Recent Approaches for Cleaving the C─C Bond During Ethanol Electro‐Oxidation Reaction

Abstract Direct ethanol fuel cells (DEFCs) play an indispensable role in the cyclic utilization of carbon resources due to its high volumetric energy density, high efficiency, and environmental benign character. However, owing to the chemically stable carbon‐carbon (C─C) bond of ethanol, its incomplete electrooxidation at the anode severely inhibits the energy and power density output of DEFCs. The efficiency of C─C bond cleaving on the state‐of‐the‐art Pt or Pd catalysts is reported as low as 7.5%. Recently, tremendous efforts are devoted to this field, and some effective strategies are put forward to facilitate the cleavage of the C─C bond. It is the right time to summarize the major breakthroughs in ethanol electrooxidation reaction. In this review, some optimization strategies including constructing core–shell nanostructure with alloying effect, doping other metal atoms in Pt and Pd catalysts, engineering composite catalyst with interface synergism, introducing cascade catalytic sites, and so on, are systematically summarized. In addition, the catalytic mechanism as well as the correlations between the catalyst structure and catalytic efficiency are further discussed. Finally, the prevailing limitations and feasible improvement directions for ethanol electrooxidation are proposed.


Introduction
Fuel cells have risen to prominence as an indispensable and prospective technology, particularly in the realm of heavy-duty vehicles, in stark contrast to conventional thermal engines, renowned for their conversion of thermal energy sourced from fossil fuels into mechanical work. [1,2][5] The energy-conversion approach not only displays exceptional energy DOI: 10.1002/advs.202308958[8] Among various types of fuel cell, direct ethanol fuel cells (DEFCs) have evoked profound interest and attention in the scientific and industrial echelons, prominently featuring an elevated power density, a simple device system, and mild operating conditions. [9,10]Besides, as an environmentally-friendly, renewable, non-toxic, and portable fuel ethanol, its volumetric energy density (6.28 kWh•L -1 ) is much higher than those of methanol (4.05 kWh•L −1 ) and hydrogen gas (0.18 kWh•L −1 , compressed at 20 MPa).The above characteristics make it possible for DEFCs to replace fossil fuel consuming internal combustion engines, especially in application scenarios such as heavy-duty trucks and ocean freighter.
Up to now, platinum (Pt) and palladium (Pd) are still the state-of-the-art anodic electrocatalysts in DEFCs. [11,12]However, pure Pt and Pd catalysts with high cost show the sluggish reaction kinetic for ethanol oxidation reaction (EOR) because of their unfulfilling C─C bond breaking capability and poor *CO intermediate tolerance, which seriously hinder the output of energy and power density for DEFCs. [13,14]Generally, two parallel and competing pathways are recognized for EOR, that are, the complete oxidation pathway (C1 pathway) and incomplete oxidation pathway (C2 pathway).The C2 pathway involves 2/4 electrons transferring without C─C bond breaking, resulting in the acetaldehyde/acetic acid as the final products (Figure 1).Inversely, the preferred C1 pathway involves 12 electrons transferring with C─C bond breaking and producing CO 2 . [15]Due to the high activation energy (87.3 kcal mol −1 ) of C─C bond breaking, the C1 selectivity of Pt and Pd catalysts is very low (<7.5%). [15,16][22][23][24] The enhanced catalytic performance can be mainly attributed to the bifunctional mechanism.On the one hand, oxophilic metals can increase the lattice strain and modulate the electronic structure of Pt and Pd catalysts.On the other hand, the formed OH ads (adsorbed hydroxyl) on the surface of oxophilic metals promote the oxidation of *CO.[24][25] However, due to the leaching and dissolution of oxophilic metals in acid electrolyte, the stability of Pt and Pd catalysts should be further improved.26][27][28][29] This article reviews a series of efficient strategies for breaking C─C bonds during ethanol electro-oxidation reaction, including constructing core-shell nanostructure with alloying effect, doping other metal atoms in Pt and Pd catalysts, engineering composite catalyst with interface synergism and introducing cascade catalytic sites in recent research (Table 1).The ethanol electrooxidation mechanism on the catalysts mentioned is are further discussed.Finally, we undertake a comprehensive elucidation of the prevailing limitations of cleaving C─C bonds in the EOR process and provide some preliminary insights on feasible improvement directions to promote the industrialization development of DEFCs.

Pt-/Pd-Based Alloys
Due to the substantial energy expenditure associated with the cleavage of the C─C bond, the C1 path selectivity in the EOR process remains constrained to a value below 7.5% when employing a solitary noble-metal center, such as platinum (Pt) or palladium (Pd), as an electrocatalyst. [30]Among them, only the Pt-based center has EOR reaction activity under acidic conditions.33] As shown in Figure 2A,B, the Sun group comprehensively elucidated the transformations occurring during ethanol electrooxidation across an in situ spectrum of active sites present on the PtAuRu alloy surface within distinct potential regimes. [34]These insights carry substantial significance in guiding the strategic development of alloy catalysts characterized by enhanced C1 selectivity.Specifically, under low potentials (≤0.25 V), it was discerned that the continuous presence of two or three Pt atoms constituted the pivotal active centers responsible for cleaving the C─C bond, particularly when ethanol intermediate species were adsorbed in a bridged configuration.This adsorption configuration left carbon monoxide (*CO) and *CH x fragments preferentially adsorbed on the Pt sites and further oxidized to CO 2 .Moreover, Zhang et al reported notably heightened mass activity (4.18A mg Pt −1 ) and superior C1 pathway selectivity (61.21%) in the case of 1D Pt-Ir alloy nanorods with tensile-strained (100) facets as compared to the commercial Pt black catalyst. [35]n more intricate acidic environments, an electrocatalyst denoted as Pt 3 Ga/C, as reported by Huang et al, [36] had been employed for EOR.This catalyst exhibits a homogeneously distributed gallium (Ga) configuration on the surface of Pt nanopar- ticles; thus, ensuring an effective and infrequent generation of CO 2 at a moderate potential (≈0.3 V vs SCE).This achievement is attributed to the catalyst's capacity for the direct and sustainable oxidation of the C2 intermediate, namely, acetaldehyde, as depicted in Figure 2C.The atomic spacing structure between platinum (Pt) and gallium (Ga) plays a pivotal role in averting surface nanoparticle aggregation, and consequently, in preventing the formation of toxic *CH x and *CO species through the bridged adsorption of ethanol molecules.Contrastingly, when conventional Pt/C surfaces are employed, the cleavage of C─C bonds becomes a challenging task, further exacerbated by the laborious process of entirely oxidizing the small fraction of C1 species generated during the cleavage process, which ultimately leads to the deactivation of the catalytic active centers.Wang et al. unveiled an elegant one-pot synthesis technique for the fabrication of ternary PtCuRu nanoflowers. [37]Novel nanostructures exhibit high-index facets and display an enrichment of ruthenium (Ru) along their edges, strategically engineered to accelerate the kinetics of C─C bond cleavage.As depicted in Figure 2D, their findings reveal a marked reduction in the reaction barrier associated with the rate-determining steps for EOR, involving the cleavage of the C─C bond, when conducted on the PtCuRu (111) surface in stark contrast to Pt (111).Further, during the EOR process, ruthenium (Ru) was introduced as an ad-ditional active center, significantly augmenting the adsorption state.The incorporation of copper (Cu) doping in this catalytic system effectively modulated the electronic structure of both platinum (Pt) and ruthenium (Ru), thereby expediting the reaction kinetics and facilitating the comprehensive oxidation of ethanol to CO 2 .In terms of stability, the activity of Pt 0.68 Cu 0.18 Ru 0.14 NFs decreased by only 13% after 500 cycles.The result of analyzing the electrolyte using ICP-MS indicates that there was no significant de-alloying process.The TEM results after stability testing indicated no significant morphological changes.
Similarly, the regulatory strategy of alloying extended to the design of Pd-based electrocatalysts. [38]Lai et al. found that niobium (Nb), owing to its oxophilic high-valence characteristics when incorporated into a PdW alloy, assumed a pivotal role in facilitating C─C bond cleavage and the oxidation of CO intermediates. [39]n situ FTIR spectroscopy (as depicted in Figure 3A) reveals that the characteristic CO 3 2− band at 1390 cm −1 exhibited higher intensity in Pd 50 W 27 Nb 23 /C than in the spectrum of Pd 97 W 3 /C.This heightened intensity suggested an elevated C1 selectivity conferred by the introduction of the niobium (Nb) site.Further, the peak at 2000 cm −1 , associated with adsorbed *CO, gradually diminished with increasing applied potential, indicating accelerated CO oxidation on the Pd surface.In tandem with experimental results, density functional theory (DFT) calculations  [34] Copyright 2023, Springer.C) Proposed pathway of direct complete oxidation of ethanol through C2 intermediate on Pt 3 Ga/C, compared to traditional way on Pt/C.Reproduced with permission. [36]opyright 2023, American Chemical Society.D) HRTEM images of PtCuRu NFs and DFT-calculated reaction mechanisms of C─C bond breaking on PtCuRu (111).Reproduced with permission. [37]Copyright 2022, Wiley-VCH.
underscored the considerable reduction in energy barriers during the transition from CH 3 CO to CO on the PdWNb surface compared to pure PdW and Pd (Figure 3B).Liu et al designed quasi-single-crystalline mesoporous PdCu nanoplates at atomic dimension, with an excellent mass activity (6.09A mg Pd −1 ) and C1-product Faraday efficiency of 72.1%. [40]The step position of Pd was a key center for adsorption and activation of EtOH, as well as Cu-doping accelerating C─C bond cleavage and adsorbing OH groups, thereby further oxidizing *CO into CO 2 .Jin et al. achieved a scalable-production strategy to prepare the sizeand shape-controllable amorphous PdCu nanomaterials, affording mass activity of 15.25 A mg Pd −1 and C1 path Faraday efficiency of 69.6%. [41][44] Drawing upon prior understanding of the discrete functional roles played by various constituent elements within the EOR process, Wang et al. have embarked on a pioneering endeavor to meticulously craft PtRhFeNiCu high entropy intermetallic compounds, strategically designated as anode catalysts for high-temperature ethanol fuel cells. [45]The morphology and lattice spacing of high entropy intermetallic compounds were characterized by TEM and high-resolution STEM in Figure 3C.By harnessing the inherent precision within the atomic arrangement structure and harnessing lattice-induced stress, the power density achieved within DEFCs outfitted with high entropy intermetallic alloys achieved a remarkable 47.5 mW cm −2 (as eloquently depicted in Figure 3D), surpassing that of conventional Pt/C catalysts by a notable factor of 2.17.Delving into the intricacies, the DFT analyses (Figure 3E) substantiate that the orchestrated atomic arrangement structure played an instrumental role in substantially abating the free energy barrier associated with the pivotal cleavage of C─C bonds within the CH 2 CO* intermediates.The EOR catalyst also demonstrated excellent stability for over 50 000 s operation.
that detected with the Pd/C catalyst.As far as Au@PtIr is concerned, the Au-induced tensile strain on PtIr surface facilitated C─C bond splitting via ethanol dissociative adsorption, and Ir promoted dehydrogenation at low potentials (Figure 4B), indicating that the synergistic effects of multiple mechanisms play a key role in improving the EOR performance for platinumbased electrocatalysts. [50]According to in situ FTIR spectra, the functions of absorption intensity and potential of intermedi-ate products were summarized at Figure 4C for Au@PtIr and Au@Pt, respectively.The C carbonate /C acetate was 1.3, approximately, for Au@PtIr/C from 0.3 and 0.6 V versus RHE, suggesting ≈57% of the current of the EOR process was generated via a direct 12electron pathway.While Au@Pt exhibited comparable selectivity, it is noteworthy that the initial potential of the detected product was significantly elevated when compared to Au@PtIr.This divergence could be attributed to the lattice strain generated by the A) The HAADF-STEM image and 2D mapping of Au@PtIr particle.B) Schematic diagram of the efficient mechanism of breaking C─C bonds by Au@PtIr.C) Integrated absorbances of EOR products and molar ratio of carbonate to acetate for Au@PtIr/C and Au@Pt/C.Reproduced with permission. [50]Copyright 2019, American Chemical Society.
presence of the Au core, which played a pivotal role in facilitating C─C bond cleavage.In contrast, the introduction of iridium (Ir) expedited the oxidative dehydrogenation of ethanol.
Taking into account the operational parameters of catalysts within proton exchange membrane fuel cells, the hightemperature, high-humidity, and proton-rich environment, it becomes imperative to incorporate the challenge of mitigating metal dissolution into the electrocatalyst design process. [51,52]etal dissolution, if left unaddressed, will lead to irreversible proton channel blockage within the fuel cell system.[55] Sun et al reported a convenient strategy for preparation of Pt 3 Co with Pt-skin (Figure 5A), only 1-2 atomic layers, ≈0.5 nm, to achieve efficient acid-EOR process (0.79 mA μg Pt −1 ). [56]According to DFT (Figure 5B), CH 2 CO* is the most suitable C2 intermediate produced by the EOR process for breaking the C─C bond on the stepped Pt 3 Co (211) surface, with an energy barrier of only 0.57 eV for forming CH 2 * and CO*.However, based on the integral intensity statistics of the characteristic peaks for C1/C2 intermediates in the in situ mass spectroscopy FTIR spectra (Figure 5C), the oxidation selectivity of Pt 3 Co@Pt/PC is lower than that of platinum carbon, indicating that creating complete oxidation sites proved in theoretical calculations still poses a challenge in real experimental synthesis.A heterogeneous hcp-PtPb/fcc-Pt core/shell hexagonal nanosheet with 7.2% tensile strain wrapped on the surface of Pt (110), with Ir single atom doping, was reported by Zhang et al. as an EOR electrocatalyst to achieve the C1 pathway selectivity up to 57.93%. [57]As Figure 5D shows, the activation barriers of cleav-age for C─C bond in CH 2 CO* intermediate on the surface of Pt(110), Pt(110)+7.2%,Ir-Pt(110), and Ir-Pt(110)+7.2%are 0.82, 0.75, 0.32, and 0.21 eV, respectively, which reflects the synergistic effect of tensile strain and Ir single atom doping on the ability of the electrocatalyst to break the C─C bond.In the abovementioned process, it is not difficult to find that Ir doping plays a more dominant function in reducing energy barriers and blocking the C2 pathway, prominently.The mass specific activity of PtPb@PtIr 1 reaches 5.91 A mg Pt+Ir −1 and only loses 37.2% after 5000 cycles.The catalyst designs in the above work make EOR more inclined toward 12-electron processes, which also means less CO and CH 3 COOH in the reaction system.Reducing toxic intermediates is the key to improving stability.
Actually, the secondary metal apart from Pt or Pd in the alloy can act as the secondary active site and forms a dual active site catalyst together with Pt or Pd, which embodies the concept of "1 + 1 > 2". [58,59][65][66] The introduction of assistant active sites can also weaken the adsorption of O* intermediate through enhancing the adsorption capacity of Pt atoms to the HO* intermediate. [67]DFT calculations demonstrate that the O* + H + + e − → OH* step starts above 0.87 V with an overpotential as low as 0.36 V (Figure 6B).In addition, the electronic effect is Reproduced with permission. [56]Copyright 2017, American Chemical Society.D) The reaction barriers for breaking C─C in CH 2 CO* on different catalyst surfaces.Reproduced with permission. [57]Copyright 2015, Wiley-VCH.B) Cu defected PtCu (111) surface and free energy diagrams on Cu defected PtCu (111) surface.Reproduced with permission. [67]Copyright 2020, Wiley-VCH.C) EDX line-scanning profile of Pt 69 Ni 16 Rh 15 nanowires.D) PDOSs of Ni 3d, Ir 5d, Os 5d, and Rh 4d bands.Reproduced with permission. [32]opyright 2019, Wiley-VCH.E) HAADF-STEM image of Rh-O-Pt dual sites.F) Scheme and computed energetics of ethanol being oxidized to the major product acetaldehyde and reaction energy barriers of CH 3 CO* oxidation and cleavage on Rh-O-Pt models.Reproduced with permission. [71]Copyright 2023, American Chemical Society.
invoked to explain the activity enhancement of EOR catalysts with dual sites. [32]Guo et al. prepared ultrathin PtNiM (M = Rh, Os, and Ir) nanowires (Figure 6C) with excellent anti-CO-poisoning ability and high activity.Dynamic adsorption analysis confirms that the synergetic d-orbital interplay between Pt and Rh/Ni can lower the Pt 5d band center, and then, promote the CO ad intermediates toward full oxidization (Figure 6D).The easier desorption of *CO is also an important reason for the improved stability.
Hutchings, [68] in their meticulous exploration of hydroxyl oxidation involving 5-hydroxymethylfurfural (HMF) as a model reaction, convincingly demonstrated that the oxidation capability of discrete Pd and Au phases surpassed that of individual components, including alloys.In terms of the electro-oxidation process of ethanol, Wang et al. made an insightful discovery: the catalytic activity of the Pd-Zn dual active site significantly outperformed that of the pure Pd-Pd site, achieving a remarkable enhancement, with a reaction activity 24-fold superior to that of conventional Pd/C catalysts. [69]In further research, Guo et al designed YO x /MoO x -Pt NWs for the alcohol oxidation process, where YO x /MoO x was an important site for the oxidation of *CO intermediates. [70]The coordination of dual sites in YO x /MoO x also accelerated the cleavage of C─C bonding, and the characteristic peak of CO 2 would be observed at a low potential of ≈0.3 V in the infrared spectrum.Wang et al. constructed oxygenbridged long-range Rh-O-Pt dual sites to accelerate C─C cleavage through redistributing the surface-localized electron around Rh-O-Pt (Figure 6E). [71]Theoretical calculations disclosed that the redistribution of the surface-localized electron around Rh-O-Pt could lower the energy of C─C bond cleavage (0.59 eV, Figure 6F), accelerating C─C bond cleavage.

Cascade Electrocatalysis
The primary objective of the DEFCs is to convert ethanol into CO 2 directly; yet, the C1 pathway shares a small part of the reaction due to the high bond dissociation energy for the C─C bond breaking (87.3 kcal mol −1 ) and the sluggish kinetic of C1pathway.Researchers spare no effort to optimize the design of the active site of the catalyst to improve C1 pathway selectivity.However, it is still difficult to achieve the complete oxidation of the ethanol and achieve the 100% selectivity of CO 2 .Ethylene is also a C2 type organic compound; while, its activation energy of C═C bond (6.4 kcal mol −1 ) is much lower than that of the C─C bond in ethanol.Thus, introducing ethylene as reaction intermediates may be an effective strategy to accelerate the C─C bond breaking kinetics and realize a higher C1-pathway selectivity.
On the basis, our group creatively develop a unique composite catalyst Pt/Al 2 O 3 @TiAl with cascade active sites to catalyze dehydration of ethanol and oxidation of ethylene, respectively (Figure 7A). [72]As a result, a C1-pathway selectivity of 100 % during EOR is achieved via introducing ethylene as the precursor for the C─C bond breaking (Figure 7B).On Pt/Al 2 O 3 @TiAl, ethanol is first dehydrated on the Al 2 O 3 @TiAl support to form ethylene owing to the dehydration of Al 2 O 3 to ethanol.The dehydration occurs through an elimination mechanism, in which the -hydrogen of the ethanol is transferred to the surface oxygen of the oxides and the C─OH bond is depleted in a concerted reaction step. [73]In addition, the formed ethylene is further oxidized on Pt catalyst to CO 2 through cleaving the C═C bond, which is confirmed by the in situ Fourier transform infrared spectroscopy (Figure 7C) and differential electrochemical mass spectrometry (Figure 7D) analysis.As a result, this unique catalyst shows outstanding EOR  and D) DEMS spectra and the corresponding reaction process of EOR on Pt/Al 2 O 3 @TiAl.Reproduced with permission. [72]Copyright 2023, Wiley-VCH.E) Zoomed-out STM image of the CrPtAg alloy in the region around a step edge.F) Ethanol dehydrogenation to ethylene on Pt 1 Cr 1 Ag and Pt 1 Cr 2 Ag.Reproduced with permission. [74]Copyright 2023, American Chemical Society.

performance (3.83 mA cm −2
Pt ) and high stability with only 7% current loss after 12 h electrochemical test.
Coincidentally, Montemore et al. discovered that the dehydration of ethanol could occur on Pt-Cr sites in PtCrAg (Figure 7E) and produce ethylene when the dopant concentrations of PtCr ensembles was high (Figure 7F). [74]The selectivity to ethylene could reach to ≈80% at 10% dopant concentrations, which provided the conditions for ethylene-mediated cascade electrocatalysis for complete oxidation of ethanol.This unique pathway of ethanol first dehydrating on the first active sites, and then, further oxidizing on the second active site could provide guidance to the further study of complete ethanol electro-oxidation; we expect more cascade catalytic pathways to be found to realize the full utilization of ethanol.

Interface Synergism
Given the intricacies inherent to the EOR process, it is often imperative to employ multi-component catalyst systems, where the synergistic collaboration among diverse constituents becomes a prerequisite for achieving comprehensive oxidation. [11,75]he interface synergy between different components assumes paramount research significance as it represents a pivotal determinant for facilitating the elusive 12-electron process.For example, 2D Pd-Au heterophase nanosheet (Pd-Au HNS), [30] with abundant interphase between amorphous Pd domain and crystalline Au cluster, is prepared through a simple galvanic reaction (Figure 8A).In the displacement reaction, chloroauricate ion reacts with the low-coordination Pd atom at the edge site, disrupting the ordered single-crystal structure and forming a unique interface.Among the series of catalysts with different ratios of Pd and Au, the Pd-Au HNS, with atom ratio as 88:12, exhibits the best mass specific activity of 9.1 A mg Pd −1 , which is 9.3 and 7 times higher than traditional palladium carbon and platinum carbon, respectively.What's even more interesting is that the novel interface design, as a switch-off, to some extent, blocks the C2 pathway.Compared to the surface of Pd NS, the activation energy for further oxidation of CH 3 CO intermediate to acetic acid on Pd-Au HNS increases from 1.04 to 2.45 eV Figure 8. A) The schematic diagram of synthesis path for 2D Pd-Au heterophase nanosheet.Reproduced with permission. [30]Copyright 2021, Wiley-VCH.B) Comparison of oxidation energy barriers for CH 3 CO species on different catalyst surfaces.C) Schematic diagram of accelerating C─C bond clearance on Rh-SnO 2 interface.Reproduced with permission. [17]Copyright 2021, Wiley-VCH.D) The polarization curves and power density for different Pd-based electrocatalyst.Reproduced with permission. [86]Copyright 2023, Springer Nature Ltd.E) Schematic diagram of EOR process comparison between Pd/Co@N-C and Pd/C.
(Figure 8B), notably, which has a critical impact on the 33.2% C1 pathway selectivity exhibited by a simple-structure catalyst.
Rh is more susceptible to poisoning and deactivation by carbon oxygen and hydrocarbon intermediates in the EOR process, making it rare for rhodium-based electrocatalyst to serve as active center. [76][79] Huang et al. [17] demonstrated that constructing Rh-SnO 2 active interface (Figure 8C) will efficiently achieve a 12-electron EOR process, with a Faraday efficiency of up to 72.8%.Due to the presence of the interface, the electrons of Rh transfer to SnO 2 , causing its d-band to shift upward, which accelerates the cleavage of C─C bonds and the desorption process of C1 intermediates.Through CO-DRIFTS, it will be observed that the interface formed by the addition of SnO 2 significantly weakens the peak strength of carbonyl edge adsorption and CO bridge adsorption, accompanied by a blue shift of the peak (from 1838 to 1860 cm −1 ).In addition, the strong interaction between Rh and Sn species at the Rh─SnO 2 interface significantly boosts the EOR performance in terms of high stability.
[82] Nonetheless, it is pertinent to acknowledge that palladium exhibits a heightened affinity toward diverse oxygen species, a characteristic that significantly constrains its utility within the realm of electrocatalysis. [83]During EOR, it is noteworthy that the selectivity pertaining to the 12-electron process on the Pd surface registers at a mere range of 0.5-7.5%. [84,85]Based on the previous understanding of Pd electrocatalytic performance, Yang et al. [86] proposed an interface synergy strategy, involving the electron transfer occurring at the interface between Pd and Co@N-C, thereby reducing the electron cloud density on the surface of Pd.Interestingly, through the simultaneous activation of ORR and EOR processes by unique interface design, the power density of anion exchange membrane fuel cells reached 438 mW cm −2 with 1 mg Pd cm −2 (Figure 8D) and exhibited stability over 1000 h at 0.5 V. Further, at a low potential of 0.2 V, Pd/Co@N-C would promote C─C bonding cleavage, as well as, the C1 intermediate would be further oxidized at 0.7 V versus RHE, resulting in an exceptional 12-electron process (Figure 8E).However, traditional Pd/C, even when physically mixed with Co@N-C, is still a general four-electron process, demonstrating the irreplaceable role of the interface effect.

Doping Effect
Regarding the fact that heterogeneous catalytic reactions mostly occur on the surface/interface between the catalysts and reactants, surface active sites play vital roles in the catalytic reactions.Inspired by the preparation of single-atoms catalysts (SACs), single-atom alloy (SAA) catalysts have already been developed. [87]uch methods have received extensive attention in catalysis due to their unique reaction sites and high reactivity; however, few of such catalysts show satisfying C 1 pathway selectivity in practical application, especially in the acidic solution. [88]On the basis, researchers find that doping foreign atoms to construct surface defect can be a promising method to promote the performance of heterogeneous catalysts in the electrocatalysis process. [89]The doping to Pt electrodes by other metals such as Ru, Rh, Sn, Pd has been investigated to be effective in increasing the peak current density and lowering the onset potential significantly; [90][91][92][93][94] while, most of the main products are acetic acid and acetaldehyde.Thus, it is of vital importance to give consideration to both raising the full utilization of ethanol and enhancing the catalytic activity.
In 2014, Lin group [95] found that CH 3 CHOH* is the key intermediate during ethanol electrooxidation and the activity of -dehydrogenation is the rate determining factor that affects the CO 2 selectivity of ethanol electro-oxidation using the first principles method (Figure 9A).They demonstrated that the doping of some transition metals such as Ru, Os, Rh, and Ir can accelerate b-dehydrogenation as their doping can decrease the barrier from CH 3 CHOH* to CH 2 CHOH*.Besides, the formation of *OH by the water dissociation would lead to the formation of acetaldehyde and acetic; therefore, the doping of Ru, Os, and Ir atoms would lead to the non-CO 2 pathway as they may decrease the formation potential of *OH.Similarly, in 2016, Michel group [96] reported that though Pt(100) surface shows higher ethanol to CO 2 conversion compared to Pt(111) and Pt(110), it prefers partial oxidation to form acetic acid (CH 3 COOH) owing to the impeded kinetics of the C─C bond cleavage.They also suggested that destabilizing the gem-diol, stabilizing the acetyl, and facilitating its splitting to CH 3 and CO may contribute to a higher CO 2 selectivity.
Chen group [97] succeeded in the controlled synthesis of dispersing partially oxidized single Rh on the (100) surface of Pt nanocubes (Rh at O-Pt NCs; Figure 9B,C), which raised CO 2 selectivity to above 99.9% from 0.35 to 0.75 V (Figure 9D).The doping of Rh atoms helped to break C─C bond and remove the poisoning *CO; thus, decreasing the CO 2 generation potential to be much closer to the thermodynamic potential for the oxidation of ethanol to CO 2 (0.143 V) than the commercial Pt/C.DFT calculations have found that the adsorption of CO on Rh at O/Pt (100) sites is significantly weaker than on Pt (100) site.The in situ XAFS analysis conducted at the Rh K-edge using the chronoamperometric mode of EOR at 0.75 V suggested a unique environment of Rh at O on the Pt(100) surfaces as a new active site, which contributed to the astonishing CO 2 selectivity (Figure 9E,F).Xu group [87] used monodispersed metal sites to tailor Pt-based nano-catalysts and first construct monodispersed Ga on Pt 3 Mn nanocrystals (Ga-O-Pt 3 Mn, Figure 10A) with high-indexed facets.The specific activity of the reported Ga-O-Pt 3 Mn nano-catalyst was 3.68 and 8.41 times that of Pt 3 Mn and commercial Pt/C (Figure 10B).The theoretical modeling results confirm a strong electronic interaction between the Pt substrate and the monodispersed Ga component via the unconventional p-d orbital hybridization.The doping of Ga monodispersed atoms upshifted d-band center from the Fermi level, which could strengthen the adsorption of ethanol molecules (Figure 10C).
In addition to the above strategies, tailoring amorphous electrocatalysts with nanostructure and modifying electrocatalysts with polysulfide can also facilitate the C─C bond cleavage significantly.Jin et al. utilized amorphous nanocatalysts with the enriched coordination unsaturated surface sites to cleave the chemically stable C─C bond. [41]Their DFT calculations results revealed that the energy barrier C─C bond breaking on coordination of unsaturated surface sites (0.29 eV) was much lower than Figure 9. A) Energy profiles of ethanol electrooxidation on Pt(111).The blue line is the energy profile of the -dehydrogenation pathway and the red line is that of the -dehydrogenation pathway.Reproduced with permission. [95]Copyright 2014, Royal Society of Chemistry.B) High-angle annular dark-field STEM images, EDS mapping image, and C) schematic model of Rh at O-Pt NCs.D) The CO 2 selectivity of Rh at O-Pt NCs and other samples from 0.25 to 1.05 V. E) XANES and F) EXAFS spectra for the Rh K-edge of Rh at -O Pt NCs/C before, after, and during EOR chronoamperometric test in 0.1 m HClO 4 + 1.0 m ethanol solution at 0.75 V. Reproduced with permission. [97]Copyright 2022, Washington, DC.  410) structure.Reproduced with permission. [88]Copyright 2022, Wiley-VCH.D) HRTEM image of S 3.67 -PtCu intermetallic/C.E) Enriching effect enhances cleavage of C─C bond.Reproduced with permission. [98]Copyright 2023, Springer.
on the crystalline surface (0.85 eV).As a result, the amorphization of PdCu catalysts afforded a C1 path Faraday efficiency as high as 69.6%.To accelerate the C─C bond cleavage, Wang et al. employed sulfur bridge structure and polysulfide bond to enrich hydroxyl and ethanol for PtCu intermetallic (Figure 10D). [98]The enrichment effect of ethanol and hydroxyl on the catalyst surface could accelerate the oxidation of CO and expose a large number of active sites for splitting the C─C bond and improving the CO 2 selectivity of EOR (Figure 10E).The CO 2 selectivity of PtCu intermetallic nanocatalyst without polysulfide reached 93.5%.

Summary and Outlook
Direct ethanol fuel cell is an emerging power device that has demonstrated unique advantages in volumetric energy density (6.28 kWh•L −1 ), energy conversion efficiency, recharging time (3 min), and environmental protection. [99]At present, electrocatalysts for oxygen reduction reaction at the cathode and proton exchange membrane have made great progress.Nevertheless, the activity and stability of commercial catalysts for ethanol oxidation reaction need to be further improved to meet the scale application requirements of DEFCs.We think that the electrocatalysts for ethanol oxidation should have the following characteristics: 1) Outstanding capacity to cleave C─C bond.Compared with C1 pathway (complete oxidation of ethanol with 12 electrons transferring), the C2 pathway only involves four electrons transferring without breaking a C─C bond during incomplete oxidation of ethanol, which seriously hinders the energy density output of DE-FCs.However, the C─C bond activation is the rate-limiting step for ethanol complete oxidation owing to the high activation energy of the C─C bond (87.3 kcal mol −1 ).Taking advantage of the different adsorption strength of the two carbon atoms via bridgetype adsorption of ethanol molecules on heterogeneous dual active sites and constructing electrocatalysts with specific structure to achieve complete oxidation of ethanol by relay catalysis are directions worth focusing on in the future.2) Remarkable stability.[102] Developing corrosion resistant supports and enhancing the interaction between the active sites and supports have shown substantial promise up to now. 3) Acceptable cost.Extensive use of precious metals in catalyst layer is a main reason for the high cost of DEFCs.Optimizing the catalyst layer, such as constructing porous support to improve the utilization of precious metals and reduce the loading thereof, may be effective in reducing costs.

Figure 1 .
Figure 1.The schematic diagram of C1 and C2 pathways of EOR.

Figure 2 .
Figure 2. A) HAADF-STEM images and elemental mapping of Pt 1 Au 1 /C.B) The schematic diagram of the ethanol electro-oxidation mechanism with possible sites on the surface of Pt 1 Au 1 in different potential ranges.Reproduced with permission.[34]Copyright 2023, Springer.C) Proposed pathway of direct complete oxidation of ethanol through C2 intermediate on Pt 3 Ga/C, compared to traditional way on Pt/C.Reproduced with permission.[36]Copyright 2023, American Chemical Society.D) HRTEM images of PtCuRu NFs and DFT-calculated reaction mechanisms of C─C bond breaking on PtCuRu (111).Reproduced with permission.[37]Copyright 2022, Wiley-VCH.

Figure 3 .
Figure 3. A) In situ FTIR spectra of ethanol oxidation reaction on the Pd 50 W 27 Nb 23 /C and B) DFT-calculated reaction mechanisms of C1 pathway.Reproduced with permission.[39]Copyright 2022, Wiley-VCH.C) The morphology characterization of high-entropy intermetallic.[45]D) The high-temperature DMFCs performance with different catalysts as anodes.E) The energy barriers of C─C bond breaking ordered and disordered alloy surfaces.Copyright 2022, Wiley-VCH.

Figure 4 .
Figure 4.A) The HAADF-STEM image and 2D mapping of Au@PtIr particle.B) Schematic diagram of the efficient mechanism of breaking C─C bonds by Au@PtIr.C) Integrated absorbances of EOR products and molar ratio of carbonate to acetate for Au@PtIr/C and Au@Pt/C.Reproduced with permission.[50]Copyright 2019, American Chemical Society.

Figure 5 .
Figure 5. A) Atomic-resolution ADF-STEM image of Pt 3 Co@Pt/PC, with the intensity of sites L1, L2, L3, and L4.B) Free energy of EOR on the stepped Pt 3 Co (211) surface.C) Ratio change of integrated intensities of CO 2 and intensities CH 3 COOH of Pt 3 Co@Pt/PC and Pt/C with different increasing overpotential.Reproduced with permission.[56]Copyright 2017, American Chemical Society.D) The reaction barriers for breaking C─C in CH 2 CO* on different catalyst surfaces.Reproduced with permission.[57]Copyright 2022, Wiley-VCH.

Figure 6 .
Figure 6.A) Oxidation mechanism of intermediate Co ad with the assistance of OH* species.Reproduced with permission.[65]Copyright 2015, Wiley-VCH.B) Cu defected PtCu (111) surface and free energy diagrams on Cu defected PtCu (111) surface.Reproduced with permission.[67]Copyright 2020, Wiley-VCH.C) EDX line-scanning profile of Pt 69 Ni 16 Rh 15 nanowires.D) PDOSs of Ni 3d, Ir 5d, Os 5d, and Rh 4d bands.Reproduced with permission.[32]Copyright 2019, Wiley-VCH.E) HAADF-STEM image of Rh-O-Pt dual sites.F) Scheme and computed energetics of ethanol being oxidized to the major product acetaldehyde and reaction energy barriers of CH 3 CO* oxidation and cleavage on Rh-O-Pt models.Reproduced with permission.[71]Copyright 2023, American Chemical Society.

Figure 7 .
Figure 7. A) FIB-HRTEM image, HAADF-STEM image of Pt/Al 2 O 3 @TiAl and the corresponding elemental mapping.B) C1-pathway, C) In situ FTIR spectra,and D) DEMS spectra and the corresponding reaction process of EOR on Pt/Al 2 O 3 @TiAl.Reproduced with permission.[72]Copyright 2023, Wiley-VCH.E) Zoomed-out STM image of the CrPtAg alloy in the region around a step edge.F) Ethanol dehydrogenation to ethylene on Pt 1 Cr 1 Ag and Pt 1 Cr 2 Ag.Reproduced with permission.[74]Copyright 2023, American Chemical Society.

Figure 10 .
Figure 10.A) Aberration-corrected HAADF-STEM image and STEM-EDS elemental mapping of the Ga-O-Pt 3 Mn nanocatalyst.B) The specific activities and mass activities of Ga-O-Pt 3 Mn and other samples.C) The charge density difference of Ga-O-Pt(410) interface and the electron localization function analysis mapped for Pt(410) and Ga-O-Pt(410) structure.Reproduced with permission.[88]Copyright 2022, Wiley-VCH.D) HRTEM image of S 3.67 -PtCu intermetallic/C.E) Enriching effect enhances cleavage of C─C bond.Reproduced with permission.[98]Copyright 2023, Springer.

Chenjia
Liang is, currently pursuing a doctor's degree at the Nanjing University under the guidance of Professor Weiping Ding.His research interests focus on the novel design of electrocatalyst in mesoscale.Ruiyao Zhao received a Bachelor of Science in the Central South University in 2022 and is currently pursuing a postgraduate degree in Nanjing University.Her research interests involve surface state regulation for methanol oxidation and hydrogen evolution reaction.Teng Chen is currently an associate professor of the Air Force Logistics Academy and a post-doctor of the School of Chemistry and Chemical Engineering, Nanjing University.He received his Ph.D. (2019) from the Nanjing University with Profs.Yi Chen and Weiping Ding.His research interests involve catalytic materials in mesoscale for oxygen reduction reaction, hydrogen evolution reaction, and ethanol oxidation reaction.www.advancedscience.comWeiping Ding received his bachelor's and doctor's degrees from the Department of Chemistry, Nanjing University.He has engaged in postdoctoral research in the Department of Physics, Nanjing University, as well as the University of California at Berkeley and Harvard University, successively.He is currently a professor in the School of Chemistry and Chemical Engineering, Nanjing University and director of the Key Lab of Mesoscopic Chemistry.In recent years, his advocacy, about "Meso Catalysis" research, has achieved fruitful innovative results in hydrogenation, oxidation, acid catalysis, fuel cell catalysts, and electrocatalysis, which are being transferred to industrial applications.

Table 1 .
Summary of the EOR catalysts, catalysis abilities, and design strategies.