Foldable Perovskite Solar Cells Using Carbon Nanotube‐Embedded Ultrathin Polyimide Conductor

Abstract Recently, foldable electronics technology has become the focus of both academic and industrial research. The foldable device technology is distinct from flexible technology, as foldable devices have to withstand severe mechanical stresses such as those caused by an extremely small bending radius of 0.5 mm. To realize foldable devices, transparent conductors must exhibit outstanding mechanical resilience, for which they must be micrometer‐thin, and the conducting material must be embedded into a substrate. Here, single‐walled carbon nanotubes (CNTs)–polyimide (PI) composite film with a thickness of 7 µm is synthesized and used as a foldable transparent conductor in perovskite solar cells (PSCs). During the high‐temperature curing of the CNTs‐embedded PI conductor, the CNTs are stably and strongly p‐doped using MoOx, resulting in enhanced conductivity and hole transportability. The ultrathin foldable transparent conductor exhibits a sheet resistance of 82 Ω sq.−1 and transmittance of 80% at 700 nm, with a maximum‐power‐point‐tracking‐output of 15.2% when made into a foldable solar cell. The foldable solar cells can withstand more than 10 000 folding cycles with a folding radius of 0.5 mm. Such mechanically resilient PSCs are unprecedented; further, they exhibit the best performance among the carbon‐nanotube‐transparent‐electrode‐based flexible solar cells.


DOI: 10.1002/advs.202004092
In recent years, the growing demand for deformable electronics has spurred extensive research in this field. [1][2][3] Consequently, the research community has witnessed numerous publications on smart clothing, [4][5][6] and artificial optoelectrical skins. [7][8][9] This is now a mature field, with foldable cell phones having already been spun out into the commercial market. [10] Energy devices, such as photovoltaic devices are following suit in the form of hair-wrapping-flexible organic solar cells [11] and perovskite solar cells (PSCs) that can be crumpled. [12,13] In deformable electronics technology, transparent conductors and substrates play the most crucial role, governing the entire mechanical flexibility of the device. This is because while thin-film electronics demonstrate enough flexibility, conventional metal oxide transparent conductors such as indium tin oxide (ITO) and rigid glass substrates limit device flexibility. Much effort has been devoted to the replacement of ITO with metal nanowire-based composites, [14,15] polymer-based electrodes, [12] and multi-layered conductors. [16][17][18] Over the last 20 years, carbon nanotubes (CNTs) have generated significant excitement among researchers owing to their applicability in electronics. [19,20] In addition to high conductivity, CNTs demonstrate high transparency with remarkable mechanical resilience. They are thus considered a promising alternative to conventional electrodes, namely, ITO [21][22][23][24][25][26] and metals. [26][27][28] While the applicability of CNTs to flexible devices has been extensively studied, [21,29,30] the application of CNTs in foldable devices has not yet been reported. This is due to the more demanding requirements of the foldable device technology. Because of the severe bending conditions (bending radius of 0.5 mm) of foldable devices, CNTs to be applied in foldable devices require not only high mechanical stability but also a high adhesion strength for the substrates. Similar to hydrophobic carbon electrodes, CNTs also peel off from devices under severe stresses. To avoid such a problem, a CNT-polymer matrix with excellent durability and mechanical robustness has been reported as a conducting substrate. [31,32] However, the application of these systems in foldable devices has not yet been reported, and those used in flexible devices demonstrate mediocre optoelectrical performance.
The performance of carbon electrodes is directly related to chemical doping. The DC-to-optical conductivity ratio of pristine carbon electrodes is not comparable to that of ITO, and a high ratio can be achieved only through chemical doping. While strong acids such as HNO 3 [33] and CF 3 SO 3 H, [34] have been preferred p-dopant, their corrosiveness and instability raise concerns. Furthermore, solution-based chemical doping is unviable for polymer-CNT matrices as contact between the acid and CNTs, which is required for p-doping, is hindered by the polymer encapsulation of CNTs. However, MoO x doping proposed by Bao and coworkers, [35] overcomes the abovementioned problems. MoO 3 is safe to handle and displays excellent doping durability. Nevertheless, to induce a strong doping effect using MoO 3 , the thermal annealing of MoO 3 next to CNTs at a high temperature of approximately 300°C under anaerobic conductions is necessary. In this regard, the CNT-polymer matrix is the perfect candidate, as it can be formed after the direct deposition of MoO 3 on CNTs, and polymers with a high glass transition temperature, (T g ) can be used for the CNT-polymer matrix to utilize MoO 3 as the dopant.
In this study, we prepared a single-walled carbon nanotube (SWNT)-polyimide (PI) matrix in which a strong p-doping can be induced with MoO 3 at a high temperature under anaerobic conditions. The resulting SWNT-embedded PI (SWNT-PI) film displayed an exceptionally smooth morphology and high transparency thanks to the infiltration of the SWNTs into PI, which results in the filling of the network voids. The high T g of PI (300°C) and the effective filling of voids using the SWNTs facilitated effective thermal and anaerobic p-doping using MoO 3 . The sheet resistance (R sheet ) of the SWNT-PI conductor decreased upon doping through the reduction of MoO 3 to MoO x , (x = 2-3). [29] The MoO xdoped SWNT-PI conductor is 7 µm in thickness, which enables not only bending but also the "folding" of the devices without any photovoltaic performance drop or decrease in the DC-to-optical conductivity ratio. The foldable PSCs fabricated using the ultrathin MoO x -doped SWNT-PI film as both the electrode and substrate exhibited a power conversion efficiency (PCE) of 15.2% with an open-circuit voltage (V OC ) of 1.05 V, short-circuit current (J SC ) of 19.0 mA cm −2 , and a fill factor (FF) of 76.6%. The devices withstood more than 10 000 "folding" cycles with a 0.5 mm folding radius, whereas the control PSCs on ITO-coated polyethylene naphthalate (PEN) exhibited severe performance degradation after 1 000 "bending" cycles with 4 mm radius and could not endure even one folding cycle. The extreme folding radius of 0.5 mm presented in this work is by far the most severe condition compared with those reported previously for flexible devices as most of the demonstrated bending radius is 4 mm. To the best of our knowledge, the only electrode that exhibits a comparable folding radius is poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS). The foldable PSC based on the ultrathin MoO xdoped CNT-PI conductor exhibited a record-high PCE among the CNT-based flexible PSCs and the highest flexibility (folding radius: 0.5 mm) and mechanical robustness (10 000 folding cycles) among all the flexible PSCs reported thus far. Figure 1 shows the schematic of the fabrication of the novel SWNT-based ultrathin foldable transparent conductor. First, a thin layer of MoO 3 was thermally deposited on a quartz substrate ( Figure 1a). This is followed by the lamination of an SWNT film (Figure 1b). Immediately after MoO 3 contacts the SWNT film, charge transfer occurs and MoO 3 is partially reduced to MoO 3-. Hereafter, MoO 3-is referred to as MoO x (x = 2 to 3). Next, a PI precursor solution is applied and spin-coated on the SWNT/MoO x /quartz substrate (Figure 1c). [36] The viscous PI solution percolates through the SWNT network, forming an SWNT-PI nanocomposite. The nanocomposite film is then cured and imidized by heat. During this stage, the electron transfer from the SWNT to MoO x (p-doping) intensifies as the curing temperature reaches 300°C and MoO x is completely screened from oxygen. The cured SWNT-PI film adheres to the quartz via van der Waals forces; therefore, it can be easily removed. Thus, when immersed in deionized (DI) water, the SWNT-PI film peels off without damage ( Figure 1d). Subsequently, the film is dried and turned over such that the MoO x side faces upward, yielding ultrathin, transparent, and foldable SWNT-embedded PI electrodes ( Figure S1, Supporting Information). The electrode is denoted as SWNT-PI (without MoO x ) or MoO x /SWNT-PI ( Figure 1e). The morphology of transparent electrodes is crucial for the solar cell performance. [25] Figure 1f-h show the atomic force microscopy (AFM) images of the surface topography of the SWNT-PI conductors with their root mean square (rms) roughness values shown at the bottom of the images. The SWNT-PI films exhibit an extremely low rms roughness of 0.456 nm, indicating extremely smooth surfaces (Figure 1f). The MoO x /SWNT-PI films with a several-nanometer-thick MoO x layer also exhibited a low rms roughness value of 0.446 nm (Figure 1g). Such flat morphologies were achieved owing to the permeation of the PI precursor into the entangled SWNT network and filling of the voids at the quartz interface ( Figure 1c). In the case of the MoO x /SWNT-PI films with greater MoO x thicknesses, they likewise give good morphology with rms values less than 0.5 nm ( Figure S2, Supporting Information). Contrarily, the SWNT films on PEN substrates exhibited a high rms roughness of 7.040 nm because of the exposed entangled SWNTs (Figure 1h and Figure S3, Supporting Information). Such a high roughness results in a low PCE when assembled into PSCs. [21,25] The intrinsically entangled geometry of the SWNT network and the voids render the application of SWNTs as a bottom electrode unbearably challenging. Therefore, our PI embedding technology offers a novel way of producing SWNT-based transparent conductors with a good morphology, thereby preventing electrical current leakage when used in thin-film devices. [37,38] Figure 1i shows the optical transmittance of the SWNT-PI conductors. The transmittance of the PI film and SWNT-PI conductors are ≈80% and 88% in the wavelength range of 450-800 nm, respectively ( Figure S4, Supporting Information). The optical transparency is comparable to those of conventional ITO/PEN substrates, [39] and thus the films qualify for the transparent electrodes and the bottom substrates. The PI conductors exhibited optical interference in the long-wavelength region, which indicates their ultra-thinness (7 µm) ( Figure 1i). [40,41] This is confirmed from the PI film thickness measured via optical microscopy ( Figure S5, Supporting Information).
The p-doping of carbon electrodes is crucial as it increases the DC-to-optical conductivity ratio of the carbon electrodes and tunes the Fermi level, resulting in the performance enhancement of optoelectronic devices. [20] MoO 3 on CNTs induces strong and stable p-doping of the CNTs by reducing to MoO x [29] The creation of oxygen traps through electron extraction from CNTs increases the hole carrier concentration and lowers the Fermi level of the CNTs. [29,42] To maximize the doping effect, the MoO 3 -deposited carbon electrode was annealed at a high temperature of over 300°C under anaerobic conditions. The curing process of the ultrathin SWNT-PI conductor is illustrated in Figure 2a. The high curing temperature of PI (300°C) and the protection of MoO 3 from air during the curing process ensure the successful MoO x doping of SWNTs, which occurs automatically during the production of the SWNT-PI matrix (Figures 1a and 2a). Besides, since PI has an exceptionally high T g , only PI is exclusively compatible with this technology. The doping effect was confirmed via the X-ray photoelectron spectroscopy (XPS) of the films before and after the doping (Figure 2b,c and Figure S6, Supporting Information). Figure [35,42,43] Figure 2c shows the O 1s XPS spectra of SWNT-PI, MoO x /SWNT-PI, and MoO x /SWNT/PEN. The peak at 530 eV corresponds to the oxygen in MoO 3 , whereas the peak between 532 and 533 eV corresponds to the oxygen adsorbed on carbon. The oxygen peak appearing at a higher binding energy for the MoO x /SWNT-PI films indicates the strong doping effect. [35,44,45] The degree of doping can also be determined from the Van Hove transitions corresponding to Vis-IR absorption. [34,[46][47][48] However, the optical interference in the absorption caused by the PI film hinders the visualization of the transitions for the MoO x /SWNT-PI films ( Figure  S7, Supporting Information).
MoO x deposited by thermal evaporation under vacuum promotes film growth through the Volmer-Weber nucleation mechanism. [49] Such growth promotes island formation when the thickness of the deposited MoO x is several nanometers. The R sheet of SWNT-PI decreased with increasing MoO x thickness (Figure 2d), indicating stronger p-doping with increasing MoO x deposition. Further, the decrease in R sheet was not observed when a 10-nm-thick MoO x layer was deposited. This indicates the complete coverage of the CNT surface by MoO x . However, the work function measured by ultraviolet photoelectron spectroscopy (UPS) continuously decreased with an increase in MoO x thickness above 10 nm (Figure 2d and Figure S8, Supporting Information). Thus, determining the optimal MoO x thickness is important with regard to achieving a balance between the R sheet and energy level alignment for PSC performance.
Foldable PSCs employing the ultrathin SWNT-PI conductor were fabricated with a p-i-n inverted configuration: SWNT-PI/ MoO x /poly(triarylamine) (PTAA)/perovskite/C 60 /bathocuproine (BCP)/Cu (Figure 3a). The inverted architecture is suitable for transparent CNT applications because CNTs have a work function of approximately 5 eV (Figure 2d and Figure S8, Supporting Information). [33,50,51] As aforementioned, determining the optimal MoO x thickness is paramount for the PSC performance. Figure (Figure 3c). This is supported by the highest V OC achieved for the PSCs with a 4-nm-thick MoO x layer, which indicates efficient hole collection (Table S1, Supporting Information). Moreover, a high FF was achieved from the low series resistance (R s ), which reveals that excessive MoO x deposition increases the R s despite a decrease in the R sheet of the CNT electrode. The foldable PSCs exhibited a PCE of 15.2% and an average PCE of 14.7% (Table 1 and Figure 3d). The devices did not exhibit hysteresis (Table S2 and Figure S10, Supporting Information). The obtained PCE may not be higher than those of PSCs fabricated on ITO/glass. This is because our devices are not only flexible but also foldable and can endure severe bending conditions. The obtained PCE is the record-high efficiency among those of the reported flexible CNT-based PSCs, and the mechanical stability is the highest among those of all the PSCs that appeared in the literature ( Table 2). The SWNT-PI-based PSCs without a MoO x layer exhibited a PCE of 14.6% and an average PCE of 13.9% (Table 1 and Figure 3d). This uncovers the substantial p-doping and the charge-selective effect induced by MoO x . The enhancement in photovoltaic parameters was statistically analyzed ( Figure S11, Supporting Information). The histogram shows a considerable increase in V OC , which implies improved hole-collection owing to the well-aligned energy levels of SWNTs and PTAA due to MoO x doping ( Figure S11a, Supporting Information). However, the J SC    Figure S13, Supporting Information, and the equivalent circuit is shown in Figure S13c, Supporting Information, which was used for the fitting of R s , charge-transfer resistance (R ct ), and recombination resistance (R rec ) (Table S3, Supporting Information). The R s and R rec are plotted in Figures 3e and 3f, respectively. Under all applied voltages, the R s values of the foldable PSCs with MoO x were on average 70% lower than those of the devices without MoO x (Figure 3e). This is ascribed to the decrease in R sheet by approximately 80% upon MoO x doping (Figure 2d). [39,52] This is further confirmed by the Hall measurement of the SWNT-PI-based conductors, which revealed an increase in carrier concentration, conductivity, and mobility upon MoO x doping (Table S4 and Figure S14, Supporting Information). Meanwhile, R ct was obtained based on a high-frequency response ( Figure S13d, Supporting Information). Lower R ct values indicate good charge transfer, but the R ct values of the MoO x -doped devices were only slightly higher than those of the non-doped devices. We attribute this to the trade-off between the energy level alignment and R sheet . The R rec values of the   [30] 2017 CNT PEN/SWNT/MoO 3 11 4 2,000 90 [20] 2020 Graphene PET/EG-Graphene 12.6 9 1,000 92.2 [56] 2018 Graphene PDMS/Graphene 15 4 1,000 <80 [57] 2018 Graphene PDMS/Graphene 18.2 4 5,000 43 [58] 2018 Graphene PDMS/TFSA-Graphene 17.5 4 5,000 ≈35 [58] 2018 Graphene, CNT Graphene, CSCNTs 11.9 4 2,000 84 [59] 2018 Graphene PET/Graphene 13.94 4 1,000 ≈92 [59] 2017 Graphene PET/APTES/Graphene 17.9 4 100 >90 [59] 2016 Graphene PEN/Graphene/MoO 3 16.8 2 5,000 85 [39] 2019 PEDOT:PSS PEDOT:PSS 19 3 5,000 ≈80 [39] 2019 PEDOT:PSS PEDOT:PSS 17.03 0.5 10,000 100 [12] 2019 PEDOT:PSS PEDOT:PSS 20.25 2 5,000 97 [60] 2015 PEDOT:PSS PEDOT:PSS 10.83 1 1,000 0.9 [61] 2019 AgNW AgNW/PEDOT:PSS 15.06 5 1,000 80 [62] 2017 AgNW a-AZO/AgNW/AZO 11.23 12.5 400 94 [63] 2016 Metal grid Ag grid/PET 14 5 5,000 95.4 [64] 2020 Metal grid PI/Cu grid/Graphene 16.4 5 10,000 97 [65] 2019 Oxide/Metal/Oxide TiO 2 /Ag/TiO 2 13.00 1 1,000 97.6 [18]  MoO x -doped devices were approximately twice those of the nondoped devices under all applied voltages (Figure 3f). A high R rec indicates a small electrical loss originating from non-radiative recombination. This confirms a better energy level alignment between SWNTs and PTAA by MoO x doping, which contributes to the high FF and V OC by increasing the shunt resistance ( Figure  S11a,11c, Supporting Information). The SWNT-embedded PI-based foldable PSCs demonstrated high reproducibility with no hysteresis. This is noteworthy since CNT-laminated flexible PSCs shows a rather low reproducibility and high hysteresis. [20,30,39] For better comparison, we fabricated flexible PSCs using the SWNT-laminated PEN substrates ( Figure  S15a, Supporting Information). The cross-sectional SEM image of the devices shows that the SWNTs on PET forms a rough interface between PTAA and the perovskite layer. Thus, the SWNTlaminated PEN-based devices exhibited a large hysteresis ( Figure  S15b, Supporting Information) and low reproducibility ( Figure  S15c, Supporting Information). This can be explained by considering the case of conventional PSCs. Hysteresis has been reported to occur when the bottom FTO electrode was not fully covered by a compact TiO 2 layer and directly contacted the perovskite layer. [53] Thus, the issues in the utilization of SWNT/PEN might be attributed to its direct contact with some protruded nanotubes and the perovskite layer. This is in stark contrast to the SWNT-PI interface, where the smooth morphology and absence of air traps prevent non-radiative recombination ( Figure S16, Supporting Information). Moreover, unlike the SWNT-laminated PSCs, which required a thick PTAA layer on the SWNTs for surface roughness reduction, the SWNT-embedded PI-based PSCs needed a much thinner PTAA layer, which led to a much lower R s .
To qualify the developed PSCs as foldable devices (Figure 4a), harsh mechanical testing was conducted. Instead of the conventional bending test (bending radius, R bending = 4 mm), we performed a folding test involving a folding radius (R folding ) of 1 mm for the SWNT-PI-based PSCs, SWNT-laminated PEN-based PSCs, and ITO-deposited PEN-based PSCs; the results are shown in Figure 4a. The ITO-deposited PEN-based PSCs exhibited a high PCE of 18.5% owing to the flat ITO surface and high transmittance of the PEN substrate (Table S5 and Figures S17a,b, Supporting Information). However, under a cyclic flex test with a R bending of 4 mm, the PCE decreased continuously and diminished completely after 1 000 cycles (Figure 4b). This is not surprising since ITO develops cracks when bent at a R bending of less than 5 mm. [12,13] Cracks were generated on the ITO layer after bending at R bending = 4 mm, which led to abrupt performance degradation for the ITO/PEN-based PSCs ( Figure S17c, Supporting Information). The SWNT-laminated PEN-based PSCs could not withstand the same mechanical stress ( Figure S18a, Supporting Information). Although the SWNT films easily withstood the bending test with a R bending of 4 mm, the relatively poor adhesion between the SWNT films and PEN, as well as the thick PEN substrate (≈0.125 mm) caused the carbon electrodes to peel off during the cyclic flex test ( Figure S18b, Supporting Information). [32] The SWNT-PI-based PSCs, on the other hand, withstood the bending test with a R bending of 1 mm for more than 10 000 cycles with no drop in the PCE (Figure 4b). Furthermore, the devices endured the cyclic folding test with a R folding of 0.5 mm without PCE reduction (Figure 4c). All the photovoltaic parameters, namely V OC , J SC , and FF, were retained after 10 000 folding cycles (Figure S19, Supporting Information), and no mechanical failure was observed in either the device or the ultrathin conductor, as determined from the cross-sectional FIB-SEM images obtained after the cyclic test ( Figure S20, Supporting Information). We evaluated the mechanical stability of the SWNT-PI conductor-based PSCs via a cyclic crumpling test. During the test, delamination and cracks occurred on the perovskite layer ( Figures S21a,b, Supporting Information), and after 20 crumpling cycles, the electrical resistance of the SWNT-PI conductor increased by approximately 40% ( Figure S21c, Supporting Information). Therefore, it is reasonable to assume that the percolated PI in the SWNT-PI composite affects the SWNT networks. The SWNT network might have disconnected in some areas under the large mechanical stress/strain induced by crumpling. An additional capping layer is necessary to adjust the mechanical neutral plane to impart mechanical stability against crumpling. [12] The foldable PSCs demonstrated a maximum power point tracking output of 15.2% after the folding cycles (Figure 4d). We attribute the excellent mechanical resilience to the embedding of the SWNTs in PI as well as the ultra-thinness of the SWNT-PI film (7 µm). Moreover, the devices were stable for over 25 days, which indicates that the lasting effect of MoO x doping in the SWNT-PI system is durable (Figure 1e).
In conclusion, foldable PSCs were realized using SWNT transparent electrodes for the first time to the best of our knowledge. [17,18] The higher requirements of foldable electronics, which mandates harsh mechanical conditions of 0.5 mm bending (or folding) radius, were met by implementing an ultrathin MoO x -doped SWNT-PI matrix. The ultrathin SWNT-PI transparent conductor exhibited exceptional mechanical resilience, 7-µm-thinness, a smooth morphology, and a high DC-tooptical conductivity ratio. Along with the mechanical robustness of SWNTs, the SWNT-PI conductor demonstrated remarkable adhesion and ultra-thinness, which are ideal for foldable electronic applications. Additionally, the percolation of PI through the SWNT network imparted a smooth surface to the SWNT-PI film and minimized recombination loss in the PSCs. Moreover, stable and strong MoO x doping was achieved by incorporating MoO 3 during the curing process to induce anaerobic thermal pdoping. This, together with the ultra-thinness, resulted in an exceptionally high DC-to-optical conductivity ratio despite the infamous low transmittance of PI. The foldable PSCs showcased a power output of 15.2% with no hysteresis and could withstand over 10 000 folding cycles with a R folding of 0.5 mm. The obtained results are some of the best among those reported thus far for flexible PSCs in terms of both efficiency and mechanical stability.

Experimental Section
SWNT Synthesis: Randomly oriented SWNT networks with high purity and a long bundle length were synthesized via the aerosol chemical vapor deposition (CVD) method. The floating catalyst (aerosol) CVD was conducted in a scaled-up reaction tube (150 mm diameter). The catalyst precursor was vaporized by passing ambient-temperature CO through a cartridge filled with ferrocene powder. For stable SWNT growth, a controlled amount of CO 2 was added with the carbon source (CO). The SWNTs were directly collected downstream of the reactor by filtering through a nitrocellulose or silver membrane filter (Millipore Corp., USA; HAWP, 0.45 µm pore diameter). The flow containing ferrocene vapor was then introduced into the high-temperature zone of a ceramic tube reactor through a water-cooled probe and mixed with additional CO. Ferrocene vapor was thermally decomposed in the gas phase of the aerosol CVD reactor at 880°C. The CO gas was supplied at 4 L min −1 and decomposed on iron nanoparticles, resulting in the growth of SWNTs. The as-synthesized SWNTs were collected via filtering with microporous filters at the downstream of the reactor. The transparency and R sheet were controlled by varying the collection time.
SWNT-PI Ultrathin Conductor Fabrication: The collected square SWNT film (side: 1.2-1.8 cm) was mechanically deposited at the middle of a quartz glass substrate with an area of 2.5 × 2.5 cm 2 via a drytransfer process (to prepare MoO x /SWNT-PI, MoO 3 was deposited on the quartz substrate using thermal vacuum evaporation before transferring the SWNT film). Anhydrous ethanol (100 µL) was dropped on the substrate to densify the entangled SWNT network followed by drying at 70°C for 1 min. The PI film was synthesized using a previously reported method. [36] Equimolar amounts of 2,2-bis[4-(4-aminophenoxy)pheny] hexafluoropropane (TCI) and 4,4′-oxydiphthalic anhydride (TCI) were dissolved in anhydrous dimethylacetamide (DMAc, Sigma Aldrich) with a concentration of 19 wt% and mildly stirred for 12-15 h in a nitrogen-filled glovebox. The viscous light-yellowish precursor solution was spin-coated on the SWNT/quartz substrate at 2 500 rpm (with an acceleration of 500 rpm s −1 ) for 60 s. During spin coating, the precursor solution percolates into SWNTs to form the SWNT-PI composite. The substrate was then dried at 90°C for 5 min and transferred to a box furnace to cure PI. The sample was annealed at 200°C for 20 min and 300°C for 20 min to completely cure the PI film. After cooling to room temperature, the SWNTembedded PI films were immersed in DI water where they peeled off from the quartz and floated in the water.
Device and Film Characterization: The J-V curves of the PSCs were measured using a source meter (Keithley 2400, Tektronix) at a step voltage of 20 mV and delay time of 50 ms. The AM 1.5G one-sun condition was realized using a solar simulator (Solar 3A Class, Oriel) with a KG-5filtered standard silicon cell. During J-V measurements, the devices were covered with a photomask having an aperture area of 0.56 × 0.13 cm 2 . EIS was conducted using an electrochemical potentiostat (PGSTAT100N, Autolab). Cross-sectional SEM images were obtained using a field-emission scanning electron microscope equipped with an FIB (Auriga, Carl Zeiss). Optical transmittance spectra were measured using a UV-vis-NIR spectrophotometer (Cary 5000, Agilent Technologies). Surface topography images were obtained using an atomic force microscope (NX10, Park Systems). Bending tests were performed using a cyclic bending flexibility tester (ScienceTown) with a bending frequency of 1 Hz. The EQEs were measured using a quantum efficiency measurement system (IQE-200B, Newport). XPS and UPS measurements were performed using a K-Alpha Plus spectrometer (Thermo Fisher Scientific) with Al K X-ray radiation (1486.6 eV) and a Theta Probe spectrometer (Thermo Fisher Scientific) with HeI radiation (21.2 eV), respectively.

Supporting Information
Supporting Information is available from the Wiley Online Library or from the author.