Propagating Surface Plasmon Polaritons: Towards Applications for Remote‐Excitation Surface Catalytic Reactions

Plasmonics is a well‐established field, exploiting the interaction of light and metals at the nanoscale; with the help of surface plasmon polaritons, remote‐excitation can also be observed by using silver or gold plasmonic waveguides. Recently, plasmonic catalysis was established as a new exciting platform for heterogeneous catalytic reactions. Recent reports present remote‐excitation surface catalytic reactions as a route to enhance the rate of chemical reactions, and offer a pathway to control surface catalytic reactions. In this review, we focus on recent advanced reports on silver plasmonic waveguide for remote‐excitation surface catalytic reactions. First, the synthesis methods and characterization techniques of sivelr nanowire plasmonic waveguides are summarized, and the properties and physical mechanisms of plasmonic waveguides are presented in detail. Then, the applications of plasmonic waveguides including remote excitation fluorescence and SERS are introduced, and we focus on the field of remote‐excitation surface catalytic reactions. Finally, forecasts are made for possible future applications for the remote‐excitation surface catalysis by plasmonic waveguides in living cells.


Introduction
Surface plasmons (SPs) are the collective oscillations of free electrons that are confi ned evanescently on a metal surface. [ 1 ] Coupled with photons, SPs can act as a collective excitation of conduction electrons that propagate in a wave like manner along an interface between a metal and a dielectric, known as surface plasmon polaritons (SPPs). SPPs are confi ned to the vicinity of the interface and can propagate along the metal surface until the energy dissipates, either by heat loss or by radiation into free space. [ 2 ] Localized surface plasmons (LSPs) are oscillations of charge density that are confi ned on the metallic nanoparticle's surface. The resonant LSPs, known as LSPR, result in a large enhancement of the localized electromagnetic (EM) fi eld, which is the underlying mechanism for surface enhanced spectroscopy. LSPs and SPPs have been widely used in plasmonic resonance sensors, [ 2,3 ] tip-/surface-enhanced Raman spectroscopy, socalled TERS/ SERS, [ 4,5 ] and plasmonic catalysis, [ 6 ] etc.
Since their discovery, SERS and TERS have extensively been experimentally and theoretically studied because of their extremely high sensitivity and wide applications in qualitative and quantitative analysis by fi ngerprint vibrational spectroscopy, even at the single-molecular level. [7][8][9][10][11][12][13][14] In addition, due to the high throughput and low energy requirements, a novel application of plasmonics in chemical reactions gains signifi cant attention, as reported in works on dissociation of hydrogen [ 15,16 ] and water, [ 17,18 ] photochemical [19][20][21][22][23] and plasmon-driven chemical reactions, [24][25][26][27][28][29][30][31][32][33][34][35][36][37] etc. SPs excited on the surface of gold or silver can non-radiatively decay into so-called hot electrons with a high energy between the Fermi and vacuum energy level. [36][37][38][39][40] The hot electrons could scatter into the absorbed molecule's excited state and then trigger chemical reactions by reducing the activation energy, so-called plasmonic catalysis. [ 41 ] If the reaction is monitored by SERS or TERS spectra, the nanostructures behave as catalysts and nanoscale signal enhancers, simultaneously. Plasmon catalyzed reactions monitored by TERS and SERS have been reviewed by many different groups. [ 5,6,[42][43][44][45][46][47] Currently, the plasmonic waveguide has been successfully applied in the fi eld of remote-excitation surface enhanced Raman spectroscopy. [ 48,49 ] Compared with traditional SERS, remote excitation SERS has many advantages. In normal Plasmonics is a well-established fi eld, exploiting the interaction of light and metals at the nanoscale; with the help of surface plasmon polaritons, remote-excitation can also be observed by using silver or gold plasmonic waveguides. Recently, plasmonic catalysis was established as a new exciting platform for heterogeneous catalytic reactions. Recent reports present remote-excitation surface catalytic reactions as a route to enhance the rate of chemical reactions, and offer a pathway to control surface catalytic reactions. In this review, we focus on recent advanced reports on silver plasmonic waveguide for remote-excitation surface catalytic reactions. First, the synthesis methods and characterization techniques of sivelr nanowire plasmonic waveguides are summarized, and the properties and physical mechanisms of plasmonic waveguides are presented in detail. Then, the applications of plasmonic waveguides including remote excitation fl uorescence and SERS are introduced, and we focus on the fi eld of remote-excitation surface catalytic reactions. Finally, forecasts are made for possible future applications for the remote-excitation surface catalysis by plasmonic waveguides in living cells.
SERS, the excited light is focused on the detected spot, which is called local SERS. In contrast in the 'remote SERS', the excited spot is far away from the detected target, which is excited by the SPPs with a 'remote mode'. Ag or Au waveguides offer a way to go below the size limit because they transfers optical signals via SPPs. SPPs can propagate along the metal waveguide and emit free photons at imperfections or at the end of waveguide, while some of them are lost due to the Ohmic damping. The energy transfer from the spot of illumination and the hot-spot can be mainly supported by the remote systems based on plasmonic waveguide, as illustrated in Figure 1 . The SPPs could of course excite the nanoscale hot-spot remotely, which can avoid the strong background noise because of a large area of the excited spot, and isolate heat effects from the area of excited light to the target excited in the area of sub-diffraction wavelength. Moreover, it can reduce the possibility of the sample damage by high laser excitation. Based on surface-enhanced spectroscopy, a novel way of sensing measurements can be provided by such a remote SERS system, and it can be used in systems where normal SERS is unsuitable, such as Raman and fl uorescence detection of biomolecules in living cells. [50][51][52] It is important that the plasmon-catalyzed reactions can be remotely driven by silver plasmonic waveguides. [53][54][55] In the plasmon-driven chemical reactions via the traditional SERS method, the laser is directly radiated on the molecules and metal substrate. Several environmental factors for the plasmondriven chemical reactions are diffi cult to clearly exclude, such as photons generated directly from light of the laser, electrons directly escaping from the metal surface by overcoming the work function (photoelectric effect), and heating effect of the laser or surface plasmonic resonance. The plasmonic-waveguide-driven surface catalytic reactions can provide more confi dent evidence for the mechanism and nature, since the above several environment factors can be explicitly excluded.
In this review, we introduce the recent progress of the propagating SPP (plasmonic waveguide) driven surface catalytic reaction. First, we introduce the synthesis and characterization of plasmonic waveguides of Ag nanowires (NW), and the propagating mechanism of the Ag nanowire is physically revealed. Then, we focus on the application of plasmonic waveguide for remote-excitation research, including fl uorescence and SRES, and surface catalyzed reaction of pp ′-dimercaptoazobenzene (DMAB), as revealed by remote excitation SERS spectroscopy. DMAB can be produced from para -aminothiophenol (PATP) and 4-nitrobenzenethiol (4NBT) by propagating SPPs; plasmonic waveguide-driven reduced and oxidized reactions, respectively. Finally, we provide an outlook for possible future applications on remote-excitation surface catalytic reactions in living cells.

Synthesis of Ag Nanowire Waveguides
Detection of plasmonic waveguide for remote-excitation surface catalytic reactions requires smooth surfaces, controllable size, and high crystallinity, as these factors decrease dissipative energy loss. SPPs in the visible spectrum can propagate with the least energy loss over tens of micrometers on silver nanowire. Lots of methods have been reported on the synthesis of sliver nanowires such as solution-phase, vapor-phase, [ 56,57 ] and microfabrication techniques. [ 58 ] Ag NWs prepared by lithography methods, however, have the disadvantages of producing polycrystalline structures that have inevitable defects due to the metal evaporation process. These disadvantages can signifi cantly shorten the propagation distance of SPP in NW waveguides by increasing scattering loss. [ 58 ] On the other hand, controlling the diameter and morphology of Ag NWs through the vapor-phase method is diffi cult. such as reaction time, temperature, chemical ratio, injection speed, stirring speed, and added agents. [75][76][77][78][79][80][81][82] Furthermore, the structure of synthesized Ag NWs is highly crystalline, and the surfaces are very smooth. Dissipative energy loss can be drastically suppressed, and NWs can thereby be efficiently used in plasmonic waveguides for remote-excitation surface catalytic reactions ( Figure 3 ).

Basic Modes of SPP in Metal Cylindrical NW
This review is mainly concerned with SPP propagation in Ag NW waveguide, and most of the previous works consider a cylindrical shape of NW. Herein, we fi rst describe SPP modes in an infi nite cylinder. For an infi nite cylindrical wire with radius R and permittivity ε 2 in a homogeneous medium (ε 1 , a nonmagnetic material), Chang et al. describe the electric and magnetic fi eld as follows: [ 83 ]   Chemical synthesized Ag NWs. a) SEM images of Ag NWs prepared through the conventional polyol synthesis process. b) TEM image of a Ag NW, demonstrating the bicrystallinity and corresponding growth directions. The inset shows the micro-diffraction pattern recorded by focusing the electron beam onto this NW. c) SEM image of Ag NWs obtained via ammonium carbonate-mediated polyol synthesis method. d) TEM image of an individual NW and the inset shows the selected-area electron diffraction (SAED) patterns taken from the part indicated by the dotted circles. a,b) Reproduced with permission. [ 70 ] Copyright 2002, American Chemical Society. c) Reproduced with permission. [ 71 ] Copyright 2002, American Association for the Advancement of Science. d) Reproduced with permission. [ 82 ] Copyright 2014, Elsevier.
where j = 1, 2, a condition that pertains to the medium and wire.
A solution only exists when According to the results of Chang et al., only lower-order modes ( m = 0, ±1) could exist for thin metal wires; such modes are commonly used (Figure 3 ), and higher modes are thus excluded. The mode having which m = 0 always exists; the thinner the wire is, the more confi ned the electromagnetic fi eld. For the mode in which m = ±1, there is no strict cutoff radius, but for a very small radius, the mode volume is very large. For the normal wires we used, modes for which m = 0 and m = ±1 exist. For very thick wires ( R > 150 nm in air), higher modes exist. For the cases discussed in this paper, only normal wires ( R ≈ 100 nm) are considered.

SPP modes of Ag NW by One End Excitation
In order to excite SPP in the NW, the simplest and most convenient way is directly focusing the light on one end of wire, due to the fact that local symmetry-breaking at a fi nite length NW terminus is suffi cient to excite SPP. Assuming that the harmonic monochromatic laser beam with electric fi eld E E r r E E r r e i t illuminate on the end of wire perpendicular to the wire, the modes on the wire will be excited with the following form (ignoring the time factor): corresponding to the modes which can be excited.
For an ideal cylinder, in the electrostatic approximation, when the polarization is along the wire, m = 0 mode will be excited as If the polarization perpendicular to the wire, m = ±1 modes will be excited. According to the boundary condition, these are Where j = 1, 2 refer to the medium around and wire.   when the input light phase is ϕ = 0 or ϕ = π/2 with the polarization component along the wire. The m = 1 mode is generated for 00 ϕ = 0 with polarization components perpendicular to the wire. For any polarization, the light can be divided into the two basic components with polarization along or perpendicular to the wire. The amplitude of the components excited is strongly depending on the polarization angle and of course, the shape of the illuminating terminal.

Features of Remote-Excitation SERS and Early Applications
SPPs propagating on noble-metal nanowires have been widely studied in this decade, which sought to fi nd the basic physical mechanism. [ 58,[83][84][85][86][87] In 2009, remote SERS on single silver nanowire systems was investigated by Fang et al. [ 49 ] Remote excited SERS of MGITC molecules was reported, alongside the polarization dependence on the single Ag nanowire with a nanoparticle that was excited by 632.8 nm wavelength ( Figure 5 ). The corresponding SEM, optical and SPP images are shown in Figure 5a-c. Normal SERS spectra of MGITC were obtained from the excited laser spot at left-end of the Ag nanowire or the remote site of the gap of nanowire and nanoparticle, respectively. The remote SERS spectra were obtained from the remote site by separating the signal collection spot from the laser spot. Clearly, the remote excitation SERS spectra can be observed by a single Ag nanowire waveguide after the correction of fl uorescence background. It was explained by a two-step mechanism in the numerical simulation. First, the SPs are excited and propagate to the target spot; there is an electromagnetic fi eld   Reproduced with permission. [ 87 ] Copyright 2011, American Chemical Society.
intensity enhancement (F 1 ) for the excited wavelength. Then the intensity enhancement (F 2 ) for the local structure of the target spot is achieved for the specifi c Raman peak wavelength. The product of the two factors gives the remote-excitation SP signal enhancement. This mechanism works for the other systems in this review, while for the remote-excitation catalysis, the fi rst factor (for the laser) dominates, as the hot electrons are excited by the laser excited SPPs; the second factor mainly contributes to the Raman measurement of the catalyzed products. The Raman signal is also remotely detectable as part of the energy is converted to SPPs again as well.
Remote SERS was also measured by a single Au nanowire ( Figure 6 ). [ 87 ] It was found that the remote excitation SERS is dependent on the polarization of the laser. Maximal Raman signals were obtained when the incident polarization is parallel to the nanowire waveguide. In this remote system based on a single nanowire waveguide, the polarization of the remote site could be set toward a specifi c direction by adjusting the polarization of the excited laser. This procedure, however, requires a previous measurement. Because of their antioxidant property, working time for the operation of Au plasmonic devices may be much longer under ambient environments compared with that of Ag plasmonic devices.
The plasmonic waveguide for remote excitation has been tentatively used in the fi eld of biology, chemistry and physics. In 2012, Yang's group reported a remote system based on nanowire for endoscopyin a cell, in vivo. [ 50 ] The remote endoscopy consists of single nanowire of SnO 2 attached to an optical fi ber ( Figure 7 ) by using a three-axis micro manipulating system. The inserted SnO 2 nanowire could work as an optical waveguide supporter at the designated positions in vivo cells. The sub-cellular images and the fl uorescence of the quantum dots emitted at 655 nm in single cell were presented by using nanowire endoscope. In sub-cellular spectra detection in remote endoscope system, the SnO 2 nanowire was located around the preloaded quantum dots, which can be excited by 442 nm wavelength laser. As shown in Figure 7 e, the fl uorescence signals of quantum dots in cell could be then collected by the remote nanowire waveguide connected with a spectrometer and CCD. To achieve a larger intensity of the remote signals, a Ag or Au nanowire waveguide can be used to replace the semiconductor nanowire because of the enhanced electromagnetic of SPPs.
In 2014, Uji-i etal. reported the remote excitation SERS by plasmonic waveguide in living cell. [ 51 ] As shown in Figure 8 , the plas-monic hotspot (at the gap of two Ag nanowires, or at the gap of nanowire and nanoparticles) on the Ag nanowire probe inserted into the cells was excited by SPPs, and the signals were collected from the other side the Ag nanowire probe outside the cells. A clear remote SERS spectrum can be observed by using an Ag nanowire probe hotspot inserted into a living HeLa cell.
Clearly, it is possible that plasmonic waveguide of a single metal nanowire can be used for remote excitation in living cell system. In addition, this remote excitation technique can also be used for another important application known as plasmon driven chemical reactions.  The corresponding spectrum remotely collected through the nanowire end scope system. Reproduced with permission. [ 50 ] Copyright 2012, Nature Publishing Group. [ 50 ]

Features of the Plasmon-Driven Chemical Reaction
Assisted by the plasmon-induced hot electrons, plasmonic catalysis was recently established as a very new heterogeneous catalytic reaction platform. [ 6,24,25,32,33,37,[88][89][90][91][92] Recent experimental and theoretical reports present plasmonic catalysis as a route to concentrate and direct the energy of visible light to adsorbed molecules, enhance the rate of chemical reactions, and offer a pathway to control the reaction selectivity. SPs can decay and transfer energy identical to that of incident photons to hot-electrons with kinetic energies above Fermi level. Stronger laser intensity produces more surface plasmon quantum's, subsequently producing a large density of hot-electrons generated from the plasmon decay. The hot-electrons can jump into the unoccupied resonant molecular energy level on the surface of Ag/Au metal. As the hot electrons jump on the molecules, the molecular potential energy surface (PES) can be changed from a state of neutral to temporal negative-ion. Energy from hot electrons above the Fermi surface can transfer intramolecular vibrational energy during the interactions, in which case the energy barrier of the chemical reactions decreases. In some cases, [ 29 ] hot electrons provide kinetic energy and result in a temporal negative-ion PES. But in some cases, [ 37 ] additional electrons are also needed in the surface catalysis reaction. Therefore, hot electrons provide two or three important contributions to plasmonic catalysis.
A study in 2010 revealed convincing evidence of plasmon catalysis of PATP to DMAB by LSPs. [ 24 ] As shown in Figure 9 , compare with the SERS and normal Raman spectra of PATP, it was found that additional Raman peaks are at 1143, 1390, and 1432 cm −1 . However, simulated SERS spectra of PATP on Ag 5 clusters could not be reproduced very well. Unexpectedly, the Raman spectrum of DMAB (Figure 9 d) is well reproduced by SERS spectra of PATP in Ag sol. [ 24 ] All the three strongly enhanced peaks of DMAB represent symmetric a g vibrational modes, strongly indicating the formation of DMAB from PATP through the N = N bond. These peaks are assigned to the a g12 , a g16 , and a g17 symmetric vibrational modes, respectively.
Meanwhile, Tian's group also found the same conclusion with more confi dent evidence, which revealed by SERS spectra and desorption electro-spectra ionization mass spectrometry spectra. [ 25 ] The plasmon assisted reactions of PATP to DMAB were experimentally well confi rmed by surface mass spectrometry (SMS), and electrochemistry, and it was found that the results are well consistent with the calculations. The SMS spectra were obtained from the PATP-adsorbed silver electrode after illuminated using a high power laser. [ 25 ] As shown in Figure 10 , the peaks of SMS spectra at 245.5 and 164 m z −1 could be assigned to "H+S-Ph-N = N-Ph-S" fragment and "K+S-Ph-NH 2 ", respectively. The peak of 245.5 m z −1 in Figure 10 a working as a control cannot be observed. It was found that the formation of DMAB was produced from PATP excited by a high power laser. Moreover, the SERS spectra also indicate that DMAB can be synthesized successfully, which is commercially unavailable To provide further evidence for plasmon-driven chemical reaction of PATP being converted to DAMB, it is necessary to   [ 51 ] ascertain the real SERS spectra of PATP. By using the system of nanoparticles, the strong surface plasmonic resonance make the chemical reaction easy, and the real SERS spectra of PATP would not be discovered, which is a challenge of observation of the real SERS spectra of PATP. As shown in Figure 11 , by using the SERS substrate of silver nanowire on silver, fi lm the SERS spectra of PATP was same as the normal Raman spectra of PATP, where the DMAB modes at 1140, 1390, 1432 cm −1 were not obtained (see Figure 12 ), and the SERS spectra are the same as the Raman spectrum of PATP powder. [ 89 ] Furthermore, the laser intensity dependent dynamics of surface catalytic reaction that PATP react to DMAB were also monitored (see Figure 13 ). The reason that the genuine SERS spectrum was successfully observed is that the enhancement of electromagnetic fi eld at the gap of silver nanowire and silver fi lm is much weaker than that in the normal hot-spots of silver or gold nanoparticles. [ 89 ] Then similar experimental results have also reported by many other groups. [90][91][92][93] The mechanism of Plasmon-driven www.MaterialsViews.com www.advancedscience.com Adv. Sci. 2016, 3, 1500215   Figure 9. a) Experimental SERS spectra of DMAB excited at 514.5 nm, b) the experimental normal Raman spectrum of PATP, c) theoretical SERS spectrum of a PATP-Ag 5 complex, and d) simulated Raman spectrum of DMAB. Reproduced with permission. [ 24 ] Copyright 2010, American Chemical Society. chemical reaction has been also reported by Xu et al. [ 90 ] and Tian et al., [ 30 ] respectively.

Remote-Excitation Plasmon-Driven Chemical Reactions by Nanoparticle-Nanowire Systems
Remote SERS has been introduced into plasmonic catalysis in which propagating SPPs behaved as carriers for catalysis and sensing. [53][54][55] By using remote SERS technology, the plasmon catalyzed reaction of PATP to DMAB was demonstrated at the junction at the nanowire and nanoparticle system. [ 53 ] As shown in Figure 14 , the SEM image and optical photo of propagating SPPs (Figure 14 a,b) reveal that the distance is about 3.4 μm and the size of the excitation spot is about 130 nm. Maximal signals can be obtained when the polarization of excited laser was parallel to the nanowire waveguide. The white spot at the gap of the nanowire and nanoparticle indicates that light converted by propagating SPPs from the another side of the silver nanowire. Remote plasmon driven chemical reaction of PATP to DMAB occur by using remote SERS, and the fl uctuation of polarization intensity of incident light shown by the spectra could be explained by the polarization dependence of propagating SPPs as discussed above. However, the plasmonic catalysis of PATP to DMAB cannot occur at the excited side of the nanowire, which is local SERS (Figure 14 e), because the electromagnetic fi eld intensity at the excited side is weaker than that at the hot spot of the junction, as is essential to plasmonic catalysis. The corresponding optical image and image of the Raman mode of Ag 17 of DMAB confi rm that the plasmonic catalysis occurs only at the junction of the nanowire and nanoparticle by remote SERS.   Reproduced with permission. [ 89 ] Copyright 2012, Royal Society of Chemistry. Figure 13. a,b) SERS spectra of PATP measured at the very beginning and after 60 s of laser radiating in Ag nanowire on Ag fi lm system, respectively, and c) the SERS spectrum of DMAB in Ag aggregation system. Reproduced with permission. [ 89 ] Copyright 2012, Royal Society of Chemistry.    [ 54 ] Copyright 2013, Springer.

Remote Plasmon-Driven Chemical Reactions by Crossed-Nanowire System
In the remote SERS system of the single nanowire, the distance of remote excitation was decided by the length of nanowire. In contrast, in the nanoparticle-nanowire system, the hot spot at the nanogap of the nanoparticle and adjacent nanowire can be adjusted by changing the nanoparticle position along the nanowire. However, the distance between the nanogap and the excited side of nanowire is hard to control experimentally. A crossed nanowires system formed by two nanowires may overcome the aforementioned disadvantages. The junction of the crossed nanowires produces a hot spot that could be readily positioned through a 3D micromanipulator system under the optical microscope. We were thus able to investigate catalysis by remote SERS in crossed sliver nanowires in recent report. [ 54 ] The remote SERS spectra at the junction indicates that the reaction of 4NBT to DMAB could be induced by propagating SPPs under a laser excitation of 632.8 nm wavelength focused at the nanowire side ( Figure 15 ). The optical image and corresponding SEM image of propagating SPPs are shown in Figure 15 a,b. The magnifi ed images show that the size of diameters of that two crossed nanowires were 126 and 110 nm, respectively. The clear white spot at the junction indicates that coupling photons emerged from propagating SPPs while the laser excited at one nanowire terminal was about 3.6 μm away. Distinct DMAB vibrational features (Figure 15 d) are present in the remote SERS spectra obtained with various incident polarizations. These demonstrate that the surface catalysis reaction was remotely induced by propagating SPPs. The maximal intensity of remote SERS was observed while the polarization of incident laser was parallel to the nanowire. This result can be explained by the higher effi ciency of SPPs propagation along the nanowire axis in the single-silver-nanowire system. To exclude the possibility that SERS signals obtained from the junction were due to background scattering or SPP propagation at the excited side, Raman images at the Ag 17 vibrational mode of DMAB are shown in ´Figure 15 c. The colored gap area indicates that remote plasmonic catalysis only occurred in the hot spot due to the strongly enhanced EM fi eld. In addition, the time dependent properties of remote plasmon catalyzed reactions in such crossed nanowires system were also confi rmed in this work.

Remote Plasmon-Driven Chemical Reactions by a Metal-Nanowire Array-Bundle System
In 2012, Moskovits' group reported another effi cient remote SERS system by using nanowire bundle consists of nanowire array that produced by electrochemical deposition on a porous anodic alumina (PAA) template. Due to the strongly enhanced Figure 16. (top) The sketch of the remote and local SERS based on silver nanowire array bundles system. (bottom) SEM images of system. a) Lateral and b) top view SEM images of a silver nanowire array bundles system. c) Top view of system with 11 nm inter-wire gaps. d,e) systems with 2.2 µm length (33 nm gap) and 1 µm (11 nm gap) after dissolving the porous alumina oxide template. Reproduced with permission. [ 55 ] Copyright 2012, American Chemical Society. EM fi eld at the nanowire gaps, this system were also used in plasmonic catalysis, such as water splitting and the reaction of PATP to DMAB. [94][95][96] In this remote sensing system, the silver nanowire array was used as a probe, which can be attached to a catheter or an optical fi ber to collect remote SERS signals in biological cell or liquids. [ 55 ] The SEM images of probe structures and experiment setup are illustrated in Figure 16 . The anodic alumina fi lm at top was slightly dissolved to ensure that the PATP molecules can be attached to the Ag nanowire array. An index-matching adhesive was used to reduce the refl ection from the interface between glass substrate and remote system. The bundles of silver nanowire with 11 and 33 nm gap dis-tances are presented, while the distance between nanowires was about 100 nm. The lengths of the silver nanowire array were about 2.2 and ≈1 μm for 33 and 11 nm gap, respectively. As shown in the standard SERS, the incident laser was directed to focus on the top of the nanowires where the molecules were located. But for remote SERS, the incident laser was focused on the bottom glass substrate. In contrast to the above remote SERS systems, SPPs propagating along the silver nanowires originated not only from the incident laser, but also by the molecular Raman scattering in this nanowire array remote system. So the observation suggests that the remote distance was twice the length of nanowire array. Because of electrical resistance, SPPs propagating along the Ag nanowires could be attenuated exponentially as a function of the nanowire length, which was confi rmed by the results on the remote SERS with different lengths ranging from 1 to 3 μm. The results also indicate that the Raman signals observed from larger nanowires (88 nm) were stronger than those from smaller nanowires (68 nm). The difference is due to the enhanced function of the narrower inter-nanowire gap as a hot spot and to the lower attenuation achieved with the larger nanowire. As shown in Figure 17 , excellent SERS and remote SERS spectra can be obtained by such a remote nanowire array system. [ 55 ] Clearly, the plasmon catalyzed reaction of PATP to DMAB can be observed and monitored by remote probe, although here it was not comprehended that these SERS peaks were those of DMAB. The high remote SERS intensities indicate that the excited laser produced SPPs on the silver nanowire array can reach to the remote side of the nanowire; some energy was coupled out to create an optical near fi eld in the gaps at the remote side where excited the molecules.

Conclusions and Perspectives
We have reviewed plasmonic waveguide for remote-excitation surface catalytic reactions in detail, including the synthesis methods of Ag nanowires, the property and physical mechanism of plasmonic waveguides, and the successful applications of plasmonic waveguides in the fi eld of remote-excitation surface catalytic reactions. However, some challenges should be overcome in order to understand the full potential of remote plasmonic catalysis. More experimental and theoretical research, including on plasmon induced hot electrons, SPPs and plasmonic catalysis, is necessary in the near future so as to exploit the full potential of remote SERS systems. In addition, the distance of remote SERS based Figure 17. Averaged SERS spectra taken by a,b) direct excitation and c,d) remote excitation; a,c) gap of ≈11 nm with nanowire length of ≈920 nm (red), ≈1960 nm (blue), ≈2520 nm (green), and ≈3300 nm (black), respectively. b,d) Gap of ≈33 nm with NW length of ≈860 nm (red), ≈1880 nm (blue), ≈2160 nm (green), and ≈2880 nm (black), respectively. Reproduced with permission. [ 55 ] Copyright 2012, American Chemical Society. on metal nanowire waveguide is limited to a dozen μm. In the future, more methods for the synthesis of plasmonic materials should be developed, since the yield of Ag nanowire synthesized by chemical methods is limited. Stronger plasmonic waveguides should be created by nano-antenna, since the stronger intensity of plasmonic waveguide can result in a larger probability of chemical reaction. For example, withtwo or more Ag nanowires crossed, and two or more lasers simultaneously radiated on the terminals of the nanowires, collecting the remote SERS signals at the cross point. Better substrates should be developed for decreasing the loss of plasmonic waveguide on the preparation along nanowires.