Magnetic Sponge with Neutral–Ionic Phase Transitions

Abstract Phase transitions caused by the charge instability between the neutral and ionic phases of compounds, i.e., N–I phase transitions, provide avenues for switching the intrinsic properties of compounds related to electron/spin correlation and dipole generation as well as charge distribution. However, it is extremely difficult to control the transition temperature (T c) for the N–I phase transition, and only chemical modification based on the original material have been investigated. Here, a design overview of the tuning of N–I phase transition by interstitial guest molecules is presented. This study reports a new chain coordination‐polymer [Ru2(3,4‐Cl2PhCO2)4TCNQ(EtO)2]∙DCE (1‐DCE; 3,4‐Cl2PhCO2 − = 3,4‐dichlorobenzoate; TCNQ(EtO)2 2,5‐diethoxy‐7,7,8,8‐tetracyanoquinodimethane; and DCE = 1,2‐dichloroethane) that exhibits a one‐step N–I transition at 230 K (= T c) with the N‐ and I‐states possessing a simple paramagnetic state and a ferrimagnetically correlated state for the high‐ and low‐temperature phases, respectively. The T c continuously decreases depending on the content of DCE, which eventually disappears with the complete evacuation of DCE, affording solvent‐free compound 1 with the N‐state in the entire temperature range (this behavior is reversible). This is an example of tuning the in situ T c for the N–I phase transition via the control of the interstitial guest molecules.


DOI: 10.1002/advs.201700526
of the intrinsic physical properties of materials. The electronic states of materials and their spin states with superexchange interactions, transient electronic transport, electric polarization, and structural changes are tuned as a function of external stimuli. A representative example involves the phase transition between the neutral (N:D 0 A 0 ) and ionic (I:D + A − ) charge states (i.e., N-I phase transition). This example represents a new research field in organic electron-donor (D)-acceptor (A) systems, [1][2][3][4][5][6][7][8] with the discovery of the first compound tetrathiafulvalene-chloranil in the class of alternating π-stacking DA systems by Torrance et al. [9,10] However, these organic DA systems were of low interest from the viewpoint of spin systems because of the sole production of S = 1/2 antiferromagnetic pairs in the I-state involving the structural distortion (i.e., dimerization). Conversely, a covalently bonded DA system exhibiting the N-I phase transition has been observed for a metal complex chain with the D and A of [Ru 2 (2,3,5,6-F 4 PhCO 2 ) 4 ] and DMDCNQI, respectively, [Ru 2 (2,3,5,6-F 4 PhCO 2 ) 4 DMDCNQI]·2(p-xylene) (0, 2,3,5,6-F 4 PhCO 2 − = 2,3,5,6-tetrafluorobenzoate, DMDCNQI = 2,5-dimethyl-N,N′dicyanoquinonediimine). [11] Ferrimagnetic correlation between the spins of S = 3/2 for [Ru 2 II,III ] + and S = 1/2 for DMDCNQI •− in the I-phase is produced via an electron transfer from the paramagnetic N-phase with S = 1 of [Ru 2 II,II ] without dimerization. Interestingly, this compound exhibited a stepwise transition via an intermediate state composed of N and I chains in a 1:1 ratio (average state of D 0.5+ A 0.5− ), which was caused by the effect of anisotropic interchain Coulomb interactions. This result implied that the electron transfer from D to A (or from A − to D + ) is also possibly sensitive to the environment in which D and A are located, because this could be associated with the Madelung stabilization in the I-phase, and not just sensitive to the balance of intrinsic potentials for D/A, i.e., the ionization potential (I D ) of D and the electron affinity (E A ) of A. Indeed, the transition temperature (T c ) is sensitive to the application of hydrostatic pressure and partial chemical modification in the same system. [11][12][13] These results have motivated the research of chemically switchable N-I phase transitions; as the previous compound represented the only case wherein chains with multiple spin states exhibit the N-I phase transition, new systems have been considered for developing guest-induced magnetic change (i.e., magnetic sponge) phenomena associated with the N-I phase transition.

Selection of D and A Units
The paddlewheel-type diruthenium(II, II) complex, [Ru 2 II,II (3,4-Cl 2 PhCO 2 ) 4 ], and TCNQ(EtO) 2 , were selected as the D and A units for searching a N-I phase transition compound. These DA systems exhibit the following remarkable features: (1) the I D of [Ru 2 ] and E A of the TCNQ or DCNQI derivatives can be easily tuned by modifying the substitution of ligands or molecules without changing the basic assembly form; (2) the spin set in the I-phase is not canceled even for an antiferromagnetically coupled set although it is canceled in the organic DA systems, leading to a ferrimagnetic spin correlation of S = 3/2 for [Ru 2 II,III ] + and S = 1/2 for TCNQ •− through a chain; (3) the D + A − set in the I-state did not permit the dimerization that is frequently observed in π-stacked organic systems, as a Peierls distortion [2,3] because of its robust covalently bonded framework. To predict the balance between the I D of D and E A of A, the (ΔE H-L (DA)) gap between the highest occupied molecular orbital level of D and lowest unoccupied molecular orbital level of A was easily evaluated by density functional theory calculations for each unit. A plot of ΔE H-L (DA) as a function of ΔE 1/2 (DA), wherein ΔE 1/2 (DA) is the potential gap between the redox potentials of D and A, well predicted the oxidation state of these DA and D 2 A assembly compounds ( Figure S1, Supporting Information). The N-and I-states are expected for ΔE H-L (DA) > 0 and ΔE H-L (DA) < 0, respectively. [14,15] Interestingly, the ΔE H-L (DA) value for the present DA set is 0.2291 eV. [16,17] This value is close to ΔE H-L (DA) = 0, i.e., the boundary region between N-and I-states, which is similar to that (0.2003 eV) for the DA set of the previous N-I transition compound 0 ( Figure S1, Supporting Information). [14] Notably, the chain-type compounds of the [Ru 2

Variation in the Structure of 1-DCE According to the N-I Phase Transition
The 1-DCE structure was examined by single crystal X-ray crystallography at several temperatures ranging from 103 to 270 K. First, a change in the lattice system suitable for the international union of crystallography (IUCr) rule was observed with a change in the temperature; [36] however, the Miller indices based on the cell system at 103 K were typically used for conveniently referring the crystallographic directions and planes for all data in the following discussions.
Compound 1-DCE crystallized in the triclinic P-1 space group in the entire temperature range was investigated (Tables S1-S5, Supporting Information), wherein one half of the formula unit, with inversion centers at the midpoint of the RuRu bond and the center of the TCNQ(EtO) 2 and DCE molecule, was determined as an asymmetric unit (Z = 1). Figure 1a depicts the ORTEP drawing of the formula unit of 1-DCE at 103 K with atomic numbering schemes; chlorine atoms at the meta positions of the benzoate moiety exhibited disordered positions. Table S2 (Supporting Information) summarizes the selected bond distances and angles. Although TCNQ(EtO) 2 can serve as a tetradentate ligand with four cyano groups, the moiety in 1-DCE acted as a linear-type bidentate ligand with only two cyano groups in the trans position, affording a DA alternating chain motif with an [(Ru 2 ){TCNQ( EtO) 2 }] repeat similar to 0, [11] and an ionic DA chain compound with bis(1,2,5-thiadiazolo)tetracyanoquinodimethane (BTDA-TCNQ). [37] The chains run along the <110> direction, affording a chain-aggregated layer on the (001) plane (hereafter known as a chain layer; see Figure 1b-d). Within the chain layer, chains were closely packed in an antiphase manner (i.e., ⋅⋅⋅D⋅⋅⋅A⋅⋅⋅D⋅⋅⋅A⋅⋅⋅) along the <1−10> direction, with the interchain π-stack stabilization related to each of the TCNQ molecules sandwiched from the top and bottom by the phenyl ring of the benzoate moieties in the neighboring chains (red circles in Figure 1), leading to a relatively short interchain [Ru 2 ]⋅⋅⋅TCNQ (centroid to centroid) distance of 7.39 Å at 103 K (the <1−10> direction, Table S5, Supporting Information). One DCE molecule was present as an interstitial crystallization solvent between the chain layers, occupying an isolated pore with a solvent-accessible volume of 118 Å 3 (9%) at 103 K ( Figure 1d shows the Connolly surfaces). Thus, the chains along the <001> direction (i.e., between chain layers) are significantly separated with 12.10 Å at 103 K (Table S5, Supporting Information), although π-π stacks are formed between benzoate groups because of the in-phase alignment (i.e., ⋅⋅⋅D⋅⋅⋅D⋅⋅⋅D⋅⋅⋅ or ⋅⋅⋅A⋅⋅⋅A⋅⋅⋅A⋅⋅⋅) along the <001> direction (blue circles in Figure 1).
The RuO eq length (O eq = equatorial oxygen atoms) was extremely sensitive to the oxidation state of the [ ] + . [38] Figure 2a plots the average RuO eq bond length ( ] + . In addition, the axial bond length (RuN ax ), which was also sensitive to the oxidation state of the [Ru 2 ] unit, [11] suddenly became shorter on cooling at temperatures less than 237 K (Table S3 (Supporting Information) and inset of Figure 2a). In addition, the RuRu bond length exhibited a small anomaly around 230 K (Table S3 (Supporting Information) and inset of Figure 2a). [11] The bond lengths in the TCNQ(EtO) 2 moieties reflected the oxidation state (ρ) of the TCNQ(EtO) 2 moieties (Table S4, Supporting Information), which can be typically evaluated using the Kistenmacher relationship: [39] where b, c, and d are the CC bond distances between 7,9-, 1,7-, and 1,2-positions in the TCNQ(EtO) 2 moiety, respectively, and the parameters A = −41.667 and B = 19.833 are determined by assuming a completely neutral form of TCNQ 0 (ρ = 0) [40] and a one-electron-reduced form Rb + TCNQ •− (ρ = −1). [41] Figure 2b plots the estimated ρ values at respective temperatures for 1-DCE, indicating that the TCNQ(EtO) 2 moiety exhibits a quinonoid structure (N-form) at room temperature, whereas it changes into a quasibenzenoid form (I-form) on cooling at 230 K. Thus, the variation in the charge of TCNQ(EtO) 2 moiety is completely consistent with that observed for the [Ru 2 ] unit, confirming the occurrence of the one-step N-I phase transition at 230 K.

Temperature-Dependent Infrared Spectra of 1-DCE
The N-I phase transition in 1-DCE was additionally confirmed by infrared absorption spectroscopy. Characteristic CN stretching modes (ν CN ) of TCNQ(EtO) 2 were observed at frequencies ranging from 2100 to 2250 cm −1 (Figure 3a  process). At temperatures 300-230 K, ν CN was observed as a single band at 2216 cm −1 corresponding to the N-state of TCNQ(EtO) 2 (e.g., 2221 cm −1 for free TCNQ(EtO) 2 ). However, at temperatures less than 225 K, two new bands were observed at 2188 and 2161 cm −1 , corresponding to the characteristic ν CN for the I-state of TCNQ(EtO) 2 •− (e.g., 2199 and 2172 cm −1 for the anion radical salt Li + TCNQ(EtO) 2 •− ). The variation in the temperature of the normalized peak intensities for the respective peaks exhibited an inflection point at 220-225 K (Figure 3b). This temperature variation is in good agreement with that observed for structures. A similar trend was observed for the CC stretching mode (ν CC ) ( Figure S2, Supporting Information).

Effect of the N-I Phase Transition on the Magnetic Properties of 1-DCE
The most notable feature of 1-DCE is that a ferrimagnetic 1D correlation can be observed between the I-phase of ] species with S = 1. [16,17,[42][43][44][45] With decreasing temperature, the χT product monotonically decreased because of the effect of the anisotropic nature of [Ru 2 II,II ]; [16,17,[42][43][44][45] however, it suddenly increased from 1.22 cm 3 K mol −1 at 250 K to 1.87 cm 3 K mol −1 at 200 K, and gradually to 6.01 cm 3 K mol −1 at 18 K, followed by an abrupt decrease to 0.52 cm 3 K mol −1 at 1.8 K (Figure 4a). In addition, this sudden shift of χT can be observed in the χ-T plot (see inset of Figure 4a), indicating the occurrence of the N-I phase transition with a magnetic change from isolated paramagnetic spins to ferrimagnetically correlated spins. By taking d(χT)/dT (peak top), T c was determined to be 230 K (Figure 4a). The χ and χT data were simulated at temperatures ranging from 110 to 190 K using an alternating chain model with S i = 3/2 and S i+1 = 1/2 in the [46] and an adequate parameter set was obtained as g  the magnitude of J was in good agreement with that reported previously for chain compounds. [11,47] The strong antiferromagnetic coupling can be caused by a considerable overlap between the frontier π* singly occupied molecular orbital (SOMO) of [Ru 2 II,III ] + and the π* SOMO of TCNQ(EtO) 2 •− . The 1D correlated spins eventually led to antiferromagnetic longrange ordering at T N = 9.6 K related to the presence of the interchain antiferromagnetic interactions (vide infra), similar to the ionic D + A − chain, [Ru 2 (4-Cl-2-MeOPhCO 2 ) 4 (BTDA-TCNQ)]·n(solv). [47] This result was confirmed by the AC susceptibility data ( Figure S3a, Supporting Information); an H-T phase diagram (Figure 4b) was constructed using the data obtained from the field-cooled magnetization (FCM) measured at several DC fields ( Figure S3b, Supporting Information) and the field dependence of the magnetization measured at several temperatures ( Figure S3c, Supporting Information). Using the mean-field approximation with an effective spin S eff = S [Ru2] −S Rad = 1, the interchain interaction was found to be zJ′/k B = −0.27 K based on the equation 2|zJ′|S eff 2 ≈ gS eff μ B H ex , with a spin-flipping field H ex = 0.40 T at 1.8 K and g = 2 ( Figure S3c, Supporting Information) [48] although zJ′ was only useful for comparison.

Characterization of Desolvated Compound 1
Compound 1-DCE was relatively stable even at room temperature compared with the first N-I transition compound; [11] however, it gradually released the interstitial DCE molecules with increasing temperature under N 2 , thereby affording DCE-free compound (1). Compound 1 was considerably stable at high temperatures up to 450 K and simultaneously maintained its crystallinity as evidenced by thermogravimetric analysis (TGA) ( Figure S4, Supporting Information). In addition, 1 could be prepared by evacuation at room temperature. Time-course measurements for room temperature powder X-ray diffraction patterns (PXRDs) under vacuum demonstrated that the structure undergoes a gradual, continuous modification over several days (Figure 5). Most of the diffraction peaks for 1 were almost identical with those in 1-DCE, whereas some new peaks were observed for 1, leading to twice the cell volume (see below). The structure of 1 was considered to be a superstructure of 1-DCE. Adv   Although the unit cell contained two crystallographically unique DA pairs (distinguished hereafter as αand β-pairs), 1 also crystallized in the triclinic P-1 space group (Tables S1-S5, Supporting Information), wherein the inversion centers were located at the midpoint of the RuRu bond and center of the TCNQ(EtO) 2 moiety in the respective DA pairs (Z = 2, Figure 6a). [49] Hence, two crystallographically unique chains, αand β-chains, exist in a crystal. Both the chains ran along the <01−1> direction to form a chain layer on the (011) plane (Figure 6b,c). Within the chain layer, the αand β-chains were alternately arranged in an antiphase manner (i.e., ⋅⋅⋅D α ⋅⋅⋅A β ⋅⋅⋅D α ⋅⋅⋅A β ⋅⋅⋅ or ⋅⋅⋅A α ⋅⋅⋅D β ⋅⋅⋅A α ⋅⋅⋅D β ⋅⋅⋅) along the <100> direction with an interchain π-stack as observed for 1-DCE (red circles in Figure 6b), leading to a shorter [Ru 2 ]⋅⋅⋅TCNQ distance of 6.82 Å at 103 K (centroid to centroid) compared with that in 1-DCE. 1D void space channels with a solvent-accessible volume of 159 Å 3 (6.4%) at 103 K were retained between the chain layers after the release of the DCE molecules from 1-DCE, which ran along the <100> direction, i.e., perpendicular to the chain-running direction ( Figure 6c shows the Connolly surfaces). Thus, the interchain layers aligned in an in-phase manner along the <011> direction (i.e., ⋅⋅⋅D α ⋅⋅⋅D β ⋅⋅⋅D α ⋅⋅⋅D β ⋅⋅⋅ or ⋅⋅⋅A α ⋅⋅⋅A β ⋅⋅⋅A α ⋅⋅⋅A β ⋅⋅⋅) are significantly separated by 11.71 Å at 103 K (Figure 6c) although the π-stacks are still present between the benzoate groups (blue circles in Figure 6b). Thus, the orientation of DA unit is slightly modified by the desolvation for canceling the vacancy originally made by DCE in 1-DCE. Since the chain layer comprised compact chains, only half of the void space canceled without any significant change in the interchain relationship.
Temperature variation was the most important aspect in the structure of 1. The average RuO eq bond lengths for the αand β-chains in 1 were in the range of [Ru 2 II,II ] in the entire temperature range investigated (103-270 K) (  (Table S4, Supporting Information). Hence, the αand β-chains in 1 are in the N-state at T ≥ 103 K, which is completely different from the observation of the N-I phase transition in 1-DCE. This result was confirmed by the temperature variation of infrared (IR) spectra of 1 ( Figure S5, Supporting Information).

In Situ Magnetic Measurements for the Variation from 1-DCE to 1
A microcrystal sample of 1-DCE in a gelatin capsule was inserted into an MPMS-7X system (Quantum Design Ltd), and in situ  magnetic measurements with stepwise desolvation treatment were conducted. After the measurement of the fresh 1-DCE sample (Figure 4), it was desolvated in situ by evacuation for a designated time at 310 K. After evacuation, the cell was filled with He gas to enhance the thermal conductivity, and the FCM under a field of 1 kOe was recorded from 300 K (Figure 7a). With desolvation, the T c continuously shifted to lower temperatures than the original T c = 230 K (Figure 7b) although the temperature width for the N-I transition slightly increased (obtained from the dχT/dT-T plot; Figure S6, Supporting Information), [50] and the peaks in the χT-T plots certainly decreased. After evacuating for 18 h, the T c was no longer detected from the dχT/dT-T plot because of the absence of peaks ( Figure S6, Supporting Information). The peak in the χ-T plots ( Figure S7a, Supporting Information) depicted that the desolvation gradually progressed after the 18 h evacuation. However, it was almost completed after the evacuation for 96 h ( Figure S7b ] species with S = 1 considering the zero-field splitting (D), the temperature-independent paramagnetism (χ TIP ), and an impurity with S = 3/2(ρ imp ) ( Figure S8, Supporting Information).

Resolvation for 1
Desolvated compound 1 completely reverted to 1-DCE by the resolvation of DCE. With the exposure of 1 to a DCE vapor for 72 h at 298 K in a sealed MPMS cell, the magnetic behavior of the compound (denoted as 1-DCE′) was essentially the same as that of the original 1-DCE (Figure 7c and Figure S9 (Supporting Information)). These results indicated that both 1-DCE and 1 undergo excellent reversibility between a spincorrelated system with the N-I phase transition (1-DCE) and a paramagnetic system (1) by the application of SD treatments; a magnetic switch via SD cycles was demonstrated (inset of Figure 7c).
A DCE vapor adsorption isotherm at 298 K revealed that 1 adsorbs ≈1 mole of DCE ( Figure S10, Supporting Information), which is consistent with the formula of 1-DCE. This reversibility can be confirmed by the structural change; the PXRD pattern of 1 changed to its original pattern for 1-DCE by exposing 1 to DCE vapor for 24 h (Figure 5a).

Tuning the N-I Phase Transition by Applying Pressure
The pressure variation of the N-I phase transitions of 1-DCE was investigated by applying hydrostatic pressure using a piston-cylinder-type cell made of CuBe alloy in a SQUID magnetometer. Figure S11a-c (Supporting Information) shows the temperature dependence of the magnetization under various applied pressures, and Figure S11d (Supporting Information) shows the diagram of pressure versus T. The T c was dependent on the hydrostatic pressure. Even at low pressures of less than 1 kbar, T c sensitively shifted to high temperature and exceeded the upper limit of the measurement temperature range. We also applied pressures up to 10.5 kbar to 1, though, magnetic properties remained unchanged.

Solvation-Modified N-I Transition
The electronic state of simple charge-transfer complexes is approximately represented as follows [51] Adv. Sci. 2018, 5, 1700526   Figure 7. Time-course magnetic variation of 1-DCE. a) χT-T plots measured at 1 kOe. b) Time dependence of the N-I transition temperature defined by the temperature at which a peak appears in the −dχT/dT versus T plots. Error bar indicates the temperature width for the N-I phase transition defined by the half-width of the peak in the −dχT/dT versus T plots. c) Variation in the χT-T plots measured at 1 kOe by the transformation between 1-DCE and 1 by desorption/sorption (SD) cycles. Inset shows the χT value at 18 K for each step.

www.advancedscience.com
where V is the Coulombic attractive force (>0) between the nearest DA pairs, and α is the Madelung constant depending on the crystal structure. The N-and I-phases were expected in the regimes (I D − E A ) > αV and (I D − E A ) < αV, respectively, and the N-I transformation was expected to occur at (I D − E A ) = αV. As I D and E A are the basic intrinsic parameters for D and A, respectively, the (I D − E A ) value could be the same between 1-DCE and 1. In contrast, the Madelung energy αV was extremely sensitive to structural changes, i.e., the orbital overlap between the D and A units; with the increasing overlap, the αV value tended to increase and vice versa. [1] The application of hydrostatic pressures to 1-DCE, which possibly increased the orbital overlap between the D and A units, and the distance between D and A, promoted the shift of the N-I transition boundary to high temperatures ( Figure S11d, Supporting Information). In particular, the orbital overlap in 1 has been proposed to decrease from that in 1-DCE via desolvation. A simple structural comparison between 1-DCE and 1 revealed that the chain form of 1-DCE is considerably more linear than that of 1, indicative of a larger overlap between the π* orbitals of TCNQ(EtO) 2 and the [Ru 2 ] core for 1-DCE. To evaluate this hypothesis, an angular overlap model was considered (Table S3, Supporting Information). The angular part of π components (A π ) that can overlap between [Ru 2 II,II ] π* and TCNQ(EtO) 2 π* was expressed as A π = {1 − (sinδ·sinτ) 2 } 0.5 , where δ represents the RuNC angle and τ represents the dihedral angle between the least-square planes composed of CC(CN) 2 and RuRuNCC (Table S3, Supporting Information). [52] The crystal structure for 1-DCE at 270 K (N-phase) exhibited A π = 1.00, whereas the structure for 1 at 270 K exhibited A π = 0.95 and 0.97 for αand β-chain, respectively (Table S3, Supporting Information). Compound 1 exhibited a less-overlapped form. The structural deformation induced by the desolvation slightly weakened the CT interactions in 1, leading to the suppressed N-I phase transition. As described above, even a subtle structural difference is crucial for the observation of the N-I phase transition in covalently bonded DA chain systems, possibly explaining the inability of applied pressure to induce the N-I phase transition in 1 although 1-DCE is extremely sensitive to pressure ( Figure S11d, Supporting Information).

Conclusion
In this study, 1-DCE is the first example of a one-step N-I phase transition among the two examples of this type of DA chain complexes that exhibit the N-I phase transition. Furthermore, the present case is a new type of N-I phase transition system in which the T c is continuously varying depending on the accommodation degree of crystallization solvents; completely desolvated compound 1 is eventually a simple N-state system. These results suggest that the electronic state of partially desolvated compounds is not simply represented by the summation of the abundance ratios of 1-DCE and 1, although the N-(DA) and I-domains (D + A − ) coexist in the partially desolvated compounds as derived from their PXRD patterns, wherein the intensity of the diffraction peaks for 1 compensates for that for 1-DCE ( Figure 5b). As mentioned above, the N-I phase transition is sensitively affected by the environment in which the D and A units are located because of the Coulomb interactions and structural modifications. Hence, a partial desolvation could induce a DA condition variable at each step of the desolvation process. A key for such continuous regulation is the structural similarity between 1-DCE and 1, although even the marginal structural deformation significantly affects the N-I phase transition behavior. However, the control of the N-I phase transition via an external chemical stimulus first demonstrated in the present system will offer a new methodology for the design of switchable materials.

Experimental Section
General Procedures and Materials: All synthetic procedures were performed under inert atmosphere using standard Schlenk-line techniques and a commercial glove box. All chemicals purchased from commercial sources were of reagent-grade quality. Solvents were distilled under N 2 using common drying agents. [Ru 2 (3,4-Cl 2 PhCO 2 ) 4 (THF) 2 ] as precursors for 1-DCE were synthesized according to previously reported methods. [16] Preparation of 1-DCE: First, a solution of TCNQ(EtO) 2 (23.4 mg, 0.08 mmol) in CH 2 Cl 2 (40 mL) was separated into 20 portions and added into glass tubes with a narrow diameter of φ8 mm (bottom layer). Second, a mixed solvent of CH 2 Cl 2 /C 2 H 4 Cl 2 in a volume ratio of 1:1 (1 mL) was added on the bottom layer for decreasing the diffusion rate (middle layer). Finally, [Ru 2 (3,4-Cl 2 PhCO 2 ) 4 (THF) 2 ] (88.5 mg, 0.08 mmol) in C 2 H 4 Cl 2 (40 mL) was carefully added on the middle layer of each tube (top layer). The glass tubes were left undisturbed for one month to obtain block-type brown crystals of 1-DCE (24% yield). IR (Nujol): ν = 2216 (s; ν(CN)), 2188 (s; ν(CN)), 2161 cm −1 (s; ν(CN)); Anal. calcd. for C 46  Physical Measurements: IR spectra were obtained on a Jasco FT-IR 620 spectrometer using Nujol mulls sandwiched between CaF 2 plates. TGA was performed on a Shimadzu DTG-60H apparatus under N 2 at temperatures ranging from 298 to 673 K at a heating rate of 5 K min −1 . PXRD patterns were obtained using an Ultima IV diffractometer with Cu Kα radiation (λ = 1.5418 Å) at room temperature.
X-Ray Crystallographic Analyses of 1-DCE and 1: Crystal data for 1-DCE and 1 were recorded at 103-270 K (heating process) on a chargecoupled device (CCD) diffractometer (Rigaku Saturn 724) with multilayer mirror monochromated Mo Kα radiation (λ = 0.71075 Å). A single crystal was mounted on a thin Kapton film using Nujol and cooled under N 2 . The structures were solved using direct methods (SHELXT Version 2014/5), [53] which were expanded using Fourier techniques. All calculations were performed using the Crystal Structure crystallographic software package, [54] except for refinement, which was performed using SHELXL Version 2014/7. [55] CCDC 1565753 and 1565754 contain the supplementary crystallographic data for 1-DCE at 103 K and for 1 at 103 K, respectively. These data can be obtained free of charge from The Cambridge Crystallographic Data Centre (CCDC) via www.ccdc. cam.ac.uk/data_request/cif. Please contact the corresponding author if the structural information under the temperatures other than 103 K as crystallographic information file (CIF) format is required. Structural diagrams were prepared using the VESTA software. [56] The void volumes of crystal structures were estimated by PLATON. [57] Vapor Sorption Measurements: Sorption isotherm measurements for DCE were performed using an automatic volumetric adsorption apparatus (BELSORP-max; BEL Inc.) at 298 K. A known weight www.advancedscience.com (≈50 mg) of the dried sample was placed into the sample cell, and prior to measurements, the sample cell was evacuated again using the degas function of the analyzer for 12 h at 353 K. Finally, the change in the pressure was monitored, and the degree of adsorption was determined by the decrease in the pressure at the equilibrium state.
In Situ Vapor Desorption-Magnetic Measurements: Magnetic susceptibility measurements were conducted on a Quantum Design (SQUID) magnetometer MPMS-XL using a polycrystalline sample at the temperatures ranging from 1.8 to 300 K at 1000 Oe. The data were corrected for the diamagnetic contribution of the sample using Pascal's constants. [58] A known weight (≈25 mg) of the dried sample was placed in a gelatin capsule, and the capsule was held at the center of a plastic straw. The straw was then attached on the edge of a homemade sample rod made of a SUS tube and a brass male thread with a fluorocarbon tape. The sample was isolated from the surrounding atmosphere by overlaying a close-ended brass tube, which can be attached to the thread on the open end of the sample rod using screws. An airtight seal between the thread and brass tube was achieved using a silicon sealant (CAF4, Bluestar Silicones). The SUS tube was connected to a gas handling system with a turbomolecular pump and manometer. The background signals need not be subtracted from the brass tube. The sample was evacuated at 310 K for a designated time (Figure 7a). He was introduced at a pressure of 100 kPa before starting the measurement.
Magnetic Measurements under Applied Pressure: Pressure was applied to polycrystalline samples of 1-DCE in Apiezon-J oil (as the pressure transmitting medium) using a piston-cylinder-type cell made of a Cu-Be alloy. The cell was placed in a SQUID magnetometer, and the N-I phase transitions were examined by monitoring magnetic changes; the actual pressure was estimated from the superconducting transition temperature of Pb.

Supporting Information
Supporting Information is available from the Wiley Online Library or from the author.