Simultaneous Nanothermometry and Deep‐Tissue Imaging

Abstract Bright, stable, and biocompatible fluorescent contrast agents operating in the second biological window (1000–1350 nm) are attractive for imaging of deep‐lying structures (e.g., tumors) within tissues. Ideally, these contrast agents also provide functional insights, such as information on local temperature. Here, water‐dispersible barium phosphate nanoparticles doped with Mn5+ are made by scalable, continuous, and sterile flame aerosol technology and explored as fluorescent contrast agents with temperature‐sensitive peak emission in the NIR‐II (1190 nm). Detailed assessment of their stability, toxicity with three representative cell lines (HeLa, THP‐1, NHDF), and deep‐tissue imaging down to about 3 cm are presented. In addition, their high quantum yield (up to 34%) combined with excellent temperature sensitivity paves the way for concurrent deep‐tissue imaging and nanothermometry, with biologically well‐tolerated nanoparticles.

well-known susceptibility to thermal quenching. While several nanothermometry probes have been proposed for imaging in the first biological window (Cr 3+ , [17] Co 2+ , [18] Mn 3+ /Mn 4+ , [19] Ti 3+ /Ti 4+ , [20] and V 3+ /V 5+ [21] ), only a Ni 2+ -based probe has been reported so far for the second biological window with its superior tissue imaging depth. [22] Most of the aforementioned studies have focused solely on the thermometric performance. Few reports have considered other application-dependent constraints related to particle size, brightness, stability, or biocompatibility. Here, we report on biocompatible Mn 5+ -doped barium phosphate nanoparticles (d < 100 nm) for bifunctional temperaturesensitive deep-tissue imaging. Even though Mn 5+ -doped Ba 3 (PO 4 ) 2 particles have been suggested as fluorescent agents, [23] many parameters crucial to bioimaging (such as particle size, cytocompatibility, or colloidal stability) had not been evaluated.
Mn 5+ -doped barium phosphate nanoparticles were prepared by flame aerosol technology [24] (Figure S1a, Supporting Information) and annealed at 800°C in air for 2 h. To optimize the fluorescence intensity, first the Ba to P molar ratio was systematically varied from 1.45 to 1.75, leading to the formation of Mn-doped Ba 2 P 2 O 7 , Ba 3 (PO 4 ) 2 , and Ba 5 (PO 4 ) 3 OH ( Figure S1b, Supporting Information). Figure 1a shows the X-ray diffraction (XRD) pattern of a powder (Ba/(P+Mn) = 1.55) that consists of 75% Ba 3 (PO 4 ) 2 (triangles) and 25% Ba 5 (PO 4 ) 3 OH (circles). Of these, Ba 5 (PO 4 ) 3 OH could most effectively stabilize Mn in the 5+ valence state, as evidenced by the blue coloration [25] ( Figure  S2a-h, Supporting Information) and stronger absorption (Figure 1c, circles, and Figure S2i, Supporting Information) of the powder, in analogy to calcium phosphate, [26] as well as by Raman spectroscopy ( Figure S3, Supporting Information). This was further supported by elemental analysis, where the Mn content (all valence states) was comparable (± 6% relative deviation) for all hosts ( Figure S2j, Supporting Information). While absorption was lower for Ba 3 (PO 4 ) 2 , the fluorescence intensity was highest. The maximum intensity was observed at a nonstoichiometric ratio of 1.55 with the formula Ba 3 (P 0.99 Mn 0.01 O 4 ) 1.935 (Figure 1c, triangles), which from now on is labeled as BaPOMn.
The excitation and emission spectra of BaPOMn ( Figure 1b) are characterized by a broad excitation peak in the NIR-I (blueshaded area) and sharp emission line at 1190 nm in the NIR-II (red-shaded area), making them most attractive for deeptissue imaging. These spectral properties are characteristic for Mn 5+ in a strong crystal field, which was calculated [27] as Dq/B = 3.22, in agreement with Laha et al. [28] Following the matrix optimization, the Mn doping concentration was optimized and its fluorescence (Figure 1d, triangles) peaked at 1 mol% in agreement with literature, [23,29] while the absorption intensity increased linearly with Mn content (Figure 1d, circles). The actual Mn contents determined by inductively coupled plasma-optical emission spectrometry (ICP-OES) were in excellent agreement with the nominal ones (R 2 = 0.99, Figure S4a, Supporting Information). The optimization of Mn content resulted in remarkably high quantum yields (QYs, determined by an absolute method using an integrating sphere [30] ) reaching up to 34.4% for the lowest doping concentration (0.1 mol%) and 22% for the brightest probe (1 mol%) ( Figure S4b, Supporting Information). Furthermore, larger, rather aggregated BaPOMn particles (d BET = 310 nm, d XRD = 126 nm) obtained by annealing at higher temperatures (1000°C for 2 h in air) increased the QY (26.8%), most likely due to the reduction of surface defects by annealing. [31] The  [41] with SBR of 5.
QY of dispersions of BaPOMn (1 mol%, annealed at 800°C in air for 2 h) was 5.4 ± 1.6% in water and 7.1 ± 1.3 in phosphatebuffered saline (PBS). These QYs are among the highest reported in this spectral region, e.g., single-walled carbon nanotube (0.1-1%), [32] Ag 2 S QD (15.5%), [33] or ICG (13.2%, main peak in NIR-I). [34] It is worth pointing out that most of these QY are determined relative to reference dyes (such as IR-26) whose reported QY varies by an order of magnitude. [35] Particle size is important for biomedical imaging affecting biodistribution and tumor targeting efficiency. [36] The mean crystal size (d XRD ) of annealed particles (Figure 1a) was 44 nm, smaller than the primary particle size by N 2 -adsorption (d BET = 69 nm) or by microscopy (d TEM = 64 nm, Figure S5a and elemental mapping in Figure S6, Supporting Information). The deviation is attributed to the formation of sinter necks (e.g., aggregation) during annealing (inset Figure 1a). However, large aggregates can be removed by centrifugation of aqueous dispersions (Figure S5b, Supporting Information), resulting in nanoparticle dispersions with hydrodynamic sizes around 100 nm, which is well in line with sizes desired for tumor-targeting. [37] The nanoparticle colloidal stability after adsorption of human serum albumin was excellent for, at least, 72 h ( Figure S7, Supporting Information) in five biologically relevant media: H 2 O, PBS, Dulbecco's Modified Eagle's Medium (DMEM), physiological saline (0.154 m NaCl), and serum. The nanoparticles' emission characteristics were not affected by adsorbed proteins ( Figure S8, Supporting Information) and they also retained their functionality in a broad pH range ( Figure S9a, Supporting Information). Furthermore, these nanophosphors are not affected by photobleaching which is common for organic dyes [6] and QDs: [38] The fluorescence intensity of nanophosphors remained unaltered for, at least, 1 h under continuous laser excitation. In contrast, commercially available PbS-CdS QD and ICG reduced their emission intensity by 50% and 100%, respectively, within the first 10 min already ( Figure  S9b, Supporting Information).
The cytocompatibility of these Mn-doped barium phosphate particles was assessed with three cell lines, namely, the widely used carcinoma HeLa cell line, human monocytes (THP-1), and normal human dermal fibroblasts (NHDF). Higher concentrations were not measured due to the limited feasibility of these assays at ultra-high concentrations, [39] even though no interferences could be detected up to 1000 µg mL −1 .
To assess the influence of potential release of Ba 2+ ions on cell viability, water soluble BaCl 2 was also tested (red columns) under the same conditions. The viability of HeLa and THP-1 monocytes is hardly affected by Ba 2+ and only decreases for concentrations >250 µg mL −1 , whereas the NHDF cell viability shows a strong reduction at 500-1000 µg mL −1 . The LD50 of BaCl 2 for NHDF is 551 ± 21 µg mL −1 , similar to those for L929 fibroblasts (440 µg mL −1 ). [40] These results were in agreement with the release of lactate dehydrogenase by these cells (Figure S11, Supporting Information). Furthermore, the particles were also well tolerated by cells during longer exposures (e.g., 48 h, Figure S12, Supporting Information), showing no significant difference to the results after 24 h incubation. Given the high cell viability even after prolonged particle exposure, a major activation of the apoptosis pathways is not expected. This was confirmed by an apoptosis detection assay ( Figure S13, Supporting Information).
The fraction of leached barium from barium phosphate nanoparticles (500 µg mL −1 ) after 1 day in H 2 O, PBS, DMEM, and physiological saline was quantified by ICP-OES ( Figure S14,  Figure 3. Nanothermometry of annealed BaPOMn: a) temperature-dependent fluorescence spectra between 10 and 70°C. Three parameters can be used for thermal sensing: b) the total integrated intensity, c) the ratio between the two peaks P 2 /P 1 , and d) the peak position. e) Temperature measurements through tissue of different thickness. f) Repeatability over 10 cycles between 25 and 45°C.
Supporting Information), and reached 2% (relative to total dose) in cell culture medium. Thus, very high nanoparticle concentrations (≈25 mg mL −1 ) would be required to induce a 50% cell viability reduction only due to Ba 2+ ions.
To assess the potential for in vivo deep-tissue imaging, BaPOMn nanoparticles with relatively high emitter concentration (c = 1 g L −1 ), common for intratumoral administration, [42] were filled into small capillaries (diameter = 2 mm, length = 4-6 cm) and covered by layers of turkey muscle tissue. For comparison, the same experiment was conducted with commercially available organic dye ICG (c = 0.01 g L −1 , concentration with brightest emission [43] ). The fluorescent agents were illuminated under harmless laser intensities ( = 808 nm, 0.19 W cm −2 ) and the emitted signal was filtered with a 850 nm longpass and collected with a near-infrared (NIR) camera, where the exposure time was adapted to reach a signal close to saturation (1-50 ms). The performance to resolve deeper lying structures was quantified by the full-width at half-maximum (FWHM) of the capillary (Figure 2d and Figure S15b, Supporting Information). For BaPOMn, the FWHM was increased from 1.7 to 8.3 mm when covered with 12 mm thick tissue. In contrast, the FWHM of ICG reached 36 mm at the same thickness. This can be attributed to stronger scattering in the NIR-I, showing the benefit of operating in the NIR-II. Similarly, the signal intensity as a function of tissue thickness was quantified in Figure 2e by the signal-tobackground ratio (SBR). The ICG (triangles) can be detected up to a tissue thickness of 12 mm. With thicker tissues, its SBR drops below 5 (dashed line), which is the minimum required to distinguish image features with 100% certainty according to Rose criterion. [41] In contrast, nanoparticles can be detected up to 28 mm while maintaining an SBR above 5, in line with previous theoretical [44] and experimental reports. [45] This can be explained by the reduced absorption in the NIR-II and their higher brightness. However, as the emission intensity scales linearly with particle concentration ( Figure S16, Supporting Information), this imaging performance decreases for lower local concentrations.
The generated signal, however, carries more information than just intensity! Transition metal ions are very sensitive to the surrounding temperature. [46] Therefore, we investigated here, for the first time to our knowledge, the use of Mn 5+ for nanothermometry. Figure 3a shows the spectrum of aqueous nanoparticle dispersion from 10 to 70°C, while powder spectra from 25 to 200°C are shown in Figure S17a in the Supporting Information. Several features of the spectra change with temperature and can therefore be used for thermal read-out.
The total integrated intensity (Figure 3b) decreases by thermal quenching, [47] which can be fitted linearly from 20 to 70°C. While this approach is the simplest in terms of experimental implementation, it is only feasible in very stable conditions. Since it lacks reference, any change in local particle concentration or tissue absorption can distort the temperature readout.
As a second readout, the ratio between the main emission line (P 1 , 1160-1230 nm) and the vibronic sideband [47] (P 2 , 1230-1300 nm) was used. Since the sideband is hardly affected by thermal quenching (Figure S17b, Supporting Information), www.advancedsciencenews.com www.advancedscience.com the ratio P 2 /P 1 increases linearly with temperature ( Figure 3c). While such ratiometric temperature sensing is independent of particle concentration, [14] it still requires the absorption spectrum of the surroundings to be relatively constant to operate at varying depths.
Third and finally, also the peak position of the main emission line ( peak ) red-shifts with increasing temperature, from 1191.1 to 1192.5 nm between 10 and 70°C (0.022 nm°C −1 , Figure 3d). The peak position does not depend on local particle concentrations and is not influenced by the absorption of the surroundings, therefore making it a very robust anchor for deep-tissue thermal sensing.
The response to temperature changes has been linearly fitted with excellent R 2 = 0.999 for all of them and was quantified in terms of relative thermal sensitivity, which were 0.26, 0.43, and 0.33%°C −1 for the three approaches. While these values are not among the highest reported (Table S1, Supporting Information), they arise from a simple singly doped material, our BaPOMn. Similarly, also the thermometric performance of Ba 5 (P 0.99 Mn 0.01 O 4 ) 3 OH particles (having Ba/(P+Mn) = 1.75) was investigated, resulting in even higher sensitivities up to 0.83%°C −1 ( Figure S18, Supporting Information). However, due to the higher emission intensity of BaPOMn (Figure 1c, Ba/(P+Mn) = 1.55), we focused on the latter. Furthermore, the repeatability over 10 cycles was excellent (Figure 3f), and the temperature uncertainty (or resolution) was below 1°C (Figure S17c, Supporting Information).
Finally, the ability to measure the temperature through biological tissues was investigated by placing tissues of different thickness (0-4 mm) around a thermally controlled cuvette filled with an aqueous nanoparticle suspension ( Figure S17d, Supporting Information). The temperature of the cuvette was varied from 20 to 60°C and the peak position was used to determine the temperature (Figure 3e). The temperatures determined by the nanoparticles are in excellent agreement with the nominal ones. While the standard deviation increases with tissue thickness due to lower signal intensity caused by tissue absorption, the thermal imaging depth limit of 4 mm is on par with Ag/Ag 2 S [48] or BiVO 4 :Nd, [14] and above Y 2 O 3 :Nd [49] or SrF 2 :Nd,Gd [50] and perfectly feasible for intravital microscopy applications in small animals.
In conclusion, Mn 5+ -doped barium phosphate nanoparticles with sizes below 100 nm can serve as cytocompatible fluorescent contrast agents in the NIR-II for deep-tissue imaging down to 2.8 cm. These nanoparticles made by scalable and sterile flame spray pyrolysis exhibit ultra-bright and stable emission in the NIR-II window with high temperature sensitivity as shown with animal tissue of increasing thickness.

Supporting Information
Supporting Information is available from the Wiley Online Library or from the author.