Organic Thin-Film Transistors: Simultaneous Modification of Bottom-Contact Electrode and Dielectric Surfaces for Organic Thin-Film Transistors Through Single-Component Spin-Cast Monolayers (Adv. Funct. Mater. 8/2011)
An efficient process is developed by spin-coating a single-component, self-assembled monolayer (SAM) to simultaneously modify the bottom-contact electrode and dielectric surfaces of organic thin-film transistors (OTFTs). This effi cient interface modifi cation is achieved using n-alkyl phosphonic acid based SAMs to prime silver bottom-contacts and hafnium oxide (HfO2) dielectrics in low-voltage OTFTs. Surface characterization using near edge X-ray absorption fi ne structure (NEXAFS) spectroscopy, X-ray photoelectron spectroscopy (XPS), attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy, atomic force microscopy (AFM), and spectroscopic ellipsometry suggest this process yields structurally well-defi ned phosphonate SAMs on both metal and oxide surfaces. Rational selection of the alkyl length of the SAM leads to greatly enhanced performance for both n-channel (C60) and p-channel (pentacene) based OTFTs. Specifi cally, SAMs of n-octylphos-phonic acid (OPA) provide both low-contact resistance at the bottom-contact electrodes and excellent interfacial properties for compact semiconductor grain growth with high carrier mobilities. OTFTs based on OPA modifi ed silver electrode/HfO2 dielectric bottom-contact structures can be operated using < 3V with low contact resistance (down to 700 Ohm-cm), low subthreshold swing (as low as 75 mV dec−1), high on/off current ratios of 107, and charge carrier mobilities as high as 4.6 and 0.8 cm2 V−1 s−1, for C60 and pentacene, respectively. These results demonstrate that this is a simple and efficient process for improving the performance of bottom-contact OTFTs.