Transition Metal‐Involved Photon Upconversion

Upconversion (UC) luminescence of lanthanide ions (Ln3+) has been extensively investigated for several decades and is a constant research hotspot owing to its fundamental significance and widespread applications. In contrast to the multiple and fixed UC emissions of Ln3+, transition metal (TM) ions, e.g., Mn2+, usually possess a single broadband emission due to its 3d 5 electronic configuration. Wavelength‐tuneable single UC emission can be achieved in some TM ion‐activated systems ascribed to the susceptibility of d electrons to the chemical environment, which is appealing in molecular sensing and lighting. Moreover, the UC emissions of Ln3+ can be modulated by TM ions (specifically d‐block element ions with unfilled d orbitals), which benefits from the specific metastable energy levels of Ln3+ owing to the well‐shielded 4f electrons and tuneable energy levels of the TM ions. The electric versatility of d 0 ion‐containing hosts (d 0 normally viewed as charged anion groups, such as MoO6 6‐ and TiO4 4‐) may also have a strong influence on the electric dipole transition of Ln3+, resulting in multifunctional properties of modulated UC emission and electrical behaviour, such as ferroelectricity and oxide‐ion conductivity. This review focuses on recent advances in the room temperature (RT) UC of TM ions, the UC of Ln3+ tuned by TM or d 0 ions, and the UC of d 0 ion‐centred groups, as well as their potential applications in bioimaging, solar cells and multifunctional devices.


Introduction
Luminescence research has been performed for centuries, and it has increased the worldwide availability of artificial lighting and displays. Photon UC, known as anti-Stokes emission, is a nonlinear optical phenomenon in which the sequential absorption of two or more low-energy photons leads to high-energy photon emission. [1] The process appears magical, but Auzel proposed the occurrence of energy transfer to activators (luminescent centres) that are already in the excited state. [1] This transfer is well established for activators in the ground state and can explain why n photons may be summed in the UC process. Some typical UC processes, such as energy transfer upconversion (ETU), excited state absorption (ESA) after ground state absorption (GSA), levels, which results in outstanding optical properties. However, the intentional modulation of UC behaviour is attractive for researchers to achieve the desired goals of specific applications. From this point of view, the less tuneable behaviour of the UC process is a disadvantage for Ln 3+ because the 4f electrons are less affected by the chemical environment owing to the shielding of the outer shell 5d and 6s electrons.
In contrast, the optical behaviour of TM (specifically d-block element ions with unfulfilled d orbitals) and d 0 ions (herein, d 0 ions are viewed as charged anion groups owing to the highvalence states of d-block elements, such as MoO 6 6-, VO 4 3-, and TiO 4 4-) can be extensively tuned because the outermost d electrons (there is a d electron for the excited state of d 0 ions) are strongly affected by their surrounding chemical environment. However, the UC of TM and d 0 ions is generally inefficient compared to that of Ln 3+ and is only observed at cryogenic temperatures owing to the high non-radiative transition probability of TM and d 0 ions in the UC process as the temperature increases. [1,8] Figure 2a and 2b describe the transition characteristics of TM and Ln 3+ ions with the assumed reservoirs. TM ions normally have broadband absorption but large non-radiative relaxation rates and small UC rates, whereas Ln 3+ has a relatively large UC rate and small non-radiative transition rate but narrowband absorption. To elucidate how non-radiative transition strongly influences the UC process, the simplified three-energy-level UC model (not considering the difference of ETU and ESA) in Figure 2c is utilised to determine the rate equation. Suppose that there are no other processes besides the ground-state absorption P 1 , subsequent excited-state absorption P 2 , depletion by radiative transitions R 1 , R 2 , and R 3 and nonradiative transitions D 1 and D 2 . The population and depletion rates of each energy level E are proportional to their population density N. Ground-state bleaching is assumed to be negligible, and ground state population N 1 is constant. Then, the rate equation can be written as: [9][10][11]  For steady-state excitation, dN 2 /dt = dN 3 /dt = 0, which yields: Then, it can be concluded that UC luminescence (R 3 N 3 ) is primarily determined by the absorption efficiency (P 1 N 1 ) and the radiative (R 1 N 2 ) and non-radiative (D 1 N 2 ) transition probabilities of the first metastable energy level E 2 , which indicates that a large absorption cross-section (broad band) and spin-and parity-allowed electric dipole transitions (E 1 →E 2 ) are preferred for the first term P 1 N 1 . The second term suggests that a metastable excited energy level with relatively long lifetime and weak electron-phonon coupling is required. The deduction of these two terms appears to be conflicting for E 2 but is reasonable if we take it not as a single energy level but as two levels from the respective sensitiser and activator for multicentre UC systems. [11][12][13] From this point of view, TM ions are preferred as sensitisers.
Despite the large multiphonon relaxation probabilities and luminescence quenching at RT for most TM ions, there are still some advances in the research on the RT UC of TM ions, especially those with tuneable single band NIR emission, such as Mn 2+ and Cr 3+ , with relatively large gaps between the adjacent emitting level and ground state, which is attractive for bioimaging. When coupled with the multiphoton absorption of quantum dots (QDs) [14,15] or the metastable energy levels of Ln 3+ , it is possible to gain enhanced UC emission at RT or Shi Ye earned his BSc degree (2004) in Material Chemistry at Lanzhou University, and received his PhD (2009) in Inorganic Chemistry at Peking University. After a postdoctoral fellow working on downconversion/upconversion luminescent materials in South China University of Technology, he joined the faculty in 2011. His current interests include research on structure-electronic structureproperties correlations of opto-functional inorganic materials and multifunctional materials.

Review
(3 of 25) 1600302 wileyonlinelibrary.com © 2016 The Authors. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim some other interesting UC phenomena. The UC process of Ln 3+ -TM ions benefits from the specific metastable energy levels of Ln 3+ , independent of the ligand field, owing to the well-shielded 4f electrons and the tuneable energy levels of the TM ions resulting from the exposure of d electrons to the chemical coordination environment, a feature that is fascinating for many applications. The selection of different hosts and Ln 3+ / TM ions results in novel and unexpected UC properties, which leaves room for imaginative and creative applications. [1,8] Moreover, materials with TM or d 0 -centered anion groups have versatile and attractive functionalities in addition to their optical properties, including ferroelectric, magnetic and photocatalytic properties. By incorporating TM or d 0 ions into the crystal lattice with Ln 3+ , the UC behaviour of Ln 3+ can be modulated via the electronic structure of the TM or the electric properties of the d 0 -contained hosts. [16] Thus, UC materials with incorporated TM or d 0 ions (anion groups) exhibit fascinating multifunctionality. The principles and approaches for achieving modulated UC behaviour of TM or d 0 ions (anion groups) and/ or Ln 3+ are schematically summarised in Figure 3. There are several reviews on UC and its applications, but they almost exclusively focus on the UC of Ln 3+ . [2,5,7,17] Consequently, this review focuses on the recent advances in the RT UC behaviour of UC materials doped with TM or d 0 ions (anion groups) and Ln 3+ and their potential applications, such as in solar cells, [5,6] optical temperature sensors, [18] bioimaging through combined nuclear magnetic resonance and the UC method [19] and photocatalysis, [20] with an emphasis on the modulated UC behaviour.

Photon Upconversion of TM Ions
The tuneable single-band feature is an advantage for some TM UC emissions and is strongly desirable for applications such as bioimaging. The UC behaviour of TM ions as either formula components or dopants, such as Mn 2+ , Cr 3+ , Re 4+ , V 3+ , Mo 3+ , Ni 2+ , and Ti 2+ , was extensively investigated at cryogenic temperatures by Auzel and Güdel et al. [1,8] However, their RT UC behaviour was rarely reported, except for that of Mn 2+ and Cr 3+ . Generally, the electron-phonon coupling effect for the d electrons of TM ions is larger than for the f electrons of Ln 3+ , resulting in a large nonradiative transition possibility for TM ions. Therefore, the UC emission of TM ions could only be observed at cryogenic temperatures for most TM-doped UC materials. For Mn 2+ (3d 5 ) and Cr 3+ (3d 3 ) ions, the emitting levels are normally the first excited states ( 4 T 1 and 4 T 2 or 2 E, respectively) with large gaps above the ground states (approximately 10,000-20,000 cm -1 ), as observed in Figure 4a and 4b, which provides a greater possibility to prevent multiphonon relaxation, resulting in radiative emission at RT. The possibility of radiative transition between the upper excited state and lower excited state for TM ions is much smaller than that for Ln 3+ , which is also due to the electron-phonon coupling. The cross-relaxation results in greater quenching of the transition because there are abundant energy levels for TM ions, as in the case of Ni 2+ (3d 8 ) and Re 4+ (5d 3 ). The cross-relaxation of 1 T 2 → 3 T 2 + 3 A 2 → 3 T 1 quenches the 1 T 2 → 3 A 2 green UC emission of Ni 2+ in MgF 2 when pumped by 752.5 nm laser, [21] see Figure 4c. Re 4+ was the first TM ion studied in UC material [22] and the first TM ion to show RT UC phenomenon owing to the relaxation of the spin selection rules by its strong spin-orbit coupling. [23] The UCemitting state Γ 7 ( 2 T 2g ) has a branching ratio of 1:2 for luminescence to ground state Γ 8 ( 4 A 2g ) relative to the intermediate excited state The cross-relaxation process involving the Γ 8 ( 2 T 1g ) state and Γ 8 ( 2 E g ) state would further reduce the UC luminescence efficiency. [24] The spin-forbidden transition characteristics of TM ions could be beneficial to the ESA UC process owing to the relatively long lifetime of the first excited state, for instance, the 3 T 1 → 1 T 2 transition of Ti 2+ (d 2 ) in MgCl 2 . [26] The spin-allowed transition characteristics of TM ions benefit the broadband sensitisation of UC ions, such as the 3 T 1g → 3 T 2g of V 3+ (d 2 ) and 2 A 1 → 2 B 2 of Cr 5+ (d 1 ) in V 3+ -Re 4+ , [27] V 3+ -Mo 3+ , [28] V 3+ -Er 3+ , [29] V 3+ -Pr 3+ [30] and Cr 5+ -Er 3+ [31] systems.   Sensitisation of the UC emission of TM ions with another TM or Ln 3+ in codoped systems requires the emitted TM ion to absorb the sensitising energy from another TM or Ln 3+ , but the latter cannot absorb the energy emitted by the former. This requirement for energy level matching rules out many TM-TM and Ln-TM couples because they have abundant energy levels in the full range of the visible and infrared regions. Furthermore, there are forward and backward energy transfer processes in these codoped systems. Yb 3+ , with only one simple excited state at ≈10,000 cm -1 , is an unique sensitiser for TM ions, especially for near-infrared (NIR) to visible (VIS) UC emission.

Visible Upconversion of Mn 2+
The UC of Mn 2+ sensitised by Yb 3+ was initially unexpected because Yb 3+ has no f excited state above 7 F 5/2 (≈10,000 cm -1 ), whereas Mn 2+ has no d excited state below 4 T 1 (≈17,000 cm -1 ). [8] Therefore, the UC of Mn 2+ -Yb 3+ is achieved via a cooperative sensitisation mechanism or exchange-coupled Mn 2+ -Yb 3+ dimer model. Bromide and chloride hosts with highly concentrated Mn 2+ were used to guarantee the neighbouring Mn 2+ -Yb 3+ in the first reported UC cases, ensuring the possibility of a superexchange interaction. There is a tendency for trivalent impurities to cluster in pairs owing to the charge compensation requirements in the linear-chain lattice when trivalent Ln 3+ substitutes for divalent cations. [32] For instance, in the RbMnCl 3 :Yb 3+ system, three neighbouring Mn 2+ ions are replaced by two Yb 3+ ions with one divalent vacancy as charge compensation, [32] as schematically illustrated in Figure 5a. Thus, the UC of Mn 2+ can be observed at cryogenic temperature, see Figure 5b. When directly exciting Mn 2+ , the Stokes luminescence of Mn 2+ shows an apparent redshift compared to the UC emission peak when exciting Yb 3+ in Figure 5b because the former is contributed by the Mn 2+ in the system, whereas the latter is contributed by the Mn 2+ in the vicinity of Yb 3+ by superexchange interaction. The temporal decay curve in Figure 5c without a rising stage suggests that the UC mechanism of Mn 2+ -Yb 3+ in this RbMnCl 3 :Yb 3+ system is GSA/ESA ( Figure 5d). Laser light excites the Mn 2+ -Yb 3+ pair from the | 2 F 7/2 , 6 A 1 > ground state into the | 2 F 5/2 , 6 A 1 > intermediate excited state in the GSA step. In the following ESA step, the pair is further promoted from the | 2 F 5/2 , 6 A 1 > state into the | 2 F 7/2 , 4 T 1 > emitting state and emits a visible photon. The detailed UC luminescence processes are as follows: The UC efficiency of the exchange-coupled Mn 2+ -Yb 3+ dimer is configuration geometry-dependent. [33] The ratio of the Mn 2+ UC and the Yb 3+ NIR was taken as a measure of the   The histograms roughly denote the gap energy between the excited state and ground state, in which the colour-filled region and empty region represent that the energy levels locate at visible range and infrared (IR) range, respectively. Reproduced with permission. [25] Copyright 1954, The Physical Society of Japan. UC efficiency when excited by a 980 nm laser. Table 1 shows that the observed UC efficiency decreases by orders of magnitude from corner-sharing bridging in Rb 2 MnCl 4 :Yb 3+ to edge-sharing in MnCl 2 :Yb 3+ /MnBr 2 :Yb 3+ to face-sharing in CsMnBr 3 :Yb 3+ . The coupling interaction may be weakened when the Mn 2+ -Yb 3+ distance increases but is strengthened by the linear configuration.
The UC luminescence of Mn 2+ -Yb 3+ in the above systems is only observed at cryogenic temperature. One possible reason may be the low-lying red emitting state of Mn 2+ , which is above the 7 F 5/2 state of Yb 3+ , resulting in multiphonon relaxation between the two states. The higher-lying emitting state of Mn 2+ in the green region could be responsible for the RT UC phenomenon, which occurs in Zn 2 SiO 4 :Yb 3+ ,Mn 2+ . [37] Another possible reason to be considered is that the highly-concentrated Mn 2+ would significantly quench the luminescence in most of the cases. It was initially and intentionally designed for the systems with highly-concentrated Mn 2+ in the early reports of Table 1 to ensure the vicinity of Yb 3+ and Mn 2+ ions. Recently, RT green or red UC of Mn 2+ has been observed in many other hosts with diluted Mn 2+ , such as LaMgAl 11 O 19 :Mn 2+ ,Yb 3+ aluminates, [38] GdMgB 5 O 10 :Mn 2+ ,Yb 3+ borates, [10] BaB 8 O 13 :Mn 2+ ,Yb 3+ borates, [39] MgGa 2 O 4 :Mn 2+ ,Yb 3+ gallates, [40] and KZnF 3 :Mn 2+ ,Yb 3+ perovskite fluorides. [41] The emission of Mn 2+ is strongly affected by the chemical coordination environment that accommodates the Mn 2+ ion. Green emission of Mn 2+ at ≈514 nm is observed when it replaces Mg 2+ in LaMgAl 11 O 19 :Mn 2+ ,Yb 3+ , which is tetrahedrally coordinated with oxygen ions. [38] When Mn 2+ substitutes for Mg 2+ in the MgO 6 octahedron of GdMgB 5 O 10 :Mn 2+ ,Yb 3+ , it emits red light at ≈620 nm. [10] Moreover, white-light emission composed of two broadbands with peaks at 490 and 620 nm is achieved in GdMgB 5 O 10 :Mn 2+ ,Yb 3+ , as observed in Figure 6a and 6b, originating from the upconverted emissions of Yb 3+ -Yb 3+ and Yb 3+ -Mn 2+ dimers, respectively. The cooperative luminescence and sensitisation mechanisms are excluded for these two dimers according to the luminescence behaviours, and exchange interaction models are proposed for these two-photon processes based on the crystal structure. The   -1 , respectively, at 10 K; c) Temporal behavior of Mn 2+ UC emission after excitation of a pulsed laser light ≈10686 cm -1 at 15 K, inset shows the same data in a semilogarithmic scale; d) The proposed UC luminescence process. Reproduced with permission. [32] Copyright 2001, The American Physical Society. Table 1. Comparison of (Mn 2+ /Yb 3+ ) polyhedral bridging geometry, Mn 2+ -Yb 3+ distance, Mn-L-Yb angle (L = halogen ions) and UC efficiency (ratio of the Mn 2+ UC emission to the Yb 3+ NIR emission was used when a 191 mW laser beam was focused on the sample by an f = 53 mm lens). [33] Compound Bridging  [33] large deviations from two of the plot slopes (1.2 and 0.9) of the UC luminescence intensity as a function of pump power in Figure 6c are quantitatively interpreted by the large UC rate for both cases and an additional depletion pathway of relaxation from the upper excited state | 2 F 7/2 , 4 T 1 > to the intermediate state | 2 F 5/2 , 6 A 1 > for the Yb 3+ -Mn 2+ dimer ( Figure 6d) according to the exchange interaction model and rate equations. [9,10] The UC luminescence colour can be tuned by varying the amounts of Yb 3+ and Mn 2+ , indicating that GdMgB 5 O 10 :Yb 3+ , Mn 2+ is a potential candidate for lighting and displays. It was recently demonstrated that RT Mn 2+ UC emission could be tuned from 550 to 610 nm in Yb 3+ /Mn 2+ codoped fluoride perovskite homologous compounds ABF 3 (A = K + , Rb + and Cs + ; B = Mg 2+ , Zn 2+ and Cd 2+ ), as shown in Figure 7a, depending on the A + and/or the B 2+ cations. [42,43] The different bond length of (B 2+ /Mn 2+ )-Fcauses distinct crystal field strength on Mn 2+ , resulting in a different wavelength for Mn 2+ . These UC emissions have ultra-long decay lifetimes (Figure 7b). Because Yb 3+ may substitute both the A + and the B 2+ cations in KMgF 3 and KZnF 3 , two exchange-coupling geometry models for Yb 3+ -Mn 2+ UC luminescence are proposed in Figure 7c. For the other hosts, Yb 3+ could only substitutes B 2+ cation according to the luminescence data, which was also found in previous work. In contrast to the well-known multiple and fixed UC emissions from Ln 3+ activated materials, the room (or high) temperature UC emission and ultra-long UC decay lifetimes (≈25-45 ms) of the ABF 3 :Yb 3+ ,Mn 2+ perovskites suggest that they have potential applications in timeresolved luminescence imaging, lighting and solid-state lasers. UC emission of Mn 2+ could also be sensitised by the semiconductor QDs via multiphoton excitation. Multiphoton excitation, which is a process that occurs when multiple photons are simultaneously absorbed within QDs through virtual states, is a common phenomenon for semiconductor QDs. Normally, the emission of QDs in this multiphoton excitation process is intraband transition between the conduction band and the valence band. When doping with Mn 2+ , UC emission of Mn 2+ can be observed. Take ZnS:Mn 2+ for an example; strong UC luminescence of Mn 2+ is observed in bulk and nanoparticle ZnS:Mn 2+ . [14] Based on the experimental data of the quadratic power dependence of UC emission and the nearly identical luminescence profiles and lifetimes upon excitation at 385.5 and 767 nm, the authors concluded that the UC luminescence of ZnS:Mn 2+ occurred through a two-photon process, even though there is no energy level at the excitation wavelength of 767 nm for either ZnS or the Mn 2+ ion. Further UC emission experiments of Eu 3+ -codoped ZnS:Mn 2+ provided evidence of the two-photon absorption mechanism. [15] The emission profiles for UC and Stokes luminescence when exposed to UC excitation wavelengths and half of the UC excitation wavelength (double the energy) are analogous in this system. However, a change of a few nanometres in the excitation wavelength results in a dramatic change in the UC emission intensity for Eu 3+ single-doped ZnS, indicating that there is a mismatch between the Eu 3+ energy levels and double the energy of the UC excitation wavelength. Most recently, threephoton-excited UC luminescence of ZnS:Mn 2+ nanocrystals was proposed based on the slope (≈2.9) of the Mn 2+ UC emission intensity as a function of the incident power. [44] The large three-photon cross-section of ZnS QDs results in high spatial resolution for targeted cellular imaging, and the three-photon process modulated by Mn 2+ with visible red emission enables its application in high-resolution in vivo deep-tissue imaging without ultraviolet-induced photo-damage.

Near-Infrared Upconversion of Mn 2+
Single NIR UC emission is highly preferred in bioimaging applications because it can penetrate deeper into tissue with less noise. Traditionally, Mn 2+ has been considered as a VIS emitting ion. Most recently, abnormal NIR emission of Mn 2+ at RT was reported in addition to the normal VIS emission. [42,45] For KZn 0.995-x Mn x Yb 0.005 F 3 systems at a low Mn 2+ concentration (x = 0.05), the emission spectrum consists of a single VIS UC emission centred at 585 nm, as shown in Figure 8a, corresponding to the | 2 F 7/2 , 4 T 1 >→ | 2 F 7/2 , 6 A 1 > transition of the Yb 3+ -Mn 2+ dimers. In contrast, an additional anomalous NIR emission band centred at 770 nm emerges in the luminescence spectra in Figure 8a and 8b when the doping concentration of Mn 2+ is sufficiently high (x = 0.10-0.40). [45] Figure 8c and 8d demonstrate that the two emission peaks exhibit distinct decay behaviour, which suggests that the peaks originate from different emission centres. Usually, Mn 2+ in a solid matrix exhibits only visible photoluminescence owing to the relatively large energy gap (>17,000 cm -1 ) between the first excited level and the ground state of the 3d 5 electronic configuration. Normally, when the electrons of Mn 2+ are excited to energy levels above the 4 T 1 ( 4 G) emitting state, relaxation occurs non-radiatively from the higher states until the emitting state is reached. This transition strongly depends on the crystal field of the ligands, which is most visible in the characteristic green luminescence typically associated with tetrahedral-coordinated Mn 2+ (i.e., weaker ligand field) and the orange or red luminescence from octahedral Mn 2+ (i.e., stronger ligand field). [46] NIR emission has recently been observed in association with Mn 2+ doping at elevated Mn 2+ concentrations, as observed in Figure 8, which is not currently understood because only one large energy gap between the ground state and the first excited state of Mn 2+ is known to cause luminescence. There is only a single, well-defined lattice site that Mn 2+ can possibly occupy in this simple cubic perovskite compound. One possible explanation for this concentrationdependent behaviour is the occurrence of Mn 2+ ion aggregation. The delocalisation and interaction of the 3d electrons of Mn 2+ may result in novel luminescent centres with unusual luminescence behaviour. The novel NIR UC emission has been experimentally and theoretically investigated in Yb 3+ /Mn 2+ codoped KMgF 3 perovskites.
The Mn 2+ concentration-dependent photoluminescence phenomena of KMgF 3 :Yb 3+ ,Mn 2+ nanocrystals [42] are illustrated in Figure 9a, which is analogous to Figure 8. First-principle calculations of the lattice geometry of possible substitution models revealed that the model with the shortest Mn 2+ -Mn 2+ distance and antiferromagnetic (AFM) interaction has the lowest formation energy, which suggests that Mn 2+ aggregation may occur. [42] This is in agreement with the previously reported experimental observation of AFM in KMnF 3 and KMgF 3 :Mn 2+ . The extended X-ray absorption fine structure (EXAFS) provides experimental evidence for Mn 2+ ion aggregation in KMgF 3 :Mn 2+ , which is in good agreement with the luminescence behaviour of KMgF 3 :Mn 2+ with increasing Mn 2+ content. The aggregation-induced, geometrydependent coupling of Mn 2+ is indicated by the temperature-dependent emission spectra of KMnF 3 , NaMnF 3 and CsMnF 3 , which provide different Mn 2+ -Mn 2+ linkage geometry because of the different radii of the alkali ions. [42] Therefore, UC models for VIS and NIR emission in this system are proposed in Figure 9b based on the Yb 3+ -Mn 2+ dimer and Yb 3+ -Mn 2+ -Mn 2+ trimer images, respectively, with the GSA/ESA mechanism. Furthermore, the ligand-field-dependent luminescence behaviour of these emission centres was also investigated. [42] Figure 9c presents the UC emission spectra of ABF 3 :20%Mn 2+ ,0.5%Yb 3+ upon excitation with a 976 nm laser diode. The emission spectra comprise both VIS and NIR emission. The VIS UC emission occurs at 605, 585, 567, 563 and 550 nm in the Yb 3+ /Mn 2+ codoped KMgF 3 , KZnF 3 , KCdF 3 , RbCdF 3 and CsCdF 3 , respectively. In addition, the corresponding NIR UC emission is centred at 765, 770, 795, 805 and 830 nm. These results demonstrate that the UC emission centres of Yb 3+ -Mn 2+ dimers (pairs) and Yb 3+ -Mn 2+ -Mn 2+ trimers have an intrinsic formation tendency in these Yb 3+ / Mn 2+ -doped perovskite structures. Both the VIS and NIR emissions could be finely tuned. The VIS emission monotonically blueshifts with an increase in the lattice constant owing to the decrease of crystal field strength. However, the NIR emission gradually shifts in the opposite direction with increasing lattice constant. The NIR/VIS emission ratio decreases monotonically  The proposed UC luminescence mechanism. Reproduced with permission. [43] with increasing lattice constant, indicating that the Mn 2+ -Mn 2+ dimers are preferentially formed in the host lattice with shorter Mn 2+ -Mn 2+ distance. The NIR emission band may result from the 6 A 1g (S) 4 T 1g (G)→ 6 A 1g (S) 6 A 1g (S) transition of the coupled Mn 2+ -Mn 2+ dimers, which is a spin-allowed transition with a decay lifetime shorter than 0.50 ms. NIR emissions have also been found in other Mn 2+ -Yb 3+ doping systems, such as MgGa 2 O 4 : Mn 2+ ,Yb 3+ gallates. [40] The result is fascinating because the observed NIR UC emission is located in the "optical window" of living cells and tissues, which provides an opportunity to achieve high-resolution and deep penetration in biological imaging. The present results not only provide a useful and effective approach for obtaining pure NIR UC emission but also new perspective on the development of advanced photonic devices and technologies.

Upconversion of Cr 3+
Cr 3+ is another commonly used TM luminescent centre with efficient deep red or NIR emission that can be cooperatively sensitised by Yb 3+ to achieve UC emission in YAlO 3 , Y 3 Al 5 O 12 and Y 3 Ga 5 O 12 . [8] Cr 3+ has no excited states below 14,000 cm -1 , whereas Yb 3+ has none above 10,000 cm -1 . However, the UC of Yb 3+ -Cr 3+ was observed, as shown for Y 3 Ga 5 O 12 : Yb 3+ ,Cr 3+ in Figure 10. [47] The excitation spectra of Yb 3+ NIR luminescence, Yb 3+ -Yb 3+ green UC emission and Cr 3+ red UC emission have similar profiles in Figure 10a, which is ascribed to the absorption of Yb 3+ : 2 F 7/2 → 2 F 5/2 . The sharp UC emission 2 E→ 4 A 2 of Cr 3+ gradually changed to a broad UC emission of 4 T 2 → 4 A 2 of Cr 3+ with increasing temperature, as shown in Figure 10b, because the 4 T 2 state could be thermally populated at elevated temperature. The smaller gap between the 4 T 2 state of Cr 3+ and the 2 F 5/2 state of Yb 3+ (with a reference gap between the 2 E state of Cr 3+ and the 2 F 5/2 state of Yb 3+ ) causes stronger temperature quenching in this system. The apparent increase in the early stage of the UC decay curve in Figure 10c suggests the occurrence of energy transfer. Because the Yb 3+ -Yb 3+ dimer is not likely formed in this garnet structure, the excited energy of two Yb 3+ ions could simultaneously transfer to the Cr 3+ in their vicinity, as demonstrated in Figure 10d. This so-called cooperative sensitisation mechanism requires the overlap of an excited state with twice the absorbed energy of Yb 3+ .
However, RT UC emission of Cr 3+ has rarely been reported. Recently, RT UC emission of Cr 3+ has been achieved via energy transfer from Ln 3+ ions when pumped by a 980 nm laser diode, such as La 3 Ga 5 GeO 14 :Yb 3+ ,Er 3+ , Cr 3+ , [45,48] La 3 Ga 5 GeO 14 :Yb 3+ ,Tm 3+ ,Cr 3+ , [49] and Zn 3 Ga 2 GeO 8 :Yb 3+ ,Er 3+ ,Cr 3+ . [49] When introducing the new function of persistent luminescence in the UC emission of Cr 3+ , the novel phenomenon of upconverted persistent luminescence (UCPL) has been conceptually demonstrated by combining Ln 3+ (with outstanding UC performance) with Cr 3+ (with excellent persistent luminescence) in Zn 3 Ga 2 GeO 8 :Yb 3+ ,Er 3+ ,Cr 3+ . [49] The unique NIR UCPL emission is ascribed to the 2 E→ 4 A 2 transition of Cr 3+ , as shown in Figure 11. The directly observed phenomenon is the afterglow emission after stoppage of a 980 nm laser for the samples preheated for 20 min at 400 °C to completely empty the electron traps. The UC emission of Yb 3+ -Er 3+ is firstly absorbed by Cr 3+ , as proved by the overlap between the excitation spectrum of Cr 3+ and the emission spectrum of Er 3+ in Figure 11b. Then, the absorbed energy transfers to the trap centres and is finally released in the form of Cr 3+ NIR emission by thermal activation. The VIS UC emission of Er 3+ induced persistent luminescence of Cr 3+ , as shown by the similar persistent luminescence induced by a red LED light. [49] The emission peak at ≈1000 nm in Figure 11c is due to the energy transfer from Cr 3+ to Yb 3+ . More evidence for the UCPL phenomenon is that different duration times of the 980 nm laser cause distinct thermoluminescence (TL) peaks in this Zn 3 Ga 2 GeO 8 :Yb 3+ ,Er 3+ ,Cr 3+ system, and they are also different from the TL behaviour excited by UV or visible light. It suggests that 980 nm laser illumination not only produces upconverted excitation to fill the traps but also influences the electron distribution in the traps. While the shallow traps are capturing electrons from the excited Cr 3+ , the 980 nm excitation is also promoting the trapped electrons to  Reproduced with permission. [45] the delocalised conduction band, resulting in depopulation of electrons in the shallow traps. [49] Conceptually, this NIR UCPL offers the potential of excitation-free and noise-free deep tissue in vivo imaging for bioapplications.
However, UCPL was not observed in La 3 Ga 5 GeO 14 :Cr 3+ ,Yb 3+ ,Er 3+ , even though there was NIR persistent luminescence of Cr 3+ and energy transfer from the UC of Er 3+ to Cr 3+ . [48] Therefore, the temperature-dependent UC luminescence of Er 3+ and Cr 3+ in this system was investigated in detail, and the results are presented in Figure 12. The NIR UC luminescence at ≈830 nm is ascribed to the 4 T 2 → 4 A 2 transition of Cr 3+ . The NIR emission intensities of all samples show an initial increase followed by a decline with increasing temperature, whereas that of the UC green emission of Er 3+ behaves distinctly for samples with different concentrations of Cr 3+ . For the sample with low concentration (x = 0.02) of Cr 3+ (Figure 12b), it decreases as the temperature rises, whereas for the sample with a higher concentration (x = 0.06) of Cr 3+ (Figure 12d), there is a distinct initial increase followed by a decrease as the temperature rises. For the sample with a high concentration (x = 0.15) of Cr 3+ (Figure 12f), it varies little with temperature. Additionally, the red emission intensity does not vary dramatically with temperature. Normally, thermal quenching behaviour is expected as the temperature rises because the probability of multi-phonon relaxation and energy transfer to quench the emitting levels is enhanced. However, anti-thermal-quenching behaviour was observed in this system, as shown in Figure 12. A possible reason for this phenomenon is that there may be TL in this system. The sample shows a TL peak, but after heating, there is a horizontal line in the temperature range from 313 to 473 K. When the sample is excited by a 976 nm laser for 5 min in a black box, the TL spectrum remains as a horizontal line. The TL peak reappears with sample exposure to simulated sunlight for 5 min. These facts suggest that the anomalous temperature-dependent UC emissions cannot be ascribed to the persistent luminescence of these phosphors because excitation of the samples with a 976 nm laser does not lead to TL peaks. The recovery ability of the temperature-dependent UC spectra of the samples also reveals that there is no TL effect in the temperature-dependent UC processes. The temperature-dependence of Cr 3+ emission can be explained by the configurationally coordinate model, in which different thermal activation energies for each equilibrium excited state at different temperatures are considered. The Er 3+ emission is ascribed to the complex forward and backward energy transfer processes among the dopants Cr 3+ / Yb 3+ /Er 3+ . The reason for the absence of UCPL needs to be investigated further.
UC emission of Cr 3+ could also be observed without a sensitiser, such as Ln 3+ . A sharp UC emission peak at ≈694 nm originating from 2 E→ 4 A 2 of Cr 3+ in the Al 2 O 3 crystal without Yb 3+ was observed when irradiated with an IR femtosecond laser at 800 nm. [50] Because there is no energy level at ≈800 nm according to the absorption spectrum of Al 2 O 3 :Cr 3+ , a simultaneous two-photon absorption mechanism is proposed for the UC process based on the ultrafast characteristics of the femtosecond laser. However, the same result can be achieved in Zn 3 Ga 2 GeO 8 : Cr 3+ upon excitation with continuous-wave 800 nm laser diodes with sufficient pumping power. [51] As observed in Figure 13, the broadband 650-730 nm emission of Cr 3+ , owing to the incorporation of the 2 E→ 4 A 2 and 4 T 2 → 4 A 2 transitions, is observed with 800 nm laser excitation. This material also shows persistent luminescence of Cr 3+ , and the temperature-dependent excitation photon energy and the persistent luminescence intensity suggest that it involves phonons during the excitation process. The pumpingpower-dependent integrated TL intensity in Figure 13 indicates that it is a phonon-assisted one-photon process at low power and a two-photon process at high power. It could fill low-energy traps for the former and high-energy traps for the latter. The unique single NIR emission band characteristic of Cr 3+ may also be attractive for bioimaging applications.

Upconversion of Some Other TM Ions
There are few cases of other TM ions demonstrating UC emission at RT because they all have complex and abundant energy levels in the VIS and IR region. Qin. et al. [52] recently reported that the UC emission of the Cu 2+ : 3d 8 4s 1 →3d 9 transition at ≈420 nm was observed in CaF 2 :Yb 3+ ,Cu 2+ upon 978 nm NIR laser excitation, as shown in Figure 14, owing to the energy transfer process from the Yb 3+ trimer to Cu 2+ in the host CaF 2 ; this process was indicated by the observation of triplet cooperative luminescence at ≈343 nm from the Yb 3+ trimer and the UC  . Reproduced with permission. [42] decay curve variation of the Yb 3+ trimer, Yb 3+ dimer and Cu 2+ emission. The splitting of the Cu 2+ blue emission into three peaks at low temperature was due to the Jahn-Teller effect of Cu 2+ in CaF 2 . It is interesting that the 3d 8 4s 1 →3d 9 transition of Cu 2+ is not quenched by its d-d transition and the f-f transition of the Ln 3+ ion impurity introduced by the raw materials.
In addition to the sensitisation effect of Ln 3+ in the UC process, TM ions, themselves with a suitable gap between energy levels, can also absorb the pumped light to facilitate the UC process. For instance, broadband green UC luminescence of Ni 2+ in KZnF 3 is observed at all temperatures ranging from 15 K to RT by excitation into the 3 T 1g (3F) or 1 E g excited state of Ni 2+ with monochromatic light, which is quite different from that of Ni 2+ -doped chloride and bromide materials with the 1 T 2g → 3 A 2g luminescence of Ni 2+ located in the red region and quenched well below RT. [53] Normally, the overall UC efficiency is low in UC materials for narrowband laser excitation. However, an increase of roughly an order of magnitude is observed for Cs 2 NaYCl 6 :V 3+ , Re 4+ compared with that of a Re 4+ singly doped broadband excitation, [8] which is attributed to the broadband absorption characteristics of TM ions. The UC luminescence of this material can be observed by the naked eye up to RT.
There is another distinct UC process of thermal radiation when sensitised by TM ions in Cu 2+ -or Cr 3+ -doped ZrO 2 . [54] This is a type of UC process that absorbs NIR sunlight or laser energy, resulting in a temperature increase of the material's body through multiphonon relaxation, followed by release via thermal radiation, such as the blackbody radiation, as illustrated in Figure 15. The broadband absorption nature of Cu 2+ and Cr 3+ makes the Cu 2+ -or Cr 3+ -doped ZrO 2 sample glow when excited by concentrated and filtered sunlight, whereas the Yb 3+ -doped ZrO 2 sample, with a relatively narrow absorption band, does not glow. However, the latter exhibits the highest UC power efficiency when stimulated by laser, as high as 16% greater than the former. This is because the power of concentrated and filtered sunlight is smaller than the power of a laser. The authors also stated that TM dopants inevitably alter the thermal conductivity, melting point and refractive index of the host, especially at a high doping level. The Cu 2+ -or Cr 3+ -doped ZrO 2 samples may suffer high thermal conductivity. Therefore, the authors concluded that materials with higher melting points and lower thermal conductivities would work at higher blackbody temperatures and dissipate less heat with higher UC efficiency. [54] 3. Upconversion of Ln 3+ Tuned by TM or d 0 Ions

Upconversion of Ln 3+ Modulated by TM Ions
Doping with TM ions is a novel strategy for synthesising controllable UC nanomaterials in terms of nanocrystal growth and the resulting UC behaviour. For instance, Mn 2+ -doping affects the growth dynamics and provides simultaneous control of the crystalline phase and the size of the resulting NaYF 4 :Yb/Er UC nanoparticles synthesised using a modified liquid-solid solution solvothermal strategy. [55] Without Mn 2+ doping, the resulting product is a mixture of cubic and hexagonal phases. The hexagonal phase changes to the cubic phase after doping with a sufficient amount of Mn 2+ . Generally, dopant ions with larger ionic radii favour hexagonal structures, whereas smaller dopant ions tend to produce the cubic phase in the final products. [56] www.MaterialsViews.com www.advancedscience.com Adv. Sci. 2016, 3, 1600302   Figure 10. a) Excitation spectra (I-III) of Y 3 Ga 5 O 12 (YGG):2%Cr 3+ ,1%Yb 3+ at 15 K monitoring the NIR Yb 3+ (at 9770 cm -1 ),the red Cr 3+ (at 14388 cm -1 ) and the green Yb 3+ -Yb 3+ luminescence (at 20628 cm -1 ), respectively. IV shows the square of spectrum in I; b) Temperature dependence of the UC luminescence spectra of the sample upon 10314 cm -1 laser excitation; c) time evolution of the sample following 10 ns pulsed excitation with the excitation wavelength of 14641 cm -1 (I) and 10314 cm -1 (II) at 15 K. The inset shows the enlarge scale of rise-up in (II); d) UC mechanism scheme: straight up, dashed, curly and straight down arrows represent excitation, nonradiative energy transfer, nonradiative multiphonon relaxation and luminescence steps, respectively. Reproduced with permission. [47] Copyright 2002, The American Physical Society.
In this case, the smaller Mn 2+ ion incorporated into NaYF 4 nanocrystals favours the formation of a pure cubic phase. However, Mn 2+ substituted for Y 3+ in NaYF 4 can result in an extra Fion on the grain surface and induces transient electric dipoles with their negative poles pointing outward. This effect would substantially hinder the diffusion of the Fions required for crystal growth from the solution to the grain surface owing to charge repulsion, resulting in retardation of NaYF 4 nanocrystal growth. [55,56] Similar phase transformation phenomena were observed in NaLnF 4 :Yb/Er (Ln = Lu, Yb, Gd) UC nanoparticles, [57] with simultaneous phase/size control and significantly enhanced UC intensity via Mn 2+ doping. However, a conflicting result, with uniform bundle-shaped β-NaYF 4 (hexagonal phase) microtubes composed of six half-pipes synthesised in hydrothermal solutions with trisodium citrate and Mn 2+ doping, was obtained, which was proposed to be caused by an intentional delayed phase-transition pathway induced by Mn 2+ . [58] A further demonstration of small Mn 2+ -modulated NaYF 4 nanocrystals synthesised by hot-injection was provided in a recent work, [59] indicating that the Mn 2+ dosage, growth temperature, and heating rate determine the doping modes (surface or interior). Interior doping contributes to red emission, whereas surface doping suppresses the growth of large nanocrystals.
Mn 2+ is capable of tuning the UC behaviour of Ln 3+ ions via Mn 2+ -induced morphology/phase control and through the energy levels of Mn 2+ , such as in MnF 2 :Yb 3+ ,Er 3+ . [60] It was recently demonstrated that Mn 2+ could tune the UC emission of Er 3+ , Ho 3+ , and Tm 3+ into a single emission band in KMnF 3 when codoping with Yb 3+ , [61] as demonstrated in Figure 16.
Generally, these Ln 3+ ions have more than one metastable excited state energy level, resulting in multiple emission peaks and low chromatic colour purity. The singleband emissions of Er 3+ , Ho 3+ , and Tm 3+ in KMnF 3 are caused by the efficient forward and backward energy transfer between Er 3+ / Ho 3+ /Tm 3+ and Mn 2+ at different energy levels, as shown in Figure 16. In addition, the single-band emission is independent of the dopant concentration, pump power, and temperature, which provides additional evidence of the efficient energy transfer pathway. The KMnF 3 :Er 3+ ,Yb 3+ prepared by an oil-based synthetic procedure in this work has a higher ratio of red to green emission than that synthesised by the hydrothermal method in a previous work, [62] likely because of the more homogeneous doping of the large Ln 3+ content into the KMnF 3 host in the former. The single emission band feature of UC nanocrystals has been developed for applications in anti-counterfeiting, colour displays, and deep-tissue imaging without constraints. Intense pure red emission is also obtained in sub-10 nm NaMnF 3 :Yb 3+ ,Er 3+ nanocrystals. [19] Analogous tuned behaviour of NaYF 4 :Yb 3+ ,Er 3+ nanoparticles by Mn 2+ doping was observed in previous research, [55,58,59] one of which is illustrated in Figure 17. It is attributed to the non-radiative energy transfer from the 2 H 9/2 and 4 S 3/2 levels of Er 3+ to the 4 T 1 level of Mn 2+ , followed by back energy transfer to the 4 F 9/2 level of Er 3+ , as discussed above. Mn 2+ doping facilitates the single band feature of red emission and enhances the intensity of UC emission, which arises from the change in the surrounding environment of Ln 3+ ions and the energy transfer between Er 3+ and Mn 2+ ions. Water-soluble and biocompatible poly(ethylene glycol)conjugated phospholipid (DSPE-PEG 2000) is used to coat the oleate-capped nanocrystals for imaging of deep tissue in Kunming mouse. The modified nanocrystal solutions are injected respectively at foot, back and upper leg regions of the mice to investigate the dose effect. The injection depth is estimated by the needle penetration (about 10 mm). Results show that the signals from such deep tissue are obvious for the Mn 2+ doped samples. The Mn 2+ doping also benefit the magnetic resonance imaging as a second imaging capacity. [55] Additionally, significant tuning of the output colour by adjusting the contents of Mn 2+ is only obtained in cubic NaYF 4 nanoparticles and not in hexagonal microtubes. [58] Tian et al. [63] proposed that the incorporation of Mn 2+ in hexagonal NaYbF 4 :Er reduced the Na vacancies to offset the imbalance of charge and reduced organic absorption on the surface of the nanocrystals by the extra Fand Mn 2+ on the surface, which resulted in enhanced UC emission of Er 3+ . There is additional research work on Mn 2+ incorporated in fluorides, such as in the new host matrix KLu 3 F 10 :Yb,Mn,Er/Ho/Tm, [64] the plasma coupling effects of an Ag array on NaYF 4 :Yb,Er,Mn, [65] and the high magnetic field and temperature tuning effects on NaYF 4 :Yb,Er,Mn. [66]   The upper right insert is the UCPL decay curve monitored at 700 nm emission. The left insert shows the NIR images (false color) taken at different delay times (5 min to 24 h) after ceasing the 980 nm laser excitation. For all the UCPL measurements, the samples were irradiated by a 980 nm laser for 10 min at a power of 600 mW. Reproduced with permission. [49] Copyright 2014, American Physical Society.
As observed above, Mn 2+ emission is rarely observed when codoped with Ln 3+ in an Yb 3+ -Mn 2+ UC system owing to the complex forward and backward energy transfer between Ln 3+ and Mn 2+ ions, [55,57,60,61] which have abundant energy levels above and below the 4 T 1 emitting state of Mn 2+ . There are two approaches to obtain additional Mn 2+ emission besides the Ln 3+ emission in these triply codoped systems. One is to decrease the amount of Ln 3+ ; [67,68] the other is to control the spatial distribution of Ln 3+ and Mn 2+ with a certain separated distance, such as using a core-shell structure. [69] For the combination of Mn 2+ emission with Ln 3+ emission, white light can be easily achieved, as in the example of KZnF 3 :Yb 3+ ,Mn 2+ ,Tm 3+ in Figure 18. [67] The sharp emission peaks at 480, 650 and 700 nm in Figure 18a can be ascribed to the 1 G 4 → 3 H 6 , 1 G 4 → 3 F 4 , and 3 F 2,3 → 3 H 6 transitions of the Tm 3+ ion, respectively. The broad emission band centred at 585 nm corresponds to the emission of Mn 2+ . The CIE chromaticity coordinates of white light shift slightly with variation of the pumping power, as shown in Figure 18b, which is due to the complex energy transfer involved in Yb 3+ / Mn 2+ /Tm 3+ . The power dependency of the UC emission intensities with different slope values in Figure 18c suggest that the 480 and 650 nm UC emissions are three-photon processes, whereas the 585 and 700 nm UC emissions are two-photon processes. The 4 T 1g excited state of Mn 2+ is lower than the 1 G 4 excited state of Tm 3+ but higher than the 3 F 2,3 excited state of Tm 3+ . Therefore, energy transfer between Mn 2+ and Tm 3+ ions may occur in Yb 3+ /Tm 3+ /Mn 2+ tri-doped KZnF 3 , in which the energy is transferred from 1 G 4 of Tm 3+ to 4 T 1g of Mn 2+ and then back to the 3 F 2,3 state of Tm 3+ . A possible UC mechanism in the Yb 3+ /Tm 3+ /Mn 2+ tri-doped system is proposed in Figure 18d. The broadband yellow UC luminescence is resulted from sequential GSA/ESA processes for the Yb 3+ -Mn 2+ dimer. The 700 nm band of Tm 3+ was enhanced by bi-directional energy transfer between Tm 3+ and the Yb 3+ -Mn 2+ dimer.
The concentration-dependent, temperature-dependent and laser-pulse-durationdependent energy transfer processes among Yb 3+ /Ho 3+ /Mn 2+ ions in KZnF 3 were investigated in detail, and some of the results are presented in Figure 19. [68] Upon 976 nm laser excitation, the KZnF 3 :Yb 3+ ,Mn 2+ sample exhibits a broad UC emission band centred at 585 nm in Figure 19a, originating from the   | 2 F 7/2 , 4 T 1 >→ | 2 F 7/2 , 6 A 1 > transition of Yb 3+ -Mn 2+ dimers. Three typical emission peaks located at 539, 658 and 749 nm appeared with the introduction of Ho 3+ ions into KZnF 3 :Yb 3+ ,Mn 2+ and are ascribed to the 5 S 2 / 5 F 4 → 5 I 8 , 5 F 5 → 5 I 8 and 5 S 2 / 5 F 4 → 5 I 7 transitions of Ho 3+ , respectively. The yellow UC emission from Yb 3+ -Mn 2+ dimers sharply decreases and is nearly quenched as the concentration of Ho 3+ increases to z = 0.5%. Meanwhile, the green and red UC emissions from Ho 3+ are enhanced. For the KZnF 3 : 1%Yb 3+ ,0.005%Ho 3+ ,5%Mn 2+ sample, the temperaturedependent emission intensity of all UC bands in Figure 19b decrease monotonically with increasing temperature, which is similar to that of undoped samples and is due to the non-radiative multiphonon process. The ratio of R/G behaves distinctively. When the temperature is between 298 and 373 K, the ratio of R/G gradually decreases from 1.36 to 0.98 with increasing temperature (not shown in Figure 19). Further increased the temperature increases the R/G ratio. The decrease in the R/G ratio between 298 and 373 K suggests that there is a new process to be considered. The strong red UC emission of Ho 3+ in this system is due to the bidirectional energy transfer (ET1 and ET2) between Ho 3+ and Mn 2+ (Yb 3+ -Mn 2+ dimer), as shown in Figure 19e. Because of ET1, some of the energy of Ho 3+ can be transferred to the 4 T 1 state of Mn 2+ or the | 2 F 7/2 , 4 T 1 > state of the Yb 3+ -Mn 2+ dimer. With increasing temperature, the nonradiative relaxation of Mn 2+ or Yb 3+ -Mn 2+ dimer is inevitable, promoting the dissipation of energy by defects or through the surface, which hinders the back energy transfer (ET2) to the 5 F 5 state and leads to a sharply decreasing ratio of R/G UC emission with increasing temperature. When the temperature exceeds 373 K, the multiphonon relaxation from 5 I 6 to 5 I 7 dominates, as it does in the Ho 3+ /Yb 3+ -codoped system, resulting in the increase. Figure 19c and Figure 19d show the UC emission spectra of KZnF 3 :1%Yb 3+ ,1%Ho 3+ and KZnF 3 :15% Mn 2+ ,1%Yb 3+ ,1%Ho 3+ under excitation with a 976 nm laser with different pulse widths (50 µs ≈ 6 ms). When KZnF 3 :1%Yb 3+ ,1%Ho 3+ is pumped by a long-pulse-width laser (6 ms, 100 Hz), the characteristic intense green and red UC emissions of Ho 3+ are observed. The UC spectrum under long-pulse-width laser excitation is similar to that under continuous-wave laser excitation, indicating that the long pulse width (6 ms, 10 Hz) provides a steady-state upconversion process for Ho 3+ . Decreasing the excitation pulse width from 6 ms to 50 µs decreases the R/G from 0.6 to 0.19, which could be explained by the different population processes of the excited states leading to 539 and 658 nm emission. When KZnF 3 :15%Mn 2+ ,1%Yb 3+ , 1%Ho 3+ is excited by a laser pulse width from 500 µs to 50 µs, the R/G ratio is nearly unchanged and the UC emission spectra are still dominated by red UC emission. R/G increases to 13.8 with increasing the pulse width from 500 µs to 6 ms owing to the different cross relaxation rates between Yb 3+ and Ho 3+ and the Mn 2+ -Ho 3+ energy transfer. The red emission level could be further populated by the 5 I 7 state with long excitation duration owing to the long lifetime of the 5 I 7 intermediate state (4 ms). Increasing pulse width allows for a greater possibility of cross relaxation between Yb 3+ and Ho 3+ , providing an additional population path for red UC emission. Generally, there are energy levels below ≈10,000 cm -1 for Tm 3+ , Ho 3+ and Er 3+ ions. Therefore, there is inevitably NIR emission when pumping with a 980 nm laser in these Yb 3+ -Ln 3+ -Mn 2+ systems. The green UC emission at ≈533 nm and the NIR emission at ≈1500 nm of Er 3+ could be selectively enhanced by codoping Mn 2+ in MgGa 2 O 4 :Yb 3+ ,Er 3+ owing to the sensitisation of the Yb 3+ -Mn 2+ dimer. [70] Liu et al. [69] synthesised the core-shell NaGdF 4 :Yb/Tm@ NaGdF 4 :Mn nanostructure, which produced the 535 nm emission of Mn 2+ , as observed in Figure 20.   Reproduced with permission. [54] Copyright 2014, Macmillan Publishers Limited.
that replacement of Gd 3+ with Mn 2+ requires less energy than the substitution of Na + by Mn 2+ ions. Moreover, introducing Fvacancies in the model of Mn 2+ -substituted Gd 3+ decreases the formation energy, which is consistent with the EXAFS results. Owing to the strong tendency for Mn 2+ ions to undergo oxidation, the core-shell structure can be used as a sensing probe for H 2 O 2 molecules, as shown in Figure 20c,d.
The intensity of Mn 2+ UC emission decreases gradually with increasing H 2 O 2 content, while that of Tm 3+ varies little. The oxidizable nature of Mn 2+ in the Mn 2+ -doped UC nanocrystals may make it to be a promising luminescent probe for realtime monitoring H 2 O 2 generation in a variety of biological processes. [69] The green and red UC emissions of Er 3+ in β-NaYF 4 :Yb 3+ ,Er 3+ nanocrystals can be enhanced by codoping with Fe 3+ . [71] Doping with Fe 3+ ions does not result in apparent impurity phases, even at a high doping concentration of 40%, as reported in this work. A possible mechanism for the enhanced UC emissions proposed by the authors is that Fe 3+ dopants lower the symmetry of the environment around Er 3+ , which increases the probability of an f-f electric dipole transition of Er 3+ . However, the mechanism requires further investigation because Fe 3+ has abundant energy levels, which normally leads to quenching of the visible emission.

Upconversion of Ln 3+ Ions Sensitised by TM Ions
A sensitisation process is normally required to improve the performance of UC materials, [6,8,12,13,[72][73][74][75] and there is room for creativity. Dye molecules with broadband absorption characteristic can efficiently sensitise the UC luminescence of β-NaYF 4 : Er 3+ ,Yb 3+ , [73] which provides upconverted emission from Ln 3+ ions under broadband low-power excitation. Broadband sensitisation is currently a hot topic in the research of UC materials, [74] which is motivated by the fact that UC materials suffer from a high pumping energy density and an arrow Ln 3+ excitation line. TM ions exhibit broadband absorption, which is commonly utilised to sensitise the Stokes luminescence of Ln 3+ . [12] Analogously, TM ions can also be used as broadband sensitisers for UC luminescence. [8,12,13] Piguet et al. [11] reported and discussed the very inefficient UC process in Ln 3+ supramolecular complexes, in which organic molecule ligands cause strong multiphonon relaxation between energy levels in Ln 3+ because of the large phonon energy of approximately 2000 cm -1 of the organic molecules. This would result in shortening of the metastable excited state lifetime of Ln 3+ and make the UC of Ln 3+ via the ESA mechanism too inefficient to be detected under practical excitation intensities, even at cryogenic temperatures. Theoretically, they proposed that the combination of two TM ions as sensitisers with an Ln 3+ activator in polynuclear d-f-d supramolecular complexes would overcome the limitation via the ETU process. The authors experimentally obtained UC emission at 33 K. [11] However, it is rare for TM-Ln 3+ ion codoped systems to exhibit RT UC luminescence because the non-radiative relaxation rate of TM ions is generally large, resulting in depopulation of the intermediate energy level of the TM ions serving as a storage level for subsequent UC processes. It is preferable to design TM ions as sensitisers for www.MaterialsViews.com www.advancedscience.com Adv. Sci. 2016, 3, 1600302   Figure 16. RT UC emission spectra of solutions containing: a) KMnF 3 :Yb/Er (18:2 mol %), b) KMnF 3 :Yb/Ho (18:2 mol %), and c) KMnF 3 :Yb/Tm (18:2 mol %) nanocrystals in cyclohexane (insets: proposed energy transfer mechanisms and corresponding luminescent photos of the colloidal solutions). All spectra were recorded under excitation of a 980 nm CW diode laser at a power density of 10 W cm -2 . Reproduced with permission. [61] the long-lived intermediate excited energy level of Ln 3+ ions in which the UC process occurs. In this manner, the TM-sensitised UC luminescence of Yb 3+ -Er 3+ , which is considered as a high-efficiency UC luminescence system, may be obtained at RT. Experience reveals that the material host with the desired RT UC luminescence should contain proper sites for accommodating the TM and Ln 3+ ions and that the TM ions should not absorb the desired emission of Ln 3+ . [6,10,38] According to this idea, the broadband light management phenomenon in the UC material La 3 Ga 5 GeO 14 :Cr 3+ ,Yb 3+ ,Er 3+ has been observed at RT (see Figure 21a and 21b), [75] which is ascribed to the absorption of Cr 3+ . Energy transfer among Cr 3+ /Yb 3+ /Er 3+ in the Stokes and UC luminescence processes is discussed in detail in this research work. As observed in Figure 21c, UC luminescence of Er 3+ sensitised by Cr 3+ directly with 620 nm pulsed laser light is inefficient because almost no decay signal of Er 3+ is observed without Yb 3+ . As the Yb 3+ content increases, the decay curves prolong, which can be interpreted as energy transfer from Cr 3+ to Er 3+ through Yb 3+ as a "bridge" in the UC process. The decay curves decline with increasing Cr 3+ contents in Figure 21d, suggesting large contents of Cr 3+ interfere with the energy transfer from Cr 3+ to Yb 3+ -Er 3+ . Figure 21e schematically illustrates the energy transfer processes. An obvious increase in the early stage of the decay curves occurs with the increase of the Yb 3+ contents, indicating that the UC mechanism is ETU. Therefore, the designed UC emissions 2 H 11/2 → 4 I 15/2 and 4 S 3/2 → 4 I 15/2 of Er 3+ at approximately 510-560 nm are proposed to occur through the ETU process based on the Cr 3+ -Yb 3+ dimer model with superexchange interactions according to the crystallographic data. The material is also excitable by concentrated broadband noncoherent simulated sunlight, which would largely benefit the application of such materials in solar cells.
Another case of broadband sensitised UC in oxide compounds at RT is La(Ga 0.5 Sc 0.5 )O 3 :Er 3+ ,Ni 2+ ,Nb 5+ , which converts 1100-1350 nm and 1450-1580 nm photons to 980 nm photons for application in crystalline silicon solar cells. [76] The criteria for designing the host are similar to the La 3 Ga 5 GeO 14 :Cr 3+ ,Yb 3+ ,Er 3+ case above, i.e., an La 3+ site to accommodate the UC emission centre Er 3+ , and a Ga/Sc site with proper crystal field strength for the sensitiser Ni 2+ to have long-wavelength absorption band but no absorption band in the UC emission wavelength range. The NIR emission of Er 3+ at ≈980 nm can be obtained by exciting either Er 3+ at 1570 nm or Ni 2+ at 1180 nm, as observed in Figure 22a and 22b. The wavelength-dependent UC sensitivity (similar to the excitation spectrum) in Figure 22c (bottom) reveals the broadband sensitisation characteristics at 1100-1350 nm and 1450-1580 nm, which are ascribed to the absorption of Ni 2+ and Er 3+ , respectively. These absorption bands fit the solar energy flux in Figure 22c (top). This research facilitates the design of novel photonic materials that are excitable by broadband noncoherent light for applications such as solar cells.   [55]

Upconversion of Ln 3+ Ions Tuned by d 0 Ions
The tuning effects of the Ln 3+ -centred UC behaviour by d 0 ions are mostly ascribed to the electric diversity of materials with d 0 ion-centred anion groups (including MoO 6 6and TiO 4 4-, etc.), [77] which is based on the fact that the electric dipole transitions of Ln 3+ ions are mostly affected by the surrounding electric environment comprised of d 0 ion-centred anion groups. For example, the UC emission of Yb 3+ -Er 3+ (the ratio of green to red emission) can be tuned by codoping W 6+ in the ferroelectric material Bi 4 Ti 3 O 12 , [78] as illustrated in Figure 23. Ferroelectric compounds have a large dielectric permittivity, which is strongly correlated to the separation of the positive charge centre Ti 4+ and the negative charge centre of the coordinated polyhedral O 2in the d 0 ion-centred anion group TiO 6 8-. The tuning mechanism may be that a larger polarisation effect would be induced on Er 3+ by W 6+ when substituting Ti 4+ , which might be evidenced by the larger polarisation value (see Figure 23) for the sample with higher W 6+ content. This type of material has potential applications in multifunctional optoelectronic integrated devices.
Direct evidence of the tuning behaviour of Yb 3+ -Er 3+ in BaTiO 3 ferroelectric thin films is achieved via an external electric field according to Hao,[16] as illustrated in Figure 24. The unique crystal structure of this ferroelectric host provides an opportunity to couple the variables, including the electric field, to the crystal symmetry, in addition to varying the chemical composition and/or doping, all of which affect UC behaviour. [16] In the presence of an external electric field under low bias voltage, Ti 4+ and O 2in the lattice move in opposite directions, as shown in Figure 24d, resulting in the lower symmetry of the Er 3+ site (i.e., internal electric field variation according to crystal field theory, which is based on the static point charge model) and enhancement of the Er 3+ UC green emission by a factor of 2.7. The mechanism can be explained by Judd-Ofelt theory for the electric dipole transition of the Er 3+ ion. The green emission of Er 3+ involves a hypersensitive transition, which is dominated by the Judd-Ofelt intensity parameter Ω 2 . Ω 2 is strongly associated with the asymmetry of the Ln 3+ sites. Lower symmetry normally contributes to a larger Ω 2 , resulting in selective enhancement of the green emission of the Er 3+ ion. Dynamic modulation of the UC emission of Er 3+ is observed through in situ and real-time periodical variation of the external electric field in Figure 24e, which suggests that the material could be used as electric controlled upconvertors. [16] This research work provides a reversible and in situ approach to tune the UC behaviour, and the coupling of UC luminescence and the electric field opens new opportunities to design multifunctional materials and devices. The temperature-induced internal electric field variation on Er 3+ in Er 3+ -doped perovskite PbTiO 3 nanofibres can also tune the UC of Er 3+ but in a contrasting way. [79] The decrease of tetragonality and spontaneous polarisation of the nanofibres from 50 K to 300 K, revealed by in situ X-ray diffraction, results in enhanced UC emission intensity of Er 3+ for both the green and red emission, which is caused by the recovery of Ti 4+ and  O 2to the equilibrium position for TiO 6 8octahedra with less distortion. [79] Because the dielectric permittivity can reveal polarisation, effort was made to correlate the dielectric permittivity with the UC behaviour of Ln 3+ in the Ti 4+ based ferroelectric oxides. In a filled tetragonal tungsten bronze oxide Sr 4 (La 0.85 Ho 0.025 Yb 0.125 ) 2 Ti 4 Nb 6 O 30 ceramic, the Sr-sites ionic occupation and distribution have a major influence on the local lattice distortion, whereas the dielectric permittivity may be a relatively sensitive probe of the local lattice distorted structure. Thus, it was expected that the UC variation of the Ho 3+ ion was related to the dielectric permittivity in this Sr 4 (La 0.85 Ho 0.025 Yb 0.125 ) 2 Ti 4 Nb 6 O 30 ceramic when Sr 2+ ion was substituted by Ba 2+ ion. [80] The variation tendency of the 5 S 2 → 5 I 8 , 5 F 5 → 5 I 8 and 5 S 2 → 5 I 7 transition intensities of Ho 3+ as a function of the Ba 2+ content in this (Sr 1-x Ba x ) 4 (La 0. 85 Figure 19. a) UC emission spectra of KZnF 3 : 5%Mn 2+ , 1%Yb 3+ , zHo 3+ under 976 nm LD excitation; b) Temperature-dependent UC emission spectra of KZnF 3 : 5%Mn 2+ , 1%Yb 3+ , 0.005%Ho 3+ ; UC emission spectra of the (c) KZnF 3 : 0.5%Yb 3+ ,1%Ho 3+ and (d) KZnF 3 : 15%Mn 2+ ,0.5%Yb 3+ ,1%Ho 3+ under 976 nm LD excitation with different pulse duration; e) Schematic illustration of possible UC processes. Reproduced with permission. [ frequencies of alternating current (AC) impedance spectroscopy, suggesting a correlation between the UC behaviour and the dielectric permittivity. [80] It also suggests that both properties share the same structural origins. Dielectric permittivity is contributed by different types of polarisations (i.e., electronic, ionic, dipolar, and space charge). For the frequency range of 10 kHz-1.0 MHz, dielectric permittivity is mainly contributed by dipolar polarisation in response to an AC electric field. The random stress field caused by substituting Sr 2+ with Ba 2+ affects the octahedral (Ti/ Nb)O 6 and suppresses the Ti/Nb dipolar ion orientation along the AC electric field, resulting in reduced dielectric permittivity. [80] The authors also stated [80] that for x = 0 and x = 1.0, no random stress field existed; thus, high UC intensities were observed owing to the ordered Sr and Ba-site alignment. For partial substitution cases, the random stress field was gradually enhanced with increasing x, and then suppressed when x approached 1.0. The random stress field induced by tilting and rotation of the (Ti/Nb)O 6 octahedra around the Ho 3+ site caused variation in the UC emission intensity.
However, the UC behaviour of Er 3+ (ratio of red emission intensity to green emission intensity) had no direct relation with the dielectric, piezoelectric and ferroelectric properties in (0.97-x)Pb(Mg 1/3 Nb 2/3 )O 3 -xPbTiO 3 -0.03Pb(Er 1/2 Nb 1/2 )O 3 ceramics but was correlated with the phase transition as x increased because there were three phases in the range of 0 < x < 0.40. [81] Additional work [82] showed that not all the electric dipole transitions of Ln 3+ were sensitive to polarisation induced by the distortion of d 0 ion-centred anion groups. The model of (Ba 0.77 Ca 0.23 )TiO 3 : Pr 3+ was chosen to study the correlation because it showed the highest remanent polarisation and electrostrictive strain. As a result, a strong poling effect was expected, according to Zhang et al. [82] The temperature (5-450 K) dependence of Pr 3+ emission in this (Ba 0.77 Ca 0.23 ) 1-x Pr x TiO 3 ceramic was investigated. The blue emission (≈490 nm, 3 P 0 → 3 H 4 ) of Pr 3+ has a strong thermal quenching effect, which disappears as the temperature increases to approximately 200 K, whereas the red emission (≈611 nm, 1 D 2 → 3 H 4 ) is resistant to thermal quenching, even above room temperature, partially because of the phase transition at 80-170 K. The poled sample (with a remanent polarisation of approximately 10 µC cm -2 ) shows 30% higher red emission intensity than that of the unpoled sample, whereas for the poled and unpoled Pr 3+ -doped CaTiO 3 or SrTiO 3 ceramics without ferroelectricity, the red emission intensities change little. Therefore, the ferroelectric polarisation of the ceramics owing to the distortion of the d 0 ion-centred anion group TiO 4 4could tune the red emission of Pr 3+ but has little effect on the blue emission. [82] Another example of the selective influence of d 0 -centred anion groups on the electric dipole transition of Eu 3+ was reported in Yb 3+ -Eu 3+ -doped Sr 2 Ca(Mo,W)O 6 double perovskites. [83][84][85] A remarkable phenomenon, with an emission peak at ≈690 nm concentration, inset is the corresponding UC emission spectra. Reproduced with permission. [69] www.MaterialsViews.com www.advancedscience.com Adv. Sci. 2016, 3, 1600302 upon laser beam stimulation. An analogous phenomenon is also observed in Eu 3+ -doped zeolite-Y for laser stimulation (to be published by our group). This research provides a novel technique to tailor the UC behaviour of Ln 3+ ions through the electric field of a laser beam itself in addition to applying an external electric field, and varying the chemical composition and codopants, which might inspire the design of opto-electric multifunctional devices. [84] The coordination number variation of MoO x groups in La 2 Mo 2 O 9 :Yb 3+ ,Er 3+ , which results in oxide-ion conductivity, also modulates the UC luminescence of Yb 3+ -Er 3+ . [87] La 2 Mo 2 O 9 is an outstanding oxide-ion conductor, with a two orders of magnitude increase in conductivity at ≈580 °C, at which the monoclinic α-La 2 Mo 2 O 9 transforms to cubic β-La 2 Mo 2 O 9 . [88,89] The oxide-ion conductivity of β-La 2 Mo 2 O 9 originates from the structure of α-La 2 Mo 2 O 9 . α-La 2 Mo 2 O 9 has a large unit cell with complex MoO 4 2-, MoO 5 4-, and MoO 6 6polyhedral forms, whereas β-La 2 Mo 2 O 9 has only MoO 6 6octahedra. Therefore, there is a tendency for MoO 4 2and MoO 5 4groups to transform to MoO 6 6groups with increasing temperature below the phase transformation point owing to the motion of the oxide ion, [89] which is evidenced by the temperature-dependent Raman spectra. [87] The motion of the oxide ion influences UC luminescence, see Figure 26. Yb 3+ -Er 3+ ions are used because they are well-studied, and the intensity ratio of the 2 H 11/2 → 4 I 15/2 (≈525 nm) to 4 S 3/2 → 4 I 15/2 (≈550 nm) transitions of the Er 3+ ion is independent of the luminescence loss and fluctuations in the excitation intensity because of the small energy gap between 2 H 11/2 and 4 S 3/2 . That is why the logarithm of the ratio (I 525 /I 550 ) versus 1/T in Figure 26b is linear, which is the basis of optical temperature sensing applications. Both the logarithm of the ratio (I 525 /I 660 ) and the ratio (I 660 /I 550 ) versus 1/T have break points at 150-200 °C. The temperature-dependent decay curves of the 525 and 550 nm UC emission of Er 3+ behave distinctly above 150 °C compared with that of the 660 nm UC emission, as shown in Figure 26c-e. The AC impedance shows oxide-ion long-range motion above 200 °C but does not provide specific information below 200 °C owing to the limits of the instrument. Internal friction spectroscopy illustrates the short-range oxide-ion movement, as shown in Figure 26f. The peak near ≈150 °C is ascribed to the O 2-→ V o short-range  (c) Comparison of the absorbance (1-R d ) and UC sensitivity of the sample with x = 0.5 (lower), the AM1.5G solar spectrum (upper) is also shown for reference. Reproduced with permission. [76] Copyright 2016, AIP Publishing LLC.
swapping and the peak at ≈500 °C is due to the phase transformation. Furthermore, the temperature-dependent Raman spectra also show distinct behaviour below and above 200 °C. There is a correlation between the break points in Figure 26b-d and the friction peak at ≈150 °C in Figure 26f, which indicates that the oxide-ion and oxygen-vacancy swapping has a significant influence on the UC luminescence of Yb 3+ -Er 3+ when the MoO 4 2and MoO 5 4groups transform to MoO 6 6groups and that the UC luminescence could sense oxide-ion motion. This system has potential in detecting the oxide-ion motion of oxideion conductors for applications in solid oxide fuel cells, oxygen sensors and oxygen separation.

Upconversion of d 0 ions
The Stokes luminescence of d 0 ion-centred anion groups has been previously and intensively discussed by Blasse; [46] however, the luminescence mechanism is not fully understood. In addition, the mechanism of the UC emission of d 0 ioncentred anion groups remains unknown. The UC emissions of VO 4 3-, MoO 4 2-, WO 4 2-, TiO x 4-2x and TaO x 5-2x groups were observed in YVO 4 , [90,91] TiO 2 :Mo [92] and silicate glasses with d 0 ion dopants [93][94][95] when pumped by an infrared pulsed laser or continuous-wave laser. One example of TiO x 4-2x emission is shown in Figure 27. The origin of the emission from defects is excluded according to the experimental results. [93] Therefore, there are two primary types of mechanisms for such a UC process. One mechanism involves low-valent TM ions with an intermediate energy level, such as V 4+ /V 3+ and Mo 4+ /Mo 5+ in YVO 4 [90] and TiO 2 :Mo, [92] respectively, as a storage level for the subsequent UC process. The other mechanism involves multiphoton absorption induced by a femtosecond pulsed laser in d 0 -ion-doped glass or crystal, [91,93,94,96] resulting in electron excitation from the 2p orbitals of O 2to the d orbitals of d 0 TM ions and UC emission with the reverse process. This result is deduced from the fact that there is no intermediate energy level available in the absorption spectra, which is requisite for a UC process through an ESA or ETU mechanism. Additionally, the power of the femtosecond pulsed laser is sufficiently high and the pulse is sufficiently fast to generate a nonlinear effect with multiphoton absorption. This type of material may find application in high-density optical storage and three-dimensional colour displays.

Conclusions and Perspectives
In contrast to the well-known multiple and fixed UC emissions of Ln 3+ in Ln 3+ -activated luminescent materials, TM ions with non-filled d orbitals feature single and tuneable broadband UC emission owing to the susceptibility of the d electron energy levels of TM ions to their chemical environment. The UC emissions of Ln 3+ can also be modulated by TM and d 0 ions (anion groups), which is appealing because it benefits from the specific metastable energy levels of Ln 3+ , independent of the ligand field and the tuneable energy levels of TM ions or the electric versatility of d 0 ion-contained hosts. Significant advances have recently been made in fabricating new luminescent materials, developing novel applications and exploring the mechanisms involved.
(1) For most TM ions, their UC emissions are normally quenched at RT owing to the environment-sensitive abundant d energy levels and strong phonon-electron www.MaterialsViews.com www.advancedscience.com Adv. Sci. 2016, 3, 1600302 coupling. Some exceptions, including Mn 2+ and Cr 3+ , are ascribed to the large gap between the first excited state and the ground state (>10,000 cm -1 ). The large gap decreases the possibility of multiphonon relaxation. Meanwhile, a large gap without metastable energy level that matches the excited state 2 F 5/2 of Yb 3+ at ≈10,000 cm -1 for resonant energy transfer requires cooperative sensitisation or GSA/ ESA(ETU) based on a superexchanged coupling model for Yb 3+ -TM ions. The most appealing feature of Mn 2+ /Cr 3+ is the tuneable single-band emission, which is attractive for bioimaging. Furthermore, the susceptibility of the d electrons of TM ions may make them magnetically coupled with each other or Ln 3+ , resulting in new physical processes with multifunctionality, as in the case of Mn 2+ . Since the outstanding magnetism property and excellent luminescence performance are normally contrary and always conflicts, the options of TM ions are limited. For those TM ions with abundant energy levels and small gap between the adjacent levels, the excited TM ions stimulated by NIR light via upconverted process would not result in UC emission but might cause photocatalysis when they locate at proper sites at the surface of the materials like nanocrystals for catalysis application.
(2) For the UC emissions of Ln 3+ modulated by TM ions, the options of TM ions are limited to Mn 2+ and Cr 3+ because of the large gap mentioned above and the lack of energy levels below 10,000 cm -1 to quench the UC of Ln 3+ . They generally enhance the emission of Ln 3+ that with emission levels below the emitting states of Mn 2+ /Cr 3+ owing to energy transfer. The research provides an effective approach to modulate the multiple emissions of Ln 3+ to single-band emission, which greatly increases the signal-to-noise ratio when applied in bioimaging. Also, the introduction of TM ions would facilitate the applications of these systems in the magnetism-related field due to the magnetic coupling of TM-TM ions or TM-Ln 3+ ions. It is highly desirable to utilise the broadband absorption characteristics of TM ions to sensitise Ln 3+ UC emissions for applications in solar cells because it temperatures (all the spectra are normalized for the peaks at ≈612 nm corresponding to forced electric dipole transition of 5 D 0 → 7 F 2 ); Calculated imaginary parts (Im, red stars) and real parts (Re, green balls) of dielectric function for (c) SCMO and (d) SCWO compounds. Reproduced with permission. [84] Copyright 2015, The Royal Society of Chemistry.
would increase the absorption cross section. However, much effort on controlling the spatial distribution of TM and Ln 3+ ions to a certain distance, such as constructing a core-shell structure, is required to prevent mutual quenching to further improve the luminescence efficiency.
(3) For the UC emissions of Ln 3+ modulated by d 0 ions (anion groups), the electric versatility of d 0 -contained hosts has a strong but unspecific influence on some electric dipole transitions of Ln 3+ . This is mostly ascribed to the unknown details of the d 0 -centred anion groups that coordinate Ln 3+ . There is little research on the UC luminescence of the d 0 -centred anion groups themselves. However, functions in addition to the UC property are indeed introduced in these systems, such as ferroelectricity and oxide-ion conductivity. We could imagine further to couple the UC emission of Ln 3+ ions in piezoelectric compounds, negative thermal expansion compounds and polar compounds to enlarge the UC luminescent material family and promote multifunctional applications.
Overall, the attractive electronic and magnetic behaviour of TM ions and the electric behaviour of d 0 -contained hosts make them beneficial in applications involving multifunctional materials and devices when combined with the UC behaviour of Figure 26. a) Temperature-dependent UC emission spectra of La 2 Mo 2 O 9 :Yb 3+ ,Er 3+ . All the spectra are normalized at ≈550 nm peak; b) the logarithm of peak intensity ratio versus 1/T; Temperature-dependent UC luminescence decay curves of La 2 Mo 2 O 9 :Yb 3+ ,Er 3+ upon excitation of 980 nm pulsed laser monitored at c) λ em = 525 nm, d) λ em = 550 nm, e) λ em = 660 nm; f) the internal friction and modulus versus temperature of the La 2 Mo 2 O 9 :Yb 3+ ,Er 3+ ceramics. Reproduced with permission. [87] Copyright 2016, The Royal Society of Chemistry. Figure 27. Emission spectra for Ti 4+ doped silicate glass when excited by UV light at 4.73 eV and NIR femtosecond pulsed laser at 1.59 eV. The insets are images of Ti 4+ doped silicate glass and Ta doped silicate glass irradiated by 780 nm femtosecond laser. Reproduced with permission. [93] Copyright 2007, American Institute of Physics. Ln 3+ . There remains room for more imaginative and innovative research work, which allows researchers to be creative with the mechanism and application of these materials.