulus of the cell wall (E0) and the turgor pressure. Our simulations confirmed our hypothesis that the slope at low depth was most sensitive to the cell-wall properties (and therefore E0), more so than to the turgor pressure. In contrast, the slope at large depth was most sensitive to the turgor pressure. Thus, for each slope versus displacement curve obtained from the cyclic nanoindentation experiments, an iterative fitting procedure was used to find these values by matching the initial and final slopes from each experimental curve. First, the turgor pressure was assumed to be 1 MPa (although we found that the initial guess of the turgor pressure was not particularly important). Then the simulation was repeated several times with different values of E0 until the simulation matched the experimental value of slope at the lowest depth, 100 nm. This value of E0 was then used for simulations with varying turgor pressure in order to match the slope at large depth. This process was repeated until the values for E0 and turgor pressure from successive simulations change by less than 1%. In all cases, it usually took five or six iterations for the procedure to converge. This procedure to extract thickness, instantaneous elastic modulus and turgor pressure was used for two important examples: the first associated with plasmolysis and the second associated with plant age.
Effect of plasmolysis
The first set of experiments used 22-day-old Col-0 and involved three environmental states associated with the leaf in air, water and salt solution (see Experimental procedures). The viscoelastic material parameters obtained from the fit of relaxation experiments are E1/E0 = 0.225 ± 0.063 (note that this parameter is dimensionless) and τ1 = 7.44 ± 3.2 sec. Thickness results, obtained using the method described above, for all three environmental conditions are shown in Figure 5(a). The uncertainty shown reflects the fact that the thickness at each measurement position may be different. Because it is not possible to measure thickness exactly at the indentation point, transmission electron microscopy (TEM) was used to corroborate the thickness values obtained for the cells in air (Figure 5b). In general, the cell wall is thinnest in the center of the cell and thickest near the anticlinal walls. Thickness values obtained from the TEM image are also shown in Figure 5(a), with reasonable agreement with thickness results obtained from the measured transition point. Plasmolyzed samples, on the other hand, do not show a clear transition point in the slope versus depth curve. A transition may exist below 200 nm. Unfortunately, measurements at depths below 100 nm are not accurate for these samples due to surface/adhesion effects (see Supporting information). Therefore, the cell-wall thickness in subsequent simulations for the plasmolyzed samples was examined over a range of 250–350 nm.
The resulting values of instantaneous elastic modulus and turgor pressure determined using this method are shown in Figure 6(a,b) for the three sets of samples (plasmolyzed, control and turgid) for which two different cell radii were used in the analysis. The instantaneous elastic modulus values (Figure 6a) are maximum for the plasmolyzed samples and minimum for turgid samples. The mean instantaneous elastic moduli (cell radius R =7.5 μm) for plasmolyzed, normal and turgid environments are 124 ± 22, 106 ± 31 and 79 ± 25 MPa, respectively. There is no significant difference (P >0.05) between the modulus results for cells of different radii (R =7.5 and 15 μm). The difference between the modulus values for control and plasmolyzed samples is also negligible (P >0.05). However, the turgid samples show a lower modulus compared with the plasmolyzed and control samples (P <0.05).
Figure 6(b) summarizes the values obtained for the turgor pressure of the samples. The mean turgor pressures (R =7.5 μm) estimated for the plasmolyzed, normal and turgid environments are 0.31 ± 0.050, 1.1 ± 0.30 and 2.1 ± 0.26 MPa, respectively. The turgor pressure values determined when a larger radius was used in the model (R =15 μm) were 0.19 ± 0.19, 0.69 ± 0.18 and 1.7 ± 0.48 MPa for the plasmolyzed, normal and turgid samples, respectively. Statistical analysis for the turgor pressure results shows that the radius of the cell used in the model has a greater impact on the final turgor pressure estimates than it has for the values of modulus, i.e. turgor pressure values using the measurement/simulation approach described here for a cell with radius R =7.5 μm are statistically different from the results obtained using a cell with R =15 μm (P <0.005).
Simulation results for the slope are shown in Figure 7 for the three cases using mean values found from the combined measurement/simulation (R =15 μm). The results obtained from the simulations match reasonably well with the experimental results for each of the environmental conditions.
Effect of age
Our approach was also applied to leaves at various stages of development in the control environmental state (i.e. air). Cell size was determined using confocal microscopy with image analysis software (see Experimental procedures). Relaxation tests were then used to determine the viscoelastic properties of the cell wall. Finally, the depth-dependent measurements were used with the computational model to determine the cell-wall thickness, cell-wall modulus and turgor pressure.
Table 1 summarizes the results obtained for the cell size and for relaxation tests on samples at each age investigated. According to the results, 12-day-old plant samples show a higher value of E1/E0 compared with older plants (22–32 days old). This result indicates a decrease in the viscous behavior of the cell wall with age. This phenomenon is also confirmed in the relaxation time results. (Note: the values reported for the 22-day-old sample in this set of results are statistically the same as those for samples for which the effect of plasmolysis was reported earlier; P >0.05). Clearly, the relaxation time of the cell wall reduces with age, meaning that a young wall is more viscous and therefore takes a longer time to relax to a specific load, while an older wall will relax sooner. For samples at senescence, the properties are more complicated. It is at this stage of development that the cell wall begins to lose its integrity. The results shown in Table 1 support this understanding of the cell-wall breakdown, and provide quantitative information about the size of the change with respect to the mechanical response.
Table 1. Results from the age-related study for the cell radius, as well as the relaxation test results for E1/E0 and relaxation time (τ1)
12 days old
22 days old
32 days old
Cell radius (μm)
7.5 ± 1
10 ± 0.9
12 ± 0.6
12.5 ± 0.5
0.316 ± 0.0781
0.254 ± 0.0736
0.155 ± 0.0195
1.93 ± 0.631
Relaxation time (sec)
12.9 ± 1.54
6.88 ± 2.09
4.88 ± 1.15
23.5 ± 5.02
The cyclic depth-dependent nanoindentation method was also used on these samples. Cell-wall thickness, cell-wall modulus and turgor pressure were quantified as described above. Results for the cell-wall instantaneous modulus with respect to age do not show statistically significant differences for any age (P >0.05; E0 = 65.9± 14.1 MPa). Although there is a decrease in the viscosity of the mature samples (Table 1), the instantaneous modulus is not affected. The results for thickness and turgor pressure are shown in Figure 8(a,b). The change in cell-wall thickness for the 12- and 22-day-old samples was not statistically different (P >0.05) (Figure 8a). However, samples from the 32-day-old mature plants showed a statistically significant increase in cell-wall thickness (P <0.05). In the senescing samples (52 days old), there was a very large decrease in cell-wall thickness, in agreement with knowledge regarding cell-wall breakdown during senescence. The results for turgor pressure, shown in Figure 8(b), indicate that the turgor pressure increases with age up to the maturation stage. However, at senescence, the cells show a dramatic reduction in turgor pressure.
Using the nanoindentation technique described here, in conjunction with finite element modeling, the turgor pressure, cell-wall thickness and elastic modulus have been quantified in living plant cells. In order to demonstrate that this technique captures differences in cell turgor pressure, cell-wall thickness and cell-wall elastic modulus, samples were prepared under three environmental conditions (turgid, control and plasmolyzed). Furthermore, to demonstrate an important application of this method in biology, the above parameters were quantified for plants at various developmental stages.
The results showed that the thickness values quantified by this method are in the range measured by other methods for Col-0 (Derbyshire et al., 2007, Conn et al., 2011). The results shown in Figure 5 suggest that the cell-wall thickness is also affected by the environment – the cell wall is dynamic and responds to the environmental changes. In a high-humidity environment, water passes through the wall and makes the cell turgid by osmosis. Some of this water is trapped inside the wall, leading to swelling of the cell wall and increasing its thickness. A similar observation was made by Niklas (1992) with respect to collenchyma cells, in which the cell-wall thickness for tissue immersed in water was shown to increase by as much as 150% compared with the cell-wall thickness for the same tissue in air. Similarly, there is an expectation that plasmolyzed samples will show a decrease in thickness. Unfortunately, the nanoindentation measurements were not accurate for shallow depths, so that the wall thickness for plasmolyzed samples may only be estimated as less than 200 nm.
The measured values of slope (examples given in Figure 1d) are in the range of values measured by Routier-Kierzkowska et al. (2012) on onion cells over a wide range of turgor pressure as the cells recovered from plasmolysis. In our study, the elastic modulus of the cell wall was determined using finite element simulations to match the experimental slope results. The moduli results for control and plasmolyzed cells were very similar, but the turgid sample showed a lower elastic modulus. This result suggests that the cell wall of a sample kept in water may change more dramatically than that of a sample held in a plasmolyzing solution. However, these findings should be further investigated using other techniques before any stronger conclusions may be drawn. The cell-wall modulus was quantified at a much smaller length scale by Milani et al. (2011) using an atomic force microscope. They reported that the cell wall has the same modulus in both water and salt solutions. However, it should be noted that the tip radius associated with their measurements is much smaller than that used here, highlighting the multiple length scales associated with the structure of the cell wall. Values for the elastic modulus of plant cell walls in the literature range from hundreds of MPa to a few GPa. Wang et al. (2004) and Bolduc et al. (2006) considered 185 MPa as the value of modulus in their simulations. Cell wall moduli have also been measured in Characeae, and the results show that moduli may vary widely, even in closely related plants. The modulus of the cell wall was measured in Chara corallina (Wei and Lintilhac, 2007) as a function of age, and was found to be 213 MPa for young samples and 361 MPa for older samples. Probine and Preston (1962) reported modulus values of 450–1000 MPa for Nitella opaca. An upper limit for cellulose microfibrils of 145 GPa is also given in some studies (Iwamoto S. and Isogai A., 2009). However, because most of these studies do not indicate the loading rate used in the experiments, it is difficult to make careful comparisons for time-dependent (viscoelastic) materials.
The values determined for the turgor pressure of the plant cells under various environmental conditions were in agreement with the results reported by Inan et al. (2004). As expected, maintaining the plant in water causes the cells to absorb water osmotically through the wall, forming turgid cells. Thus, the turgor pressure obtained for the cells kept in water was higher compared with the samples kept in air. On the other hand, plasmolysis causes osmotic water loss from cells, such that the turgor pressure decreases compared to the samples tested in air. These trends were captured very well using the method described.
The results associated with plant age are also in agreement with those of other researchers. Abarca et al. (2001) reported that the rate of growth was smallest for the youngest plants, suggesting that the expansibility of the cell wall changes with age. Also, Derbyshire et al. (2007) reported that, with age, there is a change in the degree of methyl esterification, which plays an in vivo mechanical role within the cell. The degree of methyl esterification is defined as the percentage of methyl-esterified carboxyl groups (-COOMe) on homogalacturonan molecules in pectin polysaccharide. This esterification blocks cross-linking by removing the negative charge from the carboxylate ion. A lower degree of methyl esterification leads to a less viscoelastic wall matrix, which reduces the wall relaxation in mature cells. This phenomenon occurs in concert with cessation of growth hormone secretion. It was reported by Goldberg et al. (1986) that mature cell walls have a lower degree of methyl esterification. These biological facts are in agreement with our results, which show that the relaxation time of the cell wall reduces with age (Table 1), implying that the cell wall in a young cell is more viscous than a mature wall. In a senescing cell, because photosynthesis has ceased, the cell is utilizing sugars in the wall (Mohapatra et al., 2010), and the cell wall begins to lose its integrity and structural support.
Typically, the stretching due to growth increases the cell size by 10–100 times. However, it has been reported that the cell-wall thickness does not change during this process (Bret-Harte et al., 1991). Thinning to the point of mechanical instability is prevented by introduction of new material into the cell wall. However, although the cell no longer expands in mature cells, cell-wall components continue to be introduced into the wall, leading to an increase in cell-wall thickness (Wei and Lintilhac, 2007). In samples from senescing tissue, the cell walls serve as a source of nutrients for the cell and start to thin (Mohapatra et al., 2010). The results obtained using our approach (Figure 8a) match these observations.
The change in the turgor pressure of cells with age has been confirmed previously (Zur et al., 1981; Zhu and Boyer, 1992). When transpiration is negligible, water potentials in growing tissues are lower than in mature tissues. Such gradients move water into the enlarging cells. Because these cells have extensible cell walls, transport of water into these cells leads to irreversible growth of the tissue. It has also been reported (Nonami and Boyer, 1993) that the osmotic potential in a growing tissue is lower than in mature tissue. Under steady-state conditions, the pressure potential (ψp) is the difference between the water potential (ψw) and the osmotic potential (ψs), i.e. ψp = ψw – ψs. Therefore, the turgor pressure in mature cells is expected to be larger when compared with younger cells. During senescence, cells show a large reduction in turgor pressure that is attributable to the fact that cells are preparing for programmed cell death. The results obtained from the measurements in this study (Figure 8b) are in agreement with these biological expectations (Shibuya et al., 2009; Das et al., 2010).
Although these measurements show great promise with respect to quantitative measurements on living plant cells, future work must address issues associated with the tip position relative to the cell geometry. An improved optical microscope would allow precise positioning of the tip such that these effects may be accurately quantified. In addition, other important components of the cell, such as microtubules, may directly or indirectly influence the cell-wall mechanical response and should be included in future models. Finally, it is important to note that the turgor pressure results reported here were obtained indirectly through use of the computational model. As improved models are implemented, the accuracy of the pressure estimates is expected to improve as well.
Plant material and growth conditions
Arabidopsis thaliana (Col-0) seeds were stratified at 4°C for 2 days and then grown in a growth chamber for 22 days under 12 h day length at 24°C and relative humidity of 50–60%. Rosette leaves were numbered by emergence, reflecting their age, as shown in Figure S2.
Nanoindentation experiments were performed using a commercial TriboScope (Hysitron Inc). The indentations were performed using a spherical indenter of radius 2.5 μm. To avoid dehydration of the samples and any change in the mechanical properties of the cell wall, all tests were performed on leaves attached to the plant. For consistency, tests were performed on leaf 3 of plants (22 days old unless otherwise stated), as shown in Figure S2. Nanoindentation was performed on cells from within the same area of the abaxial (lower) side of the leaf. The leaves were mounted to a sample holder disk using double-sided tape to eliminate any movement while performing the indentations. To ensure reproducibility of the results, 25 tests were performed on leaves from five plants.
The resolution of the nanoindenter camera was not sufficient to distinguish individual cells. Therefore, it was not possible to position the tip within single cells accurately. Thus, some of the nanoindentations may have been performed on the anticlinal walls or near guard cells. The possibility of coming into contact with such undesirable areas was estimated by Hayot et al. (2012) to be approximately 15–20% (Figure S3). However, measurements on undesirable regions were expected to look very different when compared with measurements near the middle of cells. For example, an indentation on an anticlinal wall was expected to show higher stiffness (due to the large wall depth) and was not expected to show an effect of pressure. Thus, the majority of the measurements that showed similar behavior were expected to come from positions away from anticlinal walls near the middle of the cells.
To test the reliability of the method for determining turgor pressure, 22-day-old plant cells with various turgor pressures were prepared. Hypertonic samples were prepared by immersion of the leaves in 10% NaCl solution, and hypotonic samples were prepared by immersion of the leaves in pure water. The results for these two samples were compared with those for control cells tested in air.
In order to study the effect of age, four sets of Col–0 samples were grown to four developmental stages: 12, 22, 32 and 52 days (senescence). The cell size for each developmental stage was estimated from optical micrographs using ImageJ software (see below). The measured cell radii were 7.5 ± 1.0, 10 ± 0.9, 12 ± 0.6 and 12.5 ± 0.5 μm for the 12-, 22-, 32- and 52-day-old samples, respectively.
Transmission electron microscopy
TEM images of cell walls were prepared as described by Paparozzi (1981). According to this protocol, sections of the leaf were cut and immediately immersed in fixative at 0–4°C (in ice). The fixative contained 1.5% para-formaldehyde/3% glutaraldehyde in 0.1 m sodium cacodylate, pH 7.0, plus 5 mg/ml CaCl2. Samples were fixed for 1 h. Samples were then post fixed (at 0–4°C) in 2% OsO4 in 0.1 m sodium cacodylate, pH 7.0, overnight. Samples were then dehydrated and infiltrated. Transverse sections of three leaves per sample were observed at 30 kV using a Hitachi H7500 TEM with a Windows95/NT-based computerized operating system (Microsoft) for ultra-structural analysis of sections. Images were captured for many sections of each leaf, including regions near the anticlinal walls and regions between two anticlinal walls. Overall, a total of more than 150 images were analyzed. Wall thickness was determined by drawing a tangent to the outer side of the cell wall and measuring the amount of cell-wall material perpendicular to the tangent. The thickness of the cell wall was estimated at ten locations on each image. The values shown in Figure 5(a) represent the mean of at least 100 measurements.
A two-tailed paired Student's t-test was applied to the results to quantify the significance of the changes in stiffness with respect to the frequency as well as the significance of the stiffness changes with respect to the age of the leaf sample and genetic variation for specific frequencies. Each data point is given within a confidence level of 95%.
Image analysis and cell size measurements
To determine the approximate cell size for implementation in the finite element model, ImageJ 1.41o analysis software was used. The analysis was performed for plants of various ages: 12, 22, 32 and 52 days (senescence). For this purpose, the leaves were stained with fluorescent brightener 28 (F3543 Sigma-Aldrich), which binds to cellulose in the cell wall so that the cell wall is visible under a confocal microscope (Olympus FluoView 500 mounted on an Olympus BX60 compound microscope). This dye fluoresces (peak emission wavelength 450 nm) when excited with UV or near-UV light (optimum excitation wavelength 347 nm). The size of the cell was determined by drawing circles within the lobes of the cells. First the confocal image scale was defined in the software using the known micron/pixel values (Analyze→Set Scale). Then, using the circle drawing tool, a circle was drawn such that it fitted inside the cell. Finally, the area of the circle was measured using Analyze→Measure, from which the radii were determined (see Figure S4). This method was repeated 70 times on each image with three images used for each sample. Then the mean and standard deviation were calculated.
Image analysis and positional probability
Image analysis was performed on confocal images of leaves stained with fluorescent brightener 28 in order to determine the probability that the nanoindenter tip makes contact with anticlinal walls or guard cells (undesired regions). The undesired area was assessed by measuring the ratio of the area of the cell wall and guard cells to the whole area using ImageJ analysis software and a protocol modified from that described by Straatmann (2008). First the image scale was set using the known micron/pixel values (Analyse→Set Scale). Next the brightness and contrast was adjusted using the Image→Adjust brightness, contrast. Then the image was inverted using Edit→Invert, followed by Process→Make Binary to change the image to a binary format. The guard cells and anticlinal walls were filled in black using a paintbrush tool. Finally, the undesired area percentage (black to white ratio) was quantified using the Analyze→Measure tool. Figure S3 shows the images prepared at each of these steps.
This work was supported by the US National Science Foundation under grant number EPS-0701892 and by the Nebraska Center for Energy Sciences Research at the University of Nebraska-Lincoln.