QUANTITATIVE NANOMECHANICAL MAPPING OF MARINE DIATOM IN SEAWATER USING PEAK FORCE TAPPING ATOMIC FORCE MICROSCOPY

Galja Pletikapić,

Division for Marine and Environmental Research, Ruđer Bošković Institute, Zagreb 10000, Croatia

Search for more papers by this author
Alexandre Berquand,

Bruker Nano GmbH, Mannheim 68165, Germany

Search for more papers by this author
Tea Mišić Radić,

Division for Marine and Environmental Research, Ruđer Bošković Institute, Zagreb 10000, Croatia

Search for more papers by this author
Vesna Svetličić,

Division for Marine and Environmental Research, Ruđer Bošković Institute, Zagreb 10000, Croatia

Author for correspondence: e-mail svetlicic@irb.hr.

Search for more papers by this author
First published: 14 December 2011
Citations: 55

Received 22 December 2010. Accepted 3 June 2011.

Abstract

It is generally accepted that a diatom cell wall is characterized by a siliceous skeleton covered by an organic envelope essentially composed of polysaccharides and proteins. Understanding of how the organic component is associated with the silica structure provides an important insight into the biomineralization process and patterning on the cellular level. Using a novel atomic force microscopy (AFM) imaging technique (Peak Force Tapping), we characterized nanomechanical properties (elasticity and deformation) of a weakly silicified marine diatom Cylindrotheca closterium (Ehrenb.) Reimann et J. C. Lewin (strain CCNA1). The nanomechanical properties were measured over the entire cell surface in seawater at a resolution that was not achieved previously. The fibulae were the stiffest (200 MPa) and the least deformable (only 1 nm). Girdle band region appeared as a series of parallel stripes characterized by two sets of values of Young’s modulus and deformation: one for silica stripes (43.7 Mpa, 3.7 nm) and the other between the stripes (21.3 MPa, 13.4 nm). The valve region was complex with average values of Young’s modulus (29.8 MPa) and deformation (10.2 nm) with high standard deviations. After acid treatment, we identified 15 nm sized silica spheres in the valve region connecting raphe with the girdle bands. The silica spheres were neither fused together nor forming a nanopattern. A cell wall model is proposed with individual silica nanoparticles incorporated in an organic matrix. Such organization of girdle band and valve regions enables the high flexibility needed for movement and adaptation to different environments while maintaining the integrity of the cell.